Carbon Nanostructured Catalysts as High Efficient Materials for Low Temperature Fuel Cells

  • S. Sadegh HassaniEmail author
  • L. Samiee
Reference work entry

Abstract

Low-temperature fuel cells are representative of environmentally friendly technologies, which enable directly produced electricity by converting the hydrogen/methanol/ethanol and oxygen into water/water and carbon dioxide. Although these systems have low technical complexity, because of sluggish kinetics of oxygen reduction reaction (ORR), they need an efficient catalyst.

Platinum and its alloys deposited on the carbon support were the first catalyst generations that have been extensively used as cathode electrodes because of their low overpotential as well as ability in four-electron reduction reaction. However, the stability of Pt-based catalysts and their cost are the two critical challenges that need to be considered for the successful commercialization. Thus, several researches have been done to find out a way to reduce the platinum amount in the catalyst of the low-temperature fuel cells. In this regard, several solutions have been proposed such as catalyst functionalization by transition metal oxides or using new carbon materials as catalysts supports. To overcome the platinum disadvantages such as low durability, poisoning effects, and crossover issues, nonprecious metal catalysts (NPMCs) with high oxygen reduction ability have become distinguished. In this regard, many materials were checked to reach the combination of ORR activity with good performance stability and economic consideration.

In this chapter, firstly different mechanism pathways occurred in low temperature fuel cells will be discussed. Moreover, the advantage and disadvantage of different generations of carbon-based catalysts from Pt-based and its alloys up to nonprecious metal catalysts (metal containing and metal-free ones) used in low temperature fuel cells will be studied.

