Abstract
SAF 2507® is a super duplex stainless steel (SDSS), widely used in highly corrosive environments where high strength is required, for example in offshore and chemical industries. It is known that SDSS below room temperature exhibits a ductile-to-brittle transition in fracture behaviour. The present study is aimed at understanding this behaviour in SDSS weldments using instrumented impact toughness testing. Testing was performed between the room temperature and liquid nitrogen temperature (−196 °C) on the base metal, tungsten inert gas welding (TIG) and submerged arc welding (SAW) material. Results showed that there is a significant difference in the ductile-to-brittle transition temperature (DBTT) between the base metal and the weld metal. In base metal, DBTT was observed to be about −75 °C, −105 °C in TIG weld metal and −55 °C in SAW weld metal. This shows that the DBTT is lowered for the TIG weld metal than compared to the base metal and SAW weld metal due to finer distribution of austenite in the microstructure. The possible reasons for the change in fracture behaviour are discussed.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
References
Nilsson JO (1992) Super duplex stainless steels. Mater Sci Technol 8:685–700
Gunn RN (1997) Duplex stainless steels—microstructure, properties and applications. Woodhead Publishing Ltd., Abington Hall
Ibrahim OH, Ibrahim IS, Khalifa TAF (2010) Impact behavior of different stainless steel weldments at low temperatures. Eng Fail Anal 17:1069–1076
Fager SA, Odegard L (1993) Welding of the super duplex stainless steel sandvik SAF2507™ (UNS S32750). In: Proceedings of the third internal offshore and polar engineering conference, Singapore, 6–11 June, pp 416–423
Welding guideline for SAF 2507, Sandvik internal report
ASME VIII (1989) Rules for construction of pressure vessels, ASME
Han G, Fukuyama S, Yokogawa K (1999) Tensile behavior of duplex stainless steel at low temperatures. Mater Sci Technol 15:909–920
Chai G, Ronneteg S, Kivisäkk U, Peng RL, Johansson S (2009) Mechanisms of hydrogen induced stress crack initiation and propagation in super duplex stainless steels. Steel Res Int 80:482–487
Acknowledgements
Authors would like to acknowledge AB Sandvik Materials Technology for providing the financial support and permission to publish the work.
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2018 Springer Nature Singapore Pte Ltd.
About this paper
Cite this paper
Gaddam, R., Chai, G., Stenvall, P. (2018). Impact Behaviour of Super Duplex Stainless Steel Weldments at Sub-Zero Temperatures. In: Muruganant, M., Chirazi, A., Raj, B. (eds) Frontiers in Materials Processing, Applications, Research and Technology. Springer, Singapore. https://doi.org/10.1007/978-981-10-4819-7_28
Download citation
DOI: https://doi.org/10.1007/978-981-10-4819-7_28
Published:
Publisher Name: Springer, Singapore
Print ISBN: 978-981-10-4818-0
Online ISBN: 978-981-10-4819-7
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)