Abstract
This paper offers a review of the author’s decade-long attempts to examine the tribochemical changes that occur with various crystallinities of (a) polished silicon (b) unpolished and polished polycrystalline diamond films, and (c) a commercially available version of polished polycrystalline α-SiC. Theory-based model experiments were performed in ∼1.33 × 10 Pa = 1 × 10-5 Torr vacuum (∼93% of the residual gases is water vapor) and some in low partial pressures of hydrogen test atmospheres, at temperatures ranging from lab-ambient to 950°C. The apparatus used was a unique pin-on-oscillating-flat-type scanning electron microscope (SEM) tribometer specially built to fill the gap between an atomic force microscope and a conventional, bench-top friction and wear tester. Its primary purpose has been to examine the changes in the tribological behavior of a variety of bearing materials and solid lubricants, under realistic engineering (Hertzian) contact stresses in the GPa to MPa (from many thousands to hundreds of psi) range, as influenced by elevated temperatures in moderate vacuum and in low partial pressures of inert or reactive gases. The coefficient of friction and wear measurements were occasionally complemented by surface analyses to decipher the footprints of atomic-level surface interactions by the tribological behavior of essentially microscopic (∼50 to 500 μm diameter) Hertzian contacts. All the friction trends indicate that the changes in adhesion (and thus the coefficient of adhesive friction) can be explained by the number of dangling (high-friction), reconstructed (reduced-friction) or adsorbate-passivated (low-friction) surface bonds developing on the counterfaces as a function of temperature and atmospheric environment.
Keywords
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.
This is a preview of subscription content, log in via an institution.
Buying options
Tax calculation will be finalised at checkout
Purchases are for personal use only
Learn about institutional subscriptionsPreview
Unable to display preview. Download preview PDF.
References
Achtzinger, N., Grillenberger, J., Whitthuhn, W., Linnarsson, M.K., Janson, M. and Svensson, B.G. (1998), “Hydrogen Passivation of Silicon Carbide by Low-energy Ion Implantation,” Appl. Phys. Lett., 73, 945–947.
Didziulis, S.V. Lince, J.R., Fleischauer, P.D. and Yarmoff J.A. (1991), “Photoelectron Spectroscopic Studies of the Electronic Structure of α-SiC,” Inorg. Chem., 30, 672–678.
Erdemir, A. and Fenske, G.R. (1996), “Tribological Performance of Diamond and Diamondlike Carbon Films at Elevated Temperatures, Tribol Trans., 39, 787–794.
Gardos, M.N. (1994), “Tribology and Wear Behavior of Diamond,” Chapter 12 in Synthetic Diamond: Emerging CVD Science and Technology, (K.E. Spear, and J.P. Dismukes, eds.), Electrochem. Soc. Monograph, John Wiley and Sons, New York, NY, 533–580.
Gardos, M.N. (1996), “Surface Chemistry-Controlled Tribological Behavior of Si and Diamond,” Tribol. Lett., 2, 173–187.
Gardos, M.N. (1996a), “Tribological Behavior of Polycrystalline and Single-Crystal Silicon,” Tribol. Lett., 2, 355–373.
Gardos, M.N. (1998), “Advantages and Limitations of Silicon as a Bearing Material for MEMS Applications,” in Tribology Issues and Opportunities in MEMS, (B. Bhushan, ed.) Kluwer Academic Publishers, 341–365.
Gardos, M.N. (1998a), “Re(de)construction-induced Friction Signatures of Polished Polycrystalline Diamond Films in Vacuum and Hydrogen,” Tribol. Lett., 4, 175–188.
Gardos, M.N. (1999), “Tribological Fundamentals of Polycrystalline Diamond Films,” Surf, Coat. Technol. 113,183–200.
Gardos, M.N. (2000), “Tribo-oxidative Degradation of Polished Polycrystalline Diamond Films in 0.2 Torr Partial Pressure of Oxygen,” paper presented at the 26th Leeds-Lyon Symposium on Tribology, 14-17 Sept. 1999, U. of Leeds, UK, (in press).
Gardos, M.N. and Ravi, K.V. (1989), “Tribological Behavior of CVD Diamond Films,” Electrochem. Soc. Proc. Vol. 89–12, 475–493.
Gardos, M.N. and Soriano, B.L. (1990), “The Effect of Environment on the Tribological Properties of Polycrystalline Diamond Films,” J. Mater. Res., 5, 2599–2609.
Gardos, M.N. and Ravi, K.V. (1994), “Surface-Chemistry-Controlled Friction and Wear Behavior of Si(100) vs. Textured Polycrystalline Diamond Film Tribocontacts,” Dia. Films & Technol., 4, 139–165.
Gardos, M.N. and Ravi, K.V. (1995), “Carbon-Graphite-Like Friction Behavior of Polycrystalline Diamond Sliding Against Itself in Vacuum,” The Electrochem. Soc. Proc. Vol. 95-4, 415–424.
Gardos, M.N., Adams, P.M., Barrie, J.D. and Hilton, M.R. (1997), “Crystal-Structure-Controlled Tribological Behavior of Carbon-Graphite Seal Materials in Partial Pressures of Helium and Hydrogen. I. Specimen Characterization and Fundamental Considerations,” Tribol. Lett., 3, 175–184.