References

  1. 1.
    Benson J, Xu Q, Wang P, Shen Y, Sun L, Wang T, Li M, Papakonstantinou P (2014) Tuning the catalytic activity of graphene nanosheets for oxygen reduction reaction via size and thickness reduction. ACS Appl Mater Interfaces 6:19726–19736Google Scholar
  2. 2.
    Zhou M, Wang HL, Guo S (2016) Towards high-efficiency nanoelectrocatalysts for oxygen reduction through engineering advanced carbon nanomaterials. Chem Soc Rev 45:1273–1307Google Scholar
  3. 3.
    Song C, Zhang J (2008) Electrocatalytic oxygen reduction reaction. In: Zhang J (ed) PEM fuel cell electrocatalysts and catalyst layers. Springer, London, pp 89–134Google Scholar
  4. 4.
    Wang DW, Su D (2014) Heterogeneous nanocarbon materials for oxygen reduction reaction. Energy Environ. Science 7:576–591Google Scholar
  5. 5.
    He Q, Cairns EJ (2015) Review – recent progress in electrocatalysts for oxygen reduction suitable for alkaline anion exchange membrane fuel cells. J Electrochem Soc 162:F1504–F1539Google Scholar
  6. 6.
    Blizanac BB, Ross PN, Markovic NM (2007) Oxygen electroreduction on Ag(111): the pH effect. Electrochim Acta 52:2264–2271Google Scholar
  7. 7.
    Li D, Lv H, Kang Y, Markovic NM, Stamenkovic VR (2016) Recent advances in the development of oxygen reduction reaction catalysts for low-temperature fuel cells. Annu Rev Chem Biomol Eng 7:509–532Google Scholar
  8. 8.
    Kwak DH, Lee YW, Han SB, Hwang ET, Park HC, Kim MC, Park KW (2015) Ultrasmall PtSn alloy catalyst for ethanol electro-oxidation reaction. J Power Sources 275:557–562Google Scholar
  9. 9.
    Lee YW, Oh SE, Park KW (2011) Highly active Pt-Pd alloy catalyst for oxygen reduction reaction in buffer solution. Electrochem Commun 13:1300–1303Google Scholar
  10. 10.
    Shao M, Smith BH, Guerrero S, Protsailo L, Su D, Kaneko K, Odell JH, Humbert MP, Sasaki K, Marzullo J, Darling RM (2013) Core-shell catalysts consisting of nanoporous cores for oxygen reduction reaction. Phys Chem Chem Phys 15:15078–15090Google Scholar
  11. 11.
    Li D, Wang C, Strmcnik DS, Tripkovic DV, Sun X (2014) Functional links between Pt single crystal morphology and nanoparticles with different size and shape: the oxygen reduction reaction case. Energy Environ Sci 7:4061–4069Google Scholar
  12. 12.
    Stamenkovic VR, Fowler B, Mun BS, Wang G, Ross PN, Lucas CA, Marković NM (2007) Improved oxygen reduction activity on Pt3Ni(111) via increased surface site availability. Science 315:493–497Google Scholar
  13. 13.
    Shao M, Chang Q, Dodelet JP, Chenitz R (2016) Recent advances in electrocatalysts for oxygen reduction reaction. Chem Rev 116:3594–3657Google Scholar
  14. 14.
    Nesselberger M, Ashton S, Meier JC, Katsounaros I, Mayrhofer KJJ, Arenz M (2011) The particle size effect on the oxygen reduction reaction activity of Pt catalysts: influence of electrolyte and relation to single crystal models. J Am Chem Soc 133:17428–17433Google Scholar
  15. 15.
    Nesselberger M, Roefzaad M, Faycal Hamou R, Ulrich Biedermann P, Schweinberger FF, Kunz S, Schloegl K, Wiberg GKH, Ashton S, Heiz U (2013) The effect of particle proximity on the oxygen reduction rate of size-selected platinum clusters. Nat Mater 12:919–924Google Scholar
  16. 16.
    Fabbri E, Taylor S, Rabis A, Levecque P, Conrad O, Kotz R, Schmidt TJ (2014) The effect of platinum nanoparticle distribution on oxygen electroreduction activity and selectivity. ChemCatChem 6:1410–1418Google Scholar
  17. 17.
    Stamenkovic V, Mun BS, Mayrhofer KJJ, Ross PN, Markovic NM (2006) Changing the activity of electrocatalysts for oxygen reduction by tuning the surface electronic structure. Angew Chem Int Ed 45:2897–2901Google Scholar
