Precipitation Behavior of 1.3%Si Non-oriented Silicon Steels During Strip Casting Process

  • Feng Fang
  • Xiang Lu
  • Mengfei Lan
  • Yuanxiang Zhang
  • Yang Wang
  • Guangming Cao
  • Guo Yuan
  • Yunbo Xu
  • Guodong Wang
Conference paper
Part of the Lecture Notes in Mechanical Engineering book series (LNME)

Abstract

In this work, the precipitation behaviors of 1.3%Si non-oriented silicon steel during the sub-rapid solidification process under different melt superheat were investigated using scanning electron microscope and transmission electron microscope, based on strip casting process. The results showed that the precipitates of as-cast strips were dominated by coarse AlN, and MnS particles were seldom observed. The mean size of AlN particles rapidly increased from 75 to 1060 nm, and the volume fraction increased from 0.028 to 0.069%, when the melt superheat increased from 20 to 70 °C. Besides, the precipitation quantity in the center layer of as-cast strip was obviously more than the surface layer. According to the different solubility ability in the liquid and ferrite matrix, Al or N elements tend to segregate during the sub-rapid solidification process, which is attributed to the nucleation and coarsening of AlN. On the condition of low melt superheat, the solidified layers suffered from hot deformation from the solidification end point to the nip point, which provided additional nucleation sites for precipitates and can be attributed to fine particles size. In addition, different heat conductivity and hot deformation degree in various thickness layer resulted in inhomogeneous distribution of particles through the thickness of as-cast strips.

Keywords

Strip casting Non-oriented silicon steel Precipitation behavior Melt superheat 

Notes

Acknowledgements

The authors acknowledge support by the National Natural Science Foundation of China (Nos. 51674080 and 51774083), the Program for New Century Excellent Talents in University (NCET-13-0111) and the Program for Liaoning Excellent Talents in University (LR2014007).

References

  1. 1.
    F.J.G. Landgraf, Nonoriented electrical steels. J. Miner. Met. Mater. Soc. 64, 764–771 (2012)CrossRefGoogle Scholar
  2. 2.
    K. Jenkins, M. Lindenmo, Precipitates in electrical steels. J. Magn. Magn. Mater. 320, 2423–2429 (2008)CrossRefGoogle Scholar
  3. 3.
    T. Semuma, Present status of and future prospects for precipitation research in the steel industry. ISIJ Int. 42, 1–12 (2002)CrossRefGoogle Scholar
  4. 4.
    L. Xiang, E.B. Yue, D.D. Fan et al., Calculation of AIN and MnS precipitation in non-oriented electrical steel produced by CSP process. J. Iron. Steel Res. Int. 15, 88–94 (2008)CrossRefGoogle Scholar
  5. 5.
    J.Y. Park, K.H. Oh, H.Y. Ra, Microstructure and crystallographic texture of strip cast 4.3 wt% Si steel sheet. Scr. Mater. 40, 881–885 (1999)CrossRefGoogle Scholar
  6. 6.
    H.T. Liu, Z.Y. Liu, C.G. Li et al., Solidification structure and crystallographic texture of strip casting 3 wt% Si non-oriented silicon steel. Mater. Charact. 62, 463–468 (2011)CrossRefGoogle Scholar
  7. 7.
    Y.X. Zhang, Y.B. Xu, H.T. Liu et al., Microstructure, texture and magnetic properties of strip-cast 1.3%Si non-oriented electrical steels. J. Magn. Magn. Mater. 324, 3328–3333 (2012)CrossRefGoogle Scholar
  8. 8.
    Y.B. Xu, Y.X. Zhang, Y. Wang et al., Evolution of cube texture in strip-cast non-oriented silicon steels. Scr. Mater. 87, 17–20 (2014)CrossRefGoogle Scholar
  9. 9.
    J.S. Mou, H.T. Jiao, Q.Q. Han, et al., Characterization of precipitates in strip-cast 2.7%Si steel under different heat treatment conditions, in MATEC Web of Conferences, vol. 21 (2015) 07004CrossRefGoogle Scholar
  10. 10.
    J.Y. Park, K.H. Oh, H.Y. Ra, Texture and deformation behavior through thickness direction in strip-cast 4.5 wt%Si steel sheet. ISIJ Int. 40, 1210–1215 (2000)CrossRefGoogle Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2018

Authors and Affiliations

  • Feng Fang
    • 1
  • Xiang Lu
    • 1
  • Mengfei Lan
    • 1
  • Yuanxiang Zhang
    • 1
  • Yang Wang
    • 1
  • Guangming Cao
    • 1
  • Guo Yuan
    • 1
  • Yunbo Xu
    • 1
  • Guodong Wang
    • 1
  1. 1.State Key Laboratory of Rolling and AutomationNortheastern UniversityShenyangChina

Personalised recommendations