Surface Analytical Investigation of the Corrosion Behaviour of Ti(Pd) Samples

  • G. Pfennig
  • H. Moers
  • H. Klewe-Nebenius
  • R. Kaufmann
  • H. J. Ache
Conference paper
Part of the Mikrochimica Acta Supplementum book series (MIKROCHIMICA, volume 11)

Abstract

For the deposition of vitrified HAW in a salt repository containers are necessary forming an additional barrier against leaching. The material must be resistant against salt brines originating from accidental flooding of the repository. Corrosion studies have been carried out at the “Institut für Nukleare Entsorgung” of KfK in order to determine the corrosion rates for different materials under various corrosion conditions1. One of the materials showing low corrosion rates is titanium with a 0.2 wt.% admixture of palladium as corrosion inhibitor (Ti 99.8-Pd, TIKRUTAN RT 12, manufactured by Krupp-Stahl, Essen, Federal Republic of Germany). However, for extrapolations to extremely long standing times, a closer inspection of the chemical processes responsible for the corrosion is necessary.

Keywords

Depth Profile Corrosion Layer Reactive Sputtering Corrode Sample Salt Brine 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    E. Smailos, R. Köster, and W. Schwarzkopf, Eur. Appl. Res. Report — Nucl. Science Technology 5/2, 175 (1983).Google Scholar
  2. 2.
    S. Hofmann and J. M. Sanz, J. Trace and Microprobe Techn. 1, 213 (1982).Google Scholar
  3. 3.
    H. J. Mathieu, J. B. Mathieu, D. E. McClure, and D. Landolt, J. Vac. Sci. Technol. 14, 1023 (1977).CrossRefGoogle Scholar
  4. 4.
    R. Kaufmann, Bestimmung von Sputterkoefflzienten an Ti-Metall und TiO2 zur Auswertung von Tiefenprofilen korrodierter Ti-Proben. Diplomarbeit, Universität Karlsruhe 1985.Google Scholar
  5. 5.
    O. K. Kurbatov, Sov. Phys.-Techn. Phys. 12, 1328 (1968).Google Scholar

Copyright information

© Springer-Verlag 1985

Authors and Affiliations

  • G. Pfennig
    • 1
  • H. Moers
    • 1
  • H. Klewe-Nebenius
    • 1
  • R. Kaufmann
    • 1
  • H. J. Ache
    • 1
  1. 1.Institut für RadiochemieKernforschungszentrum KarlsruheKarlsruheFederal Republic of Germany

Personalised recommendations