  18. 18.
    Samiee L, Shoghi F, Vinu A (2013) Fabrication and electrocatalytic application of functionalized nanoporous carbon material with different transition metal oxides. J Appl Surf Sci 265:214–221Google Scholar
  19. 19.
    Coleman EJ, Chowdhury MH, Co AC (2015) Insights into the oxygen reduction reaction activity of Pt/C and PtCu/C catalysts. ACS Catal 5:1245–1253Google Scholar
  20. 20.
    Maghsodi A, Milani Hoseini MR, Dehghani Mobarakeh M, Kheirmand M, Samiee L, Shoghi F, Kameli M (2011) Exploration of bimetallic Pt–Pd/C nanoparticles as an electrocatalyst for oxygen reduction reaction. J Appl Surf Sci 257:6353–6357Google Scholar
  21. 21.
    Samiee L, Shoghi F, Maghsodi A (2014) In-situ functionalization of mesoporous carbon electrodes with carbon nanotube for PEM fuel cell application. Mat Chem Phys J 143:1228–1235Google Scholar
  22. 22.
    Zhang B, Chen LJ, Ge KY, Guo YC, Peng BX (2005) Preparation of multiwall carbon nanotubes-supported high loading platinum for vehicular PEMFC application. Chin Chem Lett 16:1531–1534Google Scholar
  23. 23.
    Zhang N, Chen X, Lu Y, An L, Li X, Xia D, Zhang Z, Li J (2014) Boron nitride nanocages as high activity electrocatalysts for oxygen reduction reaction: synergistic catalysis by dual active sites. Small 10:2662–2669Google Scholar
  24. 24.
    Jasinski R (1964) A new fuel cell cathode catalyst. Nature 201:1212–1213Google Scholar
  25. 25.
    Bashyam R, Zelenay P (2006) A class of non-precious metal composite catalysts for fuel cells. Nature 443:63–66Google Scholar
  26. 26.
    Alonso-Vante N, Vielstich W, Lamm A, Gasteiger HA (eds) (2003) Handbook of fuel cells–fundamentals, technology and applications, vol 2. Wiley, West Sussex, p 534Google Scholar
  27. 27.
    Kim JH, Ishihara A, Mitsushima S, Kamiya N, Ota K (2007) Oxygen reduction reaction of Ta-C-N prepared by reactive sputtering with heat treatment. Electrochemistry 75:166–168Google Scholar
  28. 28.
    Wu G, Chen ZW, Artyushkova K, Garzon FH, Zelenay P (2008) Polyaniline-derived non-precious catalyst for the polymer electrolyte fuel cell cathode. ECS Trans 16:159–170Google Scholar
  29. 29.
    Hamzehie ME, Samiee L, Fattahi M, Seifkordi AA, Shoghi F, Maghsodi A (2015) Synthesis– structure– performance correlation for polyaniline–Me–C non-precious metal cathode based on mesoporous carbon, catalysts for oxygen reduction reaction in fuel cells. Renew Energy 77:558–570Google Scholar
  30. 30.
    Sadegh Hassani S, Ganjali MR, Samiee L, Rashidi AM, Tasharrofi S, Yadegari A, Shoghi F, Martel R (2018) Comparative study of various types of metal-free N and S Co-doped porous graphene for high performance oxygen reduction reaction in alkaline solution. J Nanosci Nanotechnol 18:4565–4579Google Scholar
  31. 31.
    Qu L, Liu Y, Baek JB, Dai L (2010) Nitrogen-doped graphene as efficient metal-free electrocatalyst for oxygen reduction in fuel cells. ACS Nano 4(3):1321–1326Google Scholar
  32. 32.
    Lin Z, Waller G, Liu Y, Liu M, Wong CP (2012) Facile synthesis of nitrogen doped graphene via pyrolysis of graphene oxide and urea, and its electrocatalytic activity toward the oxygen reduction reaction. Adv Energy Mater 2(7):884–888Google Scholar
  33. 33.
    Kwon K, Sa YJ, Cheon JY, Joo SH (2011) Ordered mesoporous carbon nitrides with graphitic frameworks as metal-free, highly durable, methanol-tolerant oxygen reduction catalysts in an acidic medium. Langmuir 28(1):991–996Google Scholar
  34. 34.
