Dynamic crack propagation in thin, edge notched polystyrene specimens was studied by the method of dynamic caustics. During the crack propagation, an intensive zone of crazing surrounds and precedes the propagating crack. SO, an active zone ahead of the crack tip is developed. This active zone is related to the velocity of crack propagation and the strain rate of loading. The velocity of the crack and the stress intensity factor K. or the fracture surface energy y were strongly influenced by the development of the active zone at the crack tip.
Keywords
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Preview
Unable to display preview. Download preview PDF.
References
Botsis, J., Chudnovski, A. and Moet, A., Fatigue crack layer propagation in polystyrene-Part I. Experimental observations. Int. J. Fracture, 1987, 33, 263–276.
Botsis, J., Chudnovski, A. and Moet, A., Fatigue crack layer propagation in polystyrene — Part II. Analysis. Int. J. Fracture, 1987, 33, 277–284.
Chudnovski, A. and Moet, A., Thermodynamics of translational crack layer propagation. J. Mater. Sci., 1985, 20, 630–635.
Rice, J.R., Mathematical analysis in mechanics of f racture. in Fracture, Ed. H. Liebowitz, Academic Press, NY 1964, Vol. II, 192–308.
Burech, F.E., About the process zones surrounding the crack tip in ceramics. in Fracture, Pergamon Press, London 1972, 3, 929–950.
Claussen, N., J. Amer. Ceram. Sco., 1976, 59, 49–60.
Pompe, H.A., Bahr, H.A., Gille, G. and Kreher, W., Increased fracture toughness of brittle materials by microcracking in a energy dissipative zone at the crack tip. J. Mater. Sci., 1978, 13, 2720–2723.
Donald, A.M. and Kramer, E.J., Micromechanics and kinetics of deformation zones at crack tips in polycarbonate. J. Mater. Sci., 1981, 16, 2977–2987.
Theocaris, P.S. and Papadopoulos, G.A., Elastodynamic forms of caustics for running cracks under constant velocity. Engng Fracture Mech., 1980, 13, 683–698.
Theocaris, P.S. and Papadopoulos, G., Mixed — mode dynamic stress-intensity factors from caustics. ASTM STP 791, 1983, 11320–11337.
Papadopoulos, G.A. and Theocaris, P.S., The variation of the dynamic modulus on crack propagation modes. Int. J. Fracture, 1987, 35, 195–219.
Griffith, A.A., The phenomenon of rupture and flow in solids. Phil. Trans. Roy. Soc., London, Ser. A, 1920, 221, 163–198.
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 1991 Elsevier Science Publishers Ltd
About this chapter
Cite this chapter
Papadopoulos, G.A. (1991). Study of Dynamic Crack Propagation in Polystyrene by the Method of Dynamic Caustics. In: Rossmanith, H.P., Rosakis, A.J. (eds) Dynamic Failure of Materials. Springer, Dordrecht. https://doi.org/10.1007/978-94-011-3652-5_17
Download citation
DOI: https://doi.org/10.1007/978-94-011-3652-5_17
Publisher Name: Springer, Dordrecht
Print ISBN: 978-1-85166-665-2
Online ISBN: 978-94-011-3652-5
eBook Packages: Springer Book Archive