Gardos, M.N., Davis, P.S. and Meldrum, G.R. (1997a), “Crystal-Structure-Controlled Tribological Behavior of Carbon-Graphite Seal Materials in Partial Pressures of Helium and Hydrogen. II. SEM Tribometry,” Tribol. Lett., 3, 185–198.
Gardos, M.N. and Gabelich, S.A. (1999), “Atmospheric Effects of Friction, Friction Noise and Wear with Silicon and Diamond. Part I. Test Methodology,” Tribol. Lett., 6, 79–86.
Gardos, M.N. and Gabelich, S.A. (1999a), “Atmospheric Effects of Friction, Friction Noise and Wear with Silicon and Diamond. Part II. SEM Tribometry of Silicon in Vacuum and Hydrogen,” Tribol. Lett., 6, 87–102.
Gardos, M.N. and Gabelich, S.A. (1999b), “Atmospheric Effects of Friction, Friction Noise and Wear with Silicon and Diamond. Part III. SEM Tribometry of Polycrystalline Diamond in Vacuum and Hydrogen,” Tribol. Lett., 6, 103–112.
Hilton, M.R. (1993), “Tribological Approaches to Micromachine Design and Fabrication for Space Applications,” in Micro-and Nanotechnology for Space Systems: An Initial Evaluation, (eds. H. Helvejian and E.Y. Robinson), Aerospace Report No. ATR-93(8349)-l, The Aerospace Corp., El Segundo, CA, 127–135.
Homma, Y., Suzuki, M., and Tomita, M. (1993), “Atomic Configuration Dependent Secondary Electron Emission from Reconstructed Silicon Surfaces,” Appl. Phys. Lett., 62, pp. 3276–3278.
Lee, D.H. and Joannopoulos, J.D. (1982), “Ideal and Relaxed Surfaces of SiC,” J. Vac. Sci. Technol., 21, 351–357.
Muelhoff, L., Choyke, W.J., Bozack, M.J. and Yates, J.T. Jr., (1986), “Comparative Electron Spectroscopic Studies of Surface Segregation on SiC(000l) and SiC(000l),” J. Appl. Phys., 60, 2842–2853.
Radhakhrishnan, G., Adams, P.M., Robertson, R. and Cole, R. (2000), “Integration of Wear-Resistant Titanium Carbide Coatings into MEMS Fabrication Processes,” Tribol. Lett, and references therein (in press).
Rahaman, M.N., Boiteux, Y. and De Jonghe, L.C. (1986), “Surface Characterization of Silicon Nitride and Silicon Carbide Powders,” Am. Ceram. Soc. Bull., 65, 1171–1176.
Rajan, N., Mehregany, M., Zorman, C.A. and Stefanescu, S. (1999), “Fabrication and Testing of Micromachined Silicon Carbibe and Nickel Fuel Atomizers for Gas Turbine Engines,” J. MEMS, 8, 251–257.
Shin, W., Hikosaka, T., Seo, W.-S., Ahn H.S., Sawaki, N. and Koumoto, K. (1998), “Fibrous and Porous Microstructure Formation in 6H-SiC by Anodization in HF Solution,” J. Electrochem. Soc, 145, 2456–2460.
Singh, N.N. and Rys, A. (1998), “Electrical Characterization of 6H-SiC Metal Oxide Semi-conductor Structures at High Temperature,” J. Electrochem. Soc, 145, 299–302.
Tkachenko, Yu. G., Pilyankevich, A.N., Britun, V.F., Bazilevich, V.D., Opanashchuk, N.F., Dyban’, Yu.P., Yurchenko, D.Z. and Yulyugin, V.K. (1979), “Frictional Characteristics and Contact-Zone Deformation Behavior of TiC in its Homogeneity Range,” Soviet Powder Metallurgy and Metal Ceramics, 18(6), 45–51.
Ueno, K., Asai, R. and Tsui, T. (1998), “4H-SiC MOSFET’s Utilizing the H2 Surface Cleaning Technique,” IEEE Electr. Dev. Lett., 19(7), 244–246.
Vathulya, V.R., Wang, D.N. and White, M.H. (1998), “On the Correlation between the Carbon Content and the Electrical Quality of Thermally Grown Oxides on p-type 6H-SiC,” Appl. Phys. Lett., 73, 2161–2163.
Yasseen, A.A., Zorman, C.A. and Mehregany, M. (1999), “Surface Micromachining of Polycrystalline SiC Films using Microfabricated Molds of SiO2 and Polysilicon,” J. MEMS, 8,237–242.
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2001 Springer Science+Business Media Dordrecht
About this chapter
Cite this chapter
Gardos, M.N. (2001). Determining the Nanoscale Friction and Wear Behavior of Si, SiC and Diamond by Microscale Environmental Tribometry. In: Bhushan, B. (eds) Fundamentals of Tribology and Bridging the Gap Between the Macro- and Micro/Nanoscales. NATO Science Series, vol 10. Springer, Dordrecht. https://doi.org/10.1007/978-94-010-0736-8_36
Download citation
DOI: https://doi.org/10.1007/978-94-010-0736-8_36
Publisher Name: Springer, Dordrecht
Print ISBN: 978-0-7923-6837-3
Online ISBN: 978-94-010-0736-8
eBook Packages: Springer Book Archive