    Cakicia M, Kakarla RR, Alonso-Marroquin F (2017) Advanced electrochemical energy storage supercapacitors based on the flexible carbon fiber fabric-coated with uniform coral-like MnO2 structured electrodes. Chem Eng J 309:151–158Google Scholar
  35. 35.
    Arjmandi-Tash H, Belyaeva LA, Schneider GF (2015) Single molecule detection with graphene and other two-dimensional materials: nanopores and beyond. Chem Soc Rev 45:476–493Google Scholar
  36. 36.
    Qiao X, Liao S, You C, Chen R (2015) Phosphorus and nitrogen dual doped and simultaneously reduced graphene oxide with high surface area as efficient metal-free electrocatalyst for oxygen reduction. Catalysts 5(2):981–991Google Scholar
  37. 37.
    Palaniselvam T, Valappil MO, Illathvalappil R, Kurungot S (2014) Nanoporous graphene by quantum dots removal from graphene and its conversion to a potential oxygen reduction electrocatalyst via nitrogen doping. Energy Environ Sci 7(3):1059–1067Google Scholar
  38. 38.
    Yuan W, Chen J, Shi G (2014) Nanoporous graphene materials. Mater Today 17(2):77–85Google Scholar
  39. 39.
    Russo P, Hu A, Compagnini G (2013) Synthesis, properties and potential applications of porous graphene: a review. Nano-Micro Lett 5(4):260–273Google Scholar
  40. 40.
    Guo C, Sun L, Liao W, Li Z (2016) The use of an edible mushroom-derived renewable carbon material as a highly stable electrocatalyst towards four-electron oxygen reduction. Materials 9(1):1–11Google Scholar
  41. 41.
    Tang Y, Allen BL, Kauffman DR, Star A (2009) Electrocatalytic activity of nitrogen-doped carbon nanotube cups. J Am Chem Soc 131:13200–13201Google Scholar
  42. 42.
    Chen Z, Higgins D, Tao H, Hsu RS, Chen Z (2009) Highly active nitrogen-doped carbon nanotubes for oxygen reduction reaction in fuel cell applications. J Phys Chem C 113:21008–21013Google Scholar
  43. 43.
    Vikkisk M, Kruusenberg I, Joost U, Shulga E, Kink I, Tammeveski K (2014) Electrocatalytic oxygen reduction on nitrogen-doped graphene in alkaline media. Appl Catal B 147:369–376Google Scholar
  44. 44.
    Ai W, Luo Z, Jiang J, Zhu J, Du Z, Fan Z, Xie L, Zhang H, Huang W, Yu T (2014) Nitrogen and sulfur codoped graphene: ultifunctional electrode materials for high-performance Li-Ion batteries and oxygen reduction reaction. Adv Mater 26:6186–6192Google Scholar
  45. 45.
    Guo B, Sun XG, Veith GM, Bi Z, Mahurin SM, Liao C, Bridges C, Paranthaman MP, Dai S (2013) Nitrogen-enriched carbons from alkali salts with high coulombic efficiency for energy storage applications. Adv Energy Mater 3:708–712Google Scholar
  46. 46.
    Chen L, Chen Z, Huang Z, Huang Z, Wang Y, Li H, Zhou H, Kuang Y (2015) Composition and oxygen reduction reaction performance of nitrogen-doped carbon material. J Phys Chem C 119:28757–28765Google Scholar
  47. 47.
    Rao CV, Cabrera CR, Ishikawa Y (2010) In search of the active site in nitrogen-doped carbon nanotube electrodes for the oxygen reduction reaction. J Phys Chem Lett 1:2622–2627Google Scholar
  48. 48.
    Lin Z, Gordon H, Waller G, Liu Y, Liu M, Wong CP (2013) Simple preparation of nanoporous few-layer nitrogen-doped graphene for use as an efficient electrocatalyst for oxygen reduction and oxygen evolution reactions. Carbon 53:130–136Google Scholar
  49. 49.
    Ayala P, Arenal R, Rümmeli M, Rubio A, Pichler T (2010) The doping of carbon nanotubes with nitrogen and their potential applications. Carbon 48:575–586Google Scholar
  50. 50.
    Liu H, Zhang Y, Li R, Sun X, Desilets S, Abou-Rachid H, Jaidann M, Lussier LS (2010) Structural and morphological control of aligned nitrogen-doped carbon nanotubes. Carbon 48:1498–1507Google Scholar
