Effects of Solution Temperature on Microstructure and Properties of Fe–Mn–Al–C Ferrite-Based Steel

  • Xuan Li
  • Renbo Song
  • Naipeng Zhou
  • Jiajia Li
  • Lun Li
Conference paper
Part of the Lecture Notes in Mechanical Engineering book series (LNME)

Abstract

The effects of solution temperature of 700–950 °C on microstructure and properties of Fe–8Mn–6Al–0.2C ferrite-based steel were investigated. Optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) and X-ray diffraction (XRD) were used to study the morphology and composition of microstructure. The tensile test at room temperature was used to detect mechanical properties. The results showed that the as-hot-rolled steel exhibited a complex microstructure, consisting of banded ferrite, martensite and small amount of retained austenite. With the increase of solution temperature, δ-ferrite solidified from the liquid phase and existed during subsequent heat treatment at all the temperatures, while the other phases varied from M5C2, α-ferrite, austenite and martensite. At 900 °C, dual phase microstructure with ferrite and island of austenite was obtained. With increasing solution temperature, the ultimate tensile strength (UTS) decreased at first and then increased after reaching the minimum at 850 °C, while the total elongation (TE) increased firstly and declined after the peak value of 44.5% at 850 °C. Therefore, the as-hot-rolled experimental steel heat treated at 900 °C had an excellent combination of tensile strength and elongation, with UTS of 846.4 MPa, TE of 32%, and UTS × TE of 27.1 GPa%. The remarkable mechanical properties, both strength and elongation, were attributed to the relative fraction and stability of austenite. And the partition of elements, especially for Mn, had great effect on the austenite stability.

Keywords

Fe–Mn–Al–C steel Solution temperature Microstructure evolution Mechanical properties 

References

  1. 1.
    R. Sun, W. Xu, C. Wang et al., Work hardening behavior of ultrafine grained duplex medium-Mn steels processed by ART-annealing. Steel Res. Int. 83(4), 316–321 (2012)CrossRefGoogle Scholar
  2. 2.
    L. Zhang, R. Song, C. Zhao, F. Yang, S. Qin, Y. Xu, Mater. Rev. 28(19), 111–118 (2014)Google Scholar
  3. 3.
    P.J. Jacques, Transformation-induced plasticity for high strength formable steels. Curr. Opin. Solid State Mater. Sci. 8(3–4), 259–265 (2004)CrossRefGoogle Scholar
  4. 4.
    Z.H. Cai, H. Ding, R.D.K. Misra et al., Unique serrated flow dependence of critical stress in a hot-rolled Fe–Mn–Al–C steel. Scripta Mater. 71(2), 5–8 (2014)CrossRefGoogle Scholar
  5. 5.
    S. Zaefferer, J. Ohlert, W. Bleck, Acta Mater. 52(9), 2765–2778 (2004)CrossRefGoogle Scholar
  6. 6.
    Z. Cai, H. Ding, Z. Ying et al., J. Mater. Eng. Perform. 23(4), 1131–1137 (2014)CrossRefGoogle Scholar
  7. 7.
    Z.C. Li, R.D.K. Misra, Z.H. Cai et al., Mechanical properties and deformation behavior in hot-rolled 0.2C–1.5/3Al–8.5Mn–Fe TRIP steel: the discontinuous TRIP effect. Mater. Sci. Eng., A 673, 63–72 (2016)CrossRefGoogle Scholar
  8. 8.
    R. Rana, C. Liu, R.K. Ray, Evolution of microstructure and mechanical properties during thermomechanical processing of a low-density multiphase steel for automotive application. Acta Mater. 75(16), 227–245 (2014)CrossRefGoogle Scholar
  9. 9.
    C.H. Seo, K.H. Kwon, K. Choi et al., Deformation behavior of ferrite–austenite duplex lightweight Fe–Mn–Al–C steel. Scripta Mater. 66(8), 519–522 (2012)CrossRefGoogle Scholar
  10. 10.
    S.S. Sohn, B.J. Lee, S. Lee et al., Effect of annealing temperature on microstructural modification and tensile properties in 0.35 C–3.5 Mn–5.8 Al lightweight steel. Acta Mater. 61(13), 5050–5066 (2013)CrossRefGoogle Scholar
  11. 11.
    Z.C. Li, H. Ding, R.D.K. Misra et al., Microstructure-mechanical property relationship and austenite stability in medium-Mn TRIP steels: the effect of austenite-reverted transformation and quenching-tempering treatments. Mater. Sci. Eng., A 682, 211–219 (2017)CrossRefGoogle Scholar
  12. 12.
    P.J. Gibbs, E.D. Moor, M.J. Merwin et al., Austenite stability effects on tensile behavior of manganese-enriched-austenite transformation-induced plasticity steel. Metall. Mater. Trans. A 42(12), 3691–3702 (2011)CrossRefGoogle Scholar
  13. 13.
    A. Dosho, K. Kakefuda, X-ray diffraction measurement method and X-ray diffraction apparatus. US, US7443952 (2008)Google Scholar
  14. 14.
    M. Zhang, W. Cao, H. Dong et al., Mater. Sci. Eng., A 654, 193–202 (2016)CrossRefGoogle Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2018

Authors and Affiliations

  • Xuan Li
    • 1
  • Renbo Song
    • 1
  • Naipeng Zhou
    • 1
  • Jiajia Li
    • 1
  • Lun Li
    • 2
  1. 1.School of Materials Science and EngineeringUniversity of Science and Technology BeijingBeijingChina
  2. 2.Anshan Steel Group Corporation LimitedEast Anshan Sintering PlantAnshanChina

Personalised recommendations