Abstract
It is necessary to understand phase equilibria in the Bi-system to effectively produce superconductors in this system. Experiments were performed using a quench method together with microscopic study as well as composition analyses by ICP and EPMA. Equilibrium phases at different temperatures were investigated and plotted on a quasi-binary temperature versus composition diagram between the nominal compositions Bi2Sr2Ca2Cu3Ox (2223, the high Tc phase) and Bi2Sr2CaCu2Ox(2212, the low Tc phase). The liquidus temperature of the compound with the 2223 nominal composition found to be above 1100°C, and the primary solid phase formed to be Ca-rich oxide. These results contradict those in previously reported phase diagrams, in which the temperature of the liquidus is about 1000°C. The liquidus lines along the composition axis as well as the primary phase coresponding to these lines as also reported.
This is a preview of subscription content, log in via an institution to check access.
Reference
C. Michel, M. Hervieu, M. M.Borel, A. Grandin, F. Deslandes, A. Provost and B. Raveau, Z. Physik B68 (1987}
H. Maeda, Y. Tanaka, M. Fukutomi, and T. Asao, Jpn. J. Appl. Phys. 27 (1988) L209
A.M.M.Gadalla and J. White and Trane. Brite. Ceran. Cream. Soc., 65 [4] 185(1966}
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 1990 Springer Japan
About this paper
Cite this paper
Noda, T., Izumi, T., Nakamura, A., Shiohara, Y. (1990). Phase Diagram of Bi-Based Superconductors. In: Ishiguro, T., Kajimura, K. (eds) Advances in Superconductivity II. Springer, Tokyo. https://doi.org/10.1007/978-4-431-68117-5_51
Download citation
DOI: https://doi.org/10.1007/978-4-431-68117-5_51
Publisher Name: Springer, Tokyo
Print ISBN: 978-4-431-68119-9
Online ISBN: 978-4-431-68117-5
eBook Packages: Springer Book Archive