  51. 51.
    Bag S, Mondal B, Das AK, Raj CR (2015) Nitrogen and sulfur dual-doped reduced graphene Oxide: synergistic effect of dopants towards oxygen reduction reaction. Electrochim Acta 163:16–23Google Scholar
  52. 52.
    Xu J, Dong G, Jin C, Huang M, Guan L (2013) Sulfur and nitrogen co-doped few layered graphene oxide as a highly efficient electrocatalyst for the oxygen-reduction reaction. ChemSusChem 6:493–499Google Scholar
  53. 53.
    Guo D, Shibuya R, Akiba C, Saji S, Kondo T, Nakamura J (2016) Active sites of nitrogen-doped carbon materials for oxygen reduction reaction clarified using model catalysts. Science 351(6271):361–365Google Scholar
  54. 54.
    Yang Z, Yao Z, Li G, Fang G, Nie H, Liu Z, Zhou X, Xian C, Huang S (2012) Sulfur-doped graphene as an efficient metal-free cathode catalyst for oxygen reduction. ACS Nano 6:205–211Google Scholar
  55. 55.
    Zhang L, Niu J, Li M, Xia Z (2014) Catalytic mechanisms of sulfur-doped graphene as efficient oxygen reduction reaction catalysts for fuel cells. J Phys Chem C 118:3553–3545Google Scholar
  56. 56.
    Li X, Fang Y, Zhao S, Wu J, Li F, Tian M, Long X, Jin J, Ma J (2016) Nitrogen-doped mesoporous carbon nanosheet/carbon nanotube hybrids as metal-free bi-functional electrocatalysts for water oxidation and oxygen reduction. J Mater Chem A 4(34):13133–13141Google Scholar
  57. 57.
    Silva R, Voiry D, Chhowalla M, Asefa T (2013) Efficient metal-free electrocatalysts for oxygen reduction: polyaniline-derived N-and O-doped mesoporous carbons. J Am Chem Soc 135(21):7823–7826Google Scholar
  58. 58.
    Yuan W, Feng Y, Xie A, Zhang X, Huang F, Li S, Zhang X, Shen Y (2016) Nitrogen-doped nanoporous carbon derived from waste pomelo peel as a metal-free electrocatalyst for the oxygen reduction reaction. Nanoscale 8(16):8704–8711Google Scholar
  59. 59.
    Sui ZY, Wang C, Yang QS, Shu K, Liu YW, Han BH, Wallace GG (2015) A highly nitrogen-doped porous graphene–an anode material for lithium ion batteries. J Mater Chem A 3(35):18229–18237Google Scholar
  60. 60.
    Zhou X, Qiao J, Yang L, Zhang J (2014) A review of graphene-based nanostructural materials for both catalyst supports and metal-free catalysts in PEM Fuel cell oxygen reduction reactions. Adv Energy Mater 4:1301523–1301547Google Scholar
  61. 61.
    Razmjooei F, Singh KP, Song MY, JS Y (2014) Enhanced electrocatalytic activity due to additional phosphorous doping in nitrogen and sulfur-doped graphene: a comprehensive study. Carbon 78:257–267Google Scholar
  62. 62.
    Su Y, Zhang Y, Zhuang X, Li S, Wu D, Zhang F, Feng X (2013) Low-temperature synthesis of nitrogen/sulfur co-doped three-dimensional graphene frameworks as efficient metal-free electrocatalyst for oxygen reduction reaction. Carbon 62:296–301Google Scholar
  63. 63.
    Bag S, Roy K, Gopinath CS, Raj CR (2014) Facile single-step synthesis of nitrogen-doped reduced graphene oxide-Mn3O4 hybrid functional material for the electrocatalytic reduction of oxygen. ACS Appl Mater Interfaces 6:2692–2699Google Scholar
  64. 64.
    Pan F, Jin J, Fu X, Liu Q, Zhang J (2013) Advanced oxygen reduction electrocatalyst based on nitrogen-doped graphene derived from edible sugar and urea. ACS Appl Mater Interfaces 5(21):11108–11114Google Scholar
  65. 65.
    Sheng ZH, Shao L, Chen JJ, Bao WJ, Wang FB, Xia XH (2011) Catalyst-free synthesis of nitrogen-doped graphene via thermal annealing graphite oxide with melamine and its excellent electrocatalysis. ACS Nano 5:4350–4358Google Scholar
