Abstract
The gas turbine components of jet engines and power plants are usually subjected to cyclic stresses and strains during thermal transients induced by start up and shut down. The resulting thermal/mechanical fatigue cycling determines times to failure and fracture mode of the components that are not always well reproduced by laboratory isothermal low cycle fatigue tests. In order to improve the information on high temperature mechanical properties of the alloys used for turbine components like vanes and blades, the thermal mechanical fatigue technique was introduced several years ago [1, 2]. The most important advantage of this technique is the capability to test the material with temperature and strain conditions as close as possible to those of the components in service, in particular for those new, high technology alloys that may exhibit peculiar response to in service loading, due to heterogeneity, anisotropy, etc. [3].
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Preview
Unable to display preview. Download preview PDF.
References
Rau, C.A., Jr., Gemma, A.E. and Leverant, G.R., Fatigue at Elevated Temperature, ASTM STP 520, American Society for Testing and Materials, 1973, 166–178.
Hopkins, S.W., Low Cycle Thermal Mechanical Fatigue Testing, ASTM STP 612, Spera D.A. and Mowbray D.F., (Eds.), American Society for Testing and Materials, 1976, 157–169.
Guèdou, J. Y. and Honnorat, Y., Thermomechanical Fatigue Behaviour of Materials, ASTM STP 1186, Sehitoglu H. (Ed), American Society for Testing and Materials, 1993, 157–175.
Malpertu, J.L. and Rémy L., Low Cycle Fatigue, ASTM STP 942, Solomon, H.D. et al. (Eds.), American Society for Testing and Materials, 1988, 657–671.
Shi, H.J., Robin, C. and Plevinage, G., Advances in Fatigue Lifetime Predictive Techniques, second Volume, ASTM — STP 1211, Mitchell, M.R. and Landgraf R.W. (Eds.), American Society for Testing and Materials 1993, 105–116.
Bernstein, H.L. et al., Prediction of thermal-mechanical fatigue life for gas turbines in electric power generation, ASTM — STP 1186, Sehitoglu, H. (Ed), American Society for Testing and Materials, 1993, 212–238.
Hack, G.A.J., Inconel Alloy MA 6000 A new material for high temperature turbine blades. Metal Powder Report, 36, (1981).
Janson, J. and Samuelsson, H., Anisotropic Elastic Analysis of uncooled ODS vane, Cost 501 Progress Report, September 1991.
Jaske, C.E., Thermal-mechanical, Low Cycle Fatigue of AISI 1010 Steel, ASTM STP 612, Spera D.A. and Mowbray, D.F. (Eds.), American Society for Testing and Materials, 1976, 170–198.
Marchionni, M., Bressers, J., Joos, R., Rémy, L., Timm, J., Vasseur, E., Low cycle and thermomechanical fatigue behaviour of an advanced ODS nickel-base superalloy, Proc. of the Conference Materials for Advanced Power Engineering, 1994, Liege, Vol. II, 1994, pp. 989–998.
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 1996 Springer Science+Business Media Dordrecht
About this chapter
Cite this chapter
Marchionni, M., Ranucci, D., Picco, E. (1996). Influence of Cycle Shape and Specimen Geometry on TMF of an ODS Nickel-Base Superalloy. In: Bressers, J., Rémy, L., Steen, M., Vallés, J.L. (eds) Fatigue under Thermal and Mechanical Loading: Mechanisms, Mechanics and Modelling. Springer, Dordrecht. https://doi.org/10.1007/978-94-015-8636-8_18
Download citation
DOI: https://doi.org/10.1007/978-94-015-8636-8_18
Publisher Name: Springer, Dordrecht
Print ISBN: 978-90-481-4688-8
Online ISBN: 978-94-015-8636-8
eBook Packages: Springer Book Archive