Abstract
Internal friction (IF) measurements were conducted using ferrous lath martensite specimens with different retained austenite fractions. While a distinctive Snoek-Kê-Köster (SKK) peak was detected in the IF spectra, the peak shape did not conform to the peak shape observed for fully martensitic steel. Peak analysis suggests that the peak shape is related to the overlap of the SKK peak with a Finkelstein–Rosin peak, additional Debye-type peak related to the retained austenite.
References
[1] Y. Liu: Acta Metall. Mater., 1993, vol. 41, pp. 3277-87.
[2] X. Lu, M. Jin, H. Zhao, W. Li and X. Jin: Solid State Comm., 2014, vol. 195, pp. 31-4.
[3] I. Tkalcec and D. Mari: Mater. Sci. Eng. A, 2004, vol. 370, pp. 213-7.
[4] J.J. Hoyos, A.A. Ghilarducci, H.R. Salva, C.A. Chaves and J.M. Vélez: Mater. Sci. Eng. A, 2009, vol. 521–522, pp. 347-50.
[5] W.S. Choi, J. Lee and B.C. De Cooman: Mater. Sci. Eng. A, 2015, vol. 639, pp. 439-47.
[6] D. Sulistiyo, L. Cho, E. Seo and B.C. De Cooman: Mater. Sci. Technol., 2016, vol. 33, pp. 1-14.
[7] I. Tkalcec, D. Mari and W. Benoit: Mater. Sci. Eng. A, 2006, vol. 442, pp. 471-5.
D.H. Sulistiyo: Master’s Thesis, Pohang University of Science and Technology, Pohang, Republic of Korea, 2016.
[9] A.H. Heuer, F. Ernst, H. Kahn, A. Avishai, G.M. Michal, D.J. Pitchure and R.E. Ricker: Scripta Mater., 2007, vol. 56, pp. 1067-70.
[10] S.-J. Lee, J. Kim, S.N. Kane and B.C. De Cooman: Acta Mater., 2011, vol. 59, pp. 6809-19.
[11] K. Rose and S. Gloverj: Acta Metall., 1966, vol. 14, pp. 1505-16.
[12] J.L. Snoek: Physica, 1941, vol. 8, pp. 711-33.
[13] I.-C. Jung, D.-G. Kang and B.C. De Cooman: Metall. Mater. Trans. A, 2014, vol. 45, pp. 1962-78.
[14] R. Martin, I. Tkalcec, D. Mari and R. Schaller: Phil. Mag., 2008, vol. 88, pp. 2907-20.
[15] R. Bagramov, D. Mari and W. Benoit: Phil. Mag. A, 2001, vol. 81, pp. 2797-808.
[16] R.M. Fuoss and J.G. Kirkwood: J. Am. Chem. Soc., 1941, vol. 63, pp. 385-94.
M.S. Blanter, I. Golovin, H. Neuhauser, and H. Sinning (2007) A Handbook Series: Springer Series in Materials Science. Springer, Berlin, pp. 28–30.
[18] A.E. Lord and D.N. Beshers, Acta Metall., 1966, vol. 14, pp. 1659-72.
[19] J. Gegner: Materialwiss. Werkstofftech., 2005, vol. 36, pp. 56-61.
[20] S.M. Teus, V.N. Shyvanyuk and V.G. Gavriljuk: Acta Mater., 2006, vol. 54, pp. 3773-8.
[21] E.J. Seo, L. Cho, Y. Estrin and B.C. De Cooman: Acta Mater., 2016, vol. 113, pp. 124-39.
[22] D.T. Pierce, D.R. Coughlin, D.L. Williamson, J. Kähkönen, A.J. Clarke, K.D. Clarke, J.G. Speer and E. De Moor: Scripta Mater., 2016, vol. 121, pp. 5-9.
The authors gratefully acknowledge the support of the POSCO Technical Research Laboratories (South Korea).
Author information
Authors and Affiliations
Corresponding author
Additional information
Manuscript submitted June 15, 2017.
Rights and permissions
About this article
Cite this article
Kim, J.H., Ju, Y.N., Kang, S. et al. Impulse Excitation Internal Friction Study of Retained Austenite in Ferrous Martensite. Metall Mater Trans A 49, 5235–5240 (2018). https://doi.org/10.1007/s11661-018-4886-7
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11661-018-4886-7