Study on Rolling Process of Doped Tungsten Sheets

  • Mei Gui Qi
  • Ai Long Zheng
  • Rong Kui Fan
  • Zhi Min Huang
  • Fu Sheng Peng
  • Yong Hua Xie
Conference paper

Abstract

The evolution of density of tungsten sheets with different dopant content is studied. The microstructure evolution and annealing behavior of three kinds of tungsten sheets with deformation of 63, 83, 92%, are studied. The results show that when rolling deformation reaches to 92%, the density of lanthanum-doped tungsten sheets increases from 18.4 to 18.9 g/cm3, and the density of Potassium-doped tungsten sheets increases from 17.6 to 19.15 g/cm3. The deformation of lanthanum oxide particles increases with the increment of deformation, and the tungsten sheets exhibit a typical rolling state. The microstructure of doped tungsten sheets at high temperature is more stable than that of the pure tungsten ones.

Keywords

Tungsten plates Rolling Sheet Doping 

References

  1. 1.
    Zhang Qixiao, Zhao Qinsheng. Tungsten and molybdenum metallurgy [M]. Beijing: Metallurgical Industry Press, (2005) 1–10.Google Scholar
  2. 2.
    Fan Jinglian. Tungsten alloy and its preparation technology [M]. Beijing: Metallurgical Industry Press, 2006.Google Scholar
  3. 3.
    Huang Peiyun. Powder metallurgy principle (2nd edition) [M]. Beijing: Metallurgical Industry Press, 2008.Google Scholar
  4. 4.
    Liu Guohui, Song Peng, Wu Cheng, et al. Study on texture evolution and properties of rolling tungsten plate annealing process [J]. Powder Metallurgy Industry, 24(6) (2014) 6–10.Google Scholar
  5. 5.
    Zhang Junliang. Tungsten bar step rolling [J]. Rare Metal Express, 23(1) (2004) 34–37.Google Scholar
  6. 6.
    Zhou Meiling, Zuo Tieyong. Study on deformation and organization in the process of swaging forging [J]. Journal of Central South University of Mining and Technology, 4 (1984) 11–18.Google Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2018

Authors and Affiliations

  • Mei Gui Qi
    • 1
  • Ai Long Zheng
    • 1
  • Rong Kui Fan
    • 2
  • Zhi Min Huang
    • 1
  • Fu Sheng Peng
    • 1
  • Yong Hua Xie
    • 2
  1. 1.Xiamen Honglu Tungsten Molybdenum Industry Co., Ltd.XiamenChina
  2. 2.Chengdu Lianhong Molybdenum Industry Co., Ltd.ChengduChina

Personalised recommendations