Abstract
A mathematical representation has been developed, and computed results are presented describing the spreading and solidification of droplets impacting onto a solid substrate. This impingement is of major practical interest in plasma spraying and spray forming operations. Experiments in which molten metal drops were made to impinge onto a substrate were used to test the model. High-speed videography was used to record the spreading process, which typically took a few milliseconds for the experimental conditions employed. A comparison was made of the theoretical predictions with the experimental measurements; these were found to be in very good agreement, suggesting that the theoretical treatment of the model is sound. These calculations permit the prediction of the time and extent of the spreading process, the solidification rate, and the effect of process parameters, such as droplet size, droplet velocity, superheat, and material properties, provided that a value of the thermal contact coefficient is known. The most important finding of the modeling work is that for large droplets (∼5-mm diameter) with low impinging velocities (∼2 m/s), spreading and solidification appear to take place at comparable rates; in contrast, for small (∼100−µm diameter) particles impacting at a high velocity (∼100 m/s), the time scale for spreading appears to be shorter than the time scale for solidification (within the range of parameters of this study.)
Similar content being viewed by others
References
A.R.E. Singer: inCasting of Near Net Shape Products, Y. Sahai, J.E. Battles, R.S. Carbonara, and C.E. Mobley, eds., TMS, Warrendale, PA, 1988.
A.R.E. Singer:Int. J. Powder Metall. Powder Technol., 1985, vol 21 (3).
A.G. Leatham, R.G. Brooks, and M. Yaman: inModern Developments in Powder Metallurgy, Metal Powder Industries Federation, Princeton, NJ, 1984, vol. 15, p. 157.
R.G. Brooks, C. Moore, A.G. Leatham, and J.S. Coombs:Metall. Met. Form., 1977, vol. 44, pp. 157–63.
B.A. Rickinson, F.A. Kirk, and D.R.G. Davis:Powder Metall., 1981, vol. 24 (1), pp. 1–6.
S. Annavarapu, D. Apelian, and A. Lawley:Metall. Trans. A, 1988, vol. 19A, pp. 3077–86.
E.J. Lavernia and N.J. Grant:Mater. Sci. Eng., 1988, vol. 98, pp. 381–94.
N. El-Kaddah, J. McKelliget, and J. Szekely:Metall. Trans. B, 1984, vol. 15B, pp. 59–70.
E. Gutierrez-Miravete, E.J. Lavernia, G.M. Trapaga, J. Szekely, and N.J. Grant:Metall. Trans. A, 1989, vol. 20A, pp. 71–85.
P. Mathur, D. Apelian, and A. Lawley:Ada Metall., 1989, vol. 37, p. 429.
P. Mathur, S. Annavarapu, D. Apelian, and A. Lawley:J. Met., 1989, vol. 41 (10), pp. 23–28.
G. Hartmann, P.N. Hansen, and P.R. Sahm: inModeling and Control of Casting and Welding Processes IV, A.F. Giamei and G.J. Abbaschian, eds., TMS, Warrendale, PA, 1988, p. 915.
E. Gutierrez-Miravete, G. Trapaga, and J. Szekely: inCasting of Near Net Shape Products, Y. Sahai, J.E. Battles, R.S. Carbonara, and C.E. Mobley, eds., TMS, Warrendale, PA, 1988, pp. 133–51.
G. Trapaga and J. Szekely:Metall. Trans. B, 1991, vol. 22B, pp. 901–14.
J. Madejski:Int. J. Heat Mass Transfer, 1976, vol. 19, pp. 1009–13.
P. Savic and G.T. Boult:Proc. Heat Trans. Fluid Mech. Inst., 1957, pp. 43–83.
P. Duwez and R.H. Willens:Trans. TMS-AIME, 1963, vol. 227, pp. 362–65.
D.R. Harbur, J.W. Anderson, and W.J. Maraman;Trans. TMS-AIME, 1969, vol. 245, pp. 1055–61.
K. Miyazawa and J. Szekely:Metall. Trans. B, 1979, vol. 10B, pp. 349–58.
N.J. Grant:J. Met., 1983, January, pp. 20–27.
P. Predecki, A.W. Mullendore, and N.J. Grant: Trans. TMS-AIME, 1965, vol. 233, pp. 1581–86.
R. Mehrabian, S.C. Hsu, CG. Levi, and S. Kou: inAdvances in Metal Processing, 1981, pp. 13–43.
H. Jones:J. Phys. D: Appl. Phys., 1971, vol. 4, pp. 1657–60.
C.A. Williams and H. Jones:Mater. Sci. Eng., 1975, vol. 19, pp. 293–97.
R.C Rhul:Mater. Sci. Eng., 1967, vol. 1, pp. 313–20
T.W. Clyne:Metall. Trans. B, 1984, vol. 15B, pp. 369–81.
B. Cantor: inScience and Technology of the Undercooled Melt: Rapid Solidification of Materials and Technologies, P.R. Sahm, H. Jones, and C.M. Adam, eds., Martinus Nijhoff Publishers, Dordrecht, The Netherlands, 1986.
G.X. Wang and E.F. Matthys:Int. J. Rapid Solidif, 1991, vol. 6, pp. 297–324.
FLOW-3D, Report No. FSI-87-33-1, Flow Science, Inc., Los Alamos, NM 1987.
FLOW-3D, Report No. FSI-88-00-1, Flow Science, Inc., Los Alamos, NM, 1988, vol. 1–4.
Valencia J.J., C. McCullough, C.G. Levi, and R. Mehrabian:Acta Metall., 1989, vol. 37, pp. 2517–30.
Wilde P.W. and E.F. Matthys: Technical report No. UCSB-ME-90-7, University of California, Santa Barbara, 1990.
Author information
Authors and Affiliations
Additional information
J.J. VALENCIA, formerly Postdoctoral Researcher with UCSB
This article is based on a presentation made in the symposium “Spray Processing Fundamentals: Coating and Deposition” presented as part of the 1990 TMS Fall Meeting, October 9, 1990, in Detroit, MI, under the auspices of the TMS Synthesis and Analysis in Materials Processing Committee.
Rights and permissions
About this article
Cite this article
Trapaga, G., Matthys, E.F., Valencia, J.J. et al. Fluid flow, heat transfer, and solidification of molten metal droplets impinging on substrates: Comparison of numerical and experimental results. Metall Trans B 23, 701–718 (1992). https://doi.org/10.1007/BF02656450
Issue Date:
DOI: https://doi.org/10.1007/BF02656450