Effect of Solution Treatment on Microstructure and Properties of GH3625 Alloy Tubes in Different States

  • Yutian Ding
  • Bin Meng
  • Yubi Gao
  • Yuanjun Ma
  • Jianjun Chen
Conference paper

Abstract

The influence of solution treatment temperature on microstructure evolution and mechanical properties of the GH3625 alloy tubes in different states (hot extrusion, cold rolled and annealed) were investigated by organization characterization(OM, SEM) and performance tests (hardness test and tensile test at room temperature). The results showed that the mixed grain structure of the hot extruded GH3625 alloy degraded and transformed into uniform equiaxed grain structure, as the solution treatment temperature was 1000 °C. When the solution temperature was higher than 1050 °C, the microstructure of the cold rolling GH3625 alloy was uniform equiaxed grain, and the solution amount of the carbides increases with the increase of the solution temperature. The microstructure of annealed GH3625 alloy in the whole solution temperature range (950–1150 °C) was fully recrystallized equiaxed grain, and there were a large number of lath-shaped annealed twins in the grains. The microstructure and mechanical properties of the GH3625 alloy during the solution treatment were not only affected by the solution temperature, but also influenced by the original states. After solid solution treatment at 1150 °C for 60 min and then water-cooling, the tensile fracture modes of GH3625 alloy tubes under different conditions was ductile fracture. The temperature of 1150 °C can be used as the reference temperature for optimizing the microstructure and properties of GH3625 alloy through solution treatment in different states.

Keywords

GH3625 alloy Solution treatment Microstructure Mechanical properties 

Notes

Acknowledgements

This study was funded by the National Natural Science Foundation of China (No. 51661019), The Science and Technology Projects of Gansu Province (No. 145RTSA004), The State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology.