  66. 66.
    Zhang Y, Ge J, Wang L, Wang D, Ding F, Tao X, Chen W (2013) Manageable N-doped graphene for high performance oxygen reduction reaction. Sci Rep 3:2771–2779Google Scholar
  67. 67.
    Zhou X, Yang Z, Nie H, Yao Z, Zhang L, Huang S (2011) Catalyst-free growth of large scale nitrogen-doped carbon spheres as efficient electrocatalysts for oxygen reduction in alkaline medium. J Power Sources 196(23):9970–9974Google Scholar
  68. 68.
    Xia W, Masa M, Schuhmann W, Muhler M (2011) Highly active metal-free nitrogen-containing carbon catalysts synthesized by thermal treatment of polypyridine-carbon black mixtures for the oxygen reduction in alkaline electrolyte. Electrochem Commun 13:593–596Google Scholar
  69. 69.
    Wu J, Ma L, Yadav RM, Yang Y, Zhang X, Vaitai R, Lou J, Ajayan PM (2015) Nitrogen-doped graphene with pyridinic dominance as a highly active and stable electrocatalyst for oxygen reduction. ACS Appl Mater Interface 7:14763–14769Google Scholar
  70. 70.
    Cong HP, Wang P, Gong M, SH Y (2014) Facile synthesis of mesoporous nitrogen-doped graphene: an efficient methanol–tolerant cathodic catalyst for oxygen reduction reaction. Nano Energy 3:55–63Google Scholar
  71. 71.
    Wu J, Zhang D, Wang Y, Hou B (2013) Electrocatalytic activity of nitrogen-doped graphene synthesized via a one-pot hydrothermal process towards oxygen reduction reaction. Power Sources 227:185–190Google Scholar
  72. 72.
    Yu D, Wei L, jiang W, Wang H, Sun B, Zhang Q, Goh K, Si R, Chen Y (2013) Nitrogen doped holey graphene as an efficient metal-free multifunctional electrochemical catalyst for hydrazine oxidation and oxygen reduction. Nanoscale 5:3457–3464Google Scholar
  73. 73.
    Higgins D, Chen Z, Chen Z (2011) Nitrogen doped carbon nanotubes synthesized from aliphatic diamines for oxygen reduction reaction. Electrochem Acta 56(3):1570–1575Google Scholar
  74. 74.
    Dou S, Huang X, Ma Z, Wu J, Wang S (2015) A simple approach to the synthesis of BCN graphene with high capacitance. Nanotechnology 26:045402–045409Google Scholar
  75. 75.
    Jo G, Sanetuntikul J, Shanmugam S (2013) Boron and phosphorous-doped graphene as metal-free electrocatalyst for oxygen reduction reaction in alkaline medium. RSC Adv 5:53637–53643Google Scholar
  76. 76.
    Wang S, Zhang L, Xia Z, Roy A, Chang DW, Baek JB, Dai L (2012) BCN graphene as efficient metal-free electrocatalyst for the oxygen reduction reaction. Angew Chem Int Ed 51:4209–4212Google Scholar
  77. 77.
    Sudhakara Prasad K, Pallela R, Kim DM, Shim YB (2013) Microwave-assisted one-pot synthesis of metal-free nitrogen and phosphorus dual-doped nanocarbon for electrocatalysis and cell imaging. Part Part Syst Charact 30:557–564Google Scholar
  78. 78.
    Wang Y, Zhang B, Xu M, He X (2015) Tunable ternary (P, S, N)-doped graphene as an efficient electrocatalyst for oxygen reduction reaction in an alkaline medium. RSC Adv 5:86746–86753Google Scholar
  79. 79.
    Lin H, Chu L, Wang X, Yao Z, Liu F, Ai Y, Zhuang X, Han S (2016) Boron, nitrogen and phosphorous ternary doped graphene aerogel with hierarchically porous structures as highly efficient electrocatalysts for oxygen reduction reaction. New J Chem 40:6022–6029Google Scholar

Copyright information

© Springer Nature Switzerland AG 2019

Authors and Affiliations

  1. 1.Nanotechnology Research CenterResearch Institute of Petroleum Industry (RIPI)TehranIran
  2. 2.Development and Optimization of Energy Technologies Research DivisionResearch Institute of Petroleum Industry (RIPI)TehranIran

Personalised recommendations