References

  1. 1.
    E. Loria, Superalloys 718, 625, 706 and Various Derivatives (1997).Google Scholar
  2. 2.
    G.E. Maurer, A.D. Patel, Alloy Design and Processing Challenges for Advanced Power Systems: An Alloy Producer’s Perspective, J. Advances in Science & Technology, 72 (2010) 22–30.Google Scholar
  3. 3.
    M.D. Mathew, P. Parameswaran, K.B.S. Rao, Microstructural changes in alloy 625 during high temperature creep, J. Materials Characterization, 59 (2008) 508–513.Google Scholar
  4. 4.
    S. Floreen, G.E. Fuchs, W.J. Yang. The Metallurgy of Alloy 625, J. in Superalloys (1994).Google Scholar
  5. 5.
    M. Sundararaman, P. Mukhopadhyay, S. Banerjee. Carbide Precipitation in Nickel Base Superalloys 718 and 625 and Their Effect on Mechanical Properties, J. in Superalloys, (1997).Google Scholar
  6. 6.
    P.J. Maziasz, Defining the Materials Issues and Research for Ultra-Supercritical Steam Turbines, J. (2005).Google Scholar
  7. 7.
    J.P. Shingledecker, I.G. Wright, Evaluation of the Materials Technology Required for a 760 °C Power Steam Boiler, J. Boilers (2006).Google Scholar
  8. 8.
    L. Garcia-Fresnillo, A. Chyrkin, C. Böhme, J. Barnikel, F. Schmitz, Oxidation behaviour and microstructural stability of alloy 625 during long-term exposure in steam, J. Journal of Materials Science, 49.17 (2014) 6127–6142.Google Scholar
  9. 9.
    D. Tian, Development and production of high-temperature alloy seamless tubulars, J. Steel Pope. 31.3(2002)1–6 (in Chinese).Google Scholar
  10. 10.
    J.X. Dong, Extrusion and tissue control of nickel - based alloy tubes. Metallurgical Industry Press, 2014.Google Scholar
  11. 11.
    G.E. Fuchs, Improvement of creep strength of a third generation, single-crystal Ni-base superalloy by solution heat treatment, J. Journal of Materials Engineering & Performance. 11 (2002) 19–25.Google Scholar
  12. 12.
    B.C. Wilson, J.A. Hickman, G.E. Fuchs, The effect of solution heat treatment on a single-crystal Ni-based superalloy, J. JOM. 55 (2003) 35–40.Google Scholar
  13. 13.
    M. Liu, W.J. Zheng, J.Z. Xiang, Z.G. Song, P.U. En-Xiang, Grain Growth Behavior of Inconel 625 Superalloy, J. Journal of Iron & Steel Research International, 23 (2016) 1111–1118.Google Scholar
  14. 14.
    X.D. Fang, D.P. Han, Y. Li, Effect of heat treatment on microstructure and mechanical properties of GH625 alloy hot extruded pipe, J. Hot Working Technology, 4 (2013) 35 (in Chinese).Google Scholar
  15. 15.
    D.X. Liu, X.W. Cheng, X. Zhang, Effects of Heating and Hot Extrusion Process on Microstructure and Properties of Inconel 625 Alloy, J. Journal of Wuhan University of Technology(Materials Science), 31 (2016) 1368–1376.Google Scholar
  16. 16.
    Y. Wu, M. Zhang, X. Xie, F. Lin,S. Zhao, Dynamic recrystallization of a new nickel-based alloy for 700 °C A-USC power plant applications with different initial states: as-homogenized and as-forged, J. Materials Science & Engineering A, 662 (2016) 283–295.Google Scholar
  17. 17.
    W.F. Smith, J. Hashemi, Foundations of materials science and engineering, J. 16 (2006)1–11.Google Scholar
  18. 18.
    D. Li, Q. Guo, S. Guo, H. Peng, Z. Wu, The microstructure evolution and nucleation mechanisms of dynamic recrystallization in hot-deformed Inconel 625 superalloy, J. Materials & Design, 32 (2011) 696–705.Google Scholar
  19. 19.
    H. U. Hong, H.W. Jeong, I. S.Kim, B.G. Choi, Y.S. Yoo, Significant decrease in interfacial energy of grain boundary through serrated grain boundary transition, J. Philosophical Magazine, 92 (2012) 2809–2825.Google Scholar
  20. 20.
    J.B. Singh, J.K. Chakravartty, M. Sundararaman, Work hardening behaviour of service aged Alloy 625, J. Materials Science & Engineering A, 576 (2013) 239–242.Google Scholar
  21. 21.
    W.M. Miao, Metal recrystallization and grain growth. Metallurgical Industry Press (1994).Google Scholar
  22. 22.
    C.X. Huang, G. Yang, Y.L. Gao, S.D. Wu, Z.F. Zhang, Influence of processing temperature on the microstructures and tensile properties of 304L stainless steel by ECAP, J. Materials Science & Engineering A, 485 (2008) 643–650.Google Scholar
  23. 23.
    J.L. Bair, S.L. Hatch, D.P. Field, Formation of annealing twin boundaries in nickel, J. Scripta Materialia, 81 (2014) 52–55.Google Scholar
  24. 24.
    G. Yang, L.J. Sun, L.N. Zhang, L.M. Wang, C. Wang, Annihilation of deformation twins and formation of annealing twins, J. Journal of Iron and Steel Research, 21 (2009) 39–43 (in Chinese).Google Scholar
  25. 25.
    S. Dash, N. Brown, An investigation of the origin and growth of annealing twins ☆, J. ActaMetallurgica, 11 (1963) 1067–1075.Google Scholar
  26. 26.
    Z. Tang, J. Li, R. Hu, Y. Liu, G. Bai, Effects of Solution Heat Treatment on Carbide of Ni-Cr-W Superalloy, J. Rare Metal Materials & Engineering, 39 (2010) 1157–1161.Google Scholar
  27. 27.
    G. Yang, C. Wang, L.Y. Zhang, C.X. Huang, Z.D. Liu, Recovery and recrystallization mechanism in austenitic stainless steel, J. Transactions of Materials and Heat treatment, 31 (2010) 51–55.Google Scholar
  28. 28.
    P. Li, S.S. Li, Y.F. Han, Influence of solution heat treatment on microstructure and stress rupture properties of a Ni-Al base single crystal superalloy IC6SX, J. Intermetallics, 19 (2011) 182–186.Google Scholar
  29. 29.
    D. Hull, Fractography: observing, measuring, and interpreting fracture surface topography, 1999: Cambridge University Press. 83.Google Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2018

Authors and Affiliations

  • Yutian Ding
    • 1
  • Bin Meng
    • 1
  • Yubi Gao
    • 1
  • Yuanjun Ma
    • 1
  • Jianjun Chen
    • 1
  1. 1.State Key Laboratory of Advanced Processing and Recycling of Nonferrous MetalsLanzhou University of TechnologyLanzhouChina

Personalised recommendations