Stress Corrosion Cracking

  • Helmut Kaesche
Part of the Engineering Materials and Processes book series (EMP)

Abstract

Stress corrosion cracking (SCC) is defined as crack nucleation and propagation in metals caused by the synergystic action of tensile stresses, either constant or slowly changing with time, together with crack-tip chemical reactions or other environment-induced crack-tip effects. In principle, dry hydrogen-induced cracking also is SCC, but we shall, in this chapter, assume that the environmental effect is electrolytic crack tip corrosion.

Keywords

Crack Growth Rate Stress Corrosion Stress Corrosion Crack Crack Extension Metal Dissolution 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    Mittlg. AGK Arbeitskreise ‘Wasserstoff-induzierte Werkstoffschäden’ und ‘Spannungs-u. Schwingungsrißkorrosion’: Werkstoffe u. Korr. 37 (1985) 45Google Scholar
  2. 2.
    a) Symp. Spannungs- und Dehnungs-induzierte Korr., Baden-Baden 1978: Werkstoffe u. Korr. 29 (1978) Nr. 11Google Scholar
  3. Proc. Symp. Electrochemical Corrosion Testing, San Francisco 1970. (Mansfeld, F. and Bertocci, U., eds.). ASTM, Philadelphia, 1981Google Scholar
  4. Proc. 8th Int. Conf. Metallic Corrosion, Mainz 1981. DECHEMA, Frankfurt, 1981Google Scholar
  5. Symp. Korrosion u. Bruch, Frankfurt 1988. DVM, Berlin, 1988; e) Tagung Spannungsrißkorrosion in Wasser, Zürich 1988. SVMT, Zürich 1988Google Scholar
  6. Proc. Conf. Theory of Stress Corrosion Cracking, Ericeira 1971. (Scully, J., ed.). NATO Scientifique Affairs Div., Brussels, 1971Google Scholar
  7. Proc. 4th Int. Conf. Metallic Corrosion, Amsterdam 1969. NACE, Houston, 1969Google Scholar
  8. Proc. Int. Conf. Stress Corrosion Cracking and Hydrogen Embrittlement in Iron Base Alloys, Unieux-Firminy 1973. (Staehle, R.W., Hochmann, J., McCright, R.D., and Slater, J.C., eds.): NACE, Houston, 1979Google Scholar
  9. Advances in Corrosion Science and Technology. (Fontana, M.G. and Staehle, R.W., eds.). Vol. 2. Plenum Press, New York, 1972Google Scholar
  10. Korrosion 22. DGM Tagung Spannungsrißkorrosion, Frankfurt 1968. (Kaesche, H., ed.). Verlag Chemie, Weinheim, 1969Google Scholar
  11. U.R. Evans Conf. Localized Corrosion, Williamsburgh 1971. NACE, Houston, 1974Google Scholar
  12. Proc. Int. Conf. Environment-Sensitive Cracking of Materials, Guildford 1977. (Swann, P.R., Ford, P.P., and Westwood, A.R.C., eds.). The Metals Society, London 1977Google Scholar
  13. Proc. Conf. Corrosion Chemistry within Pits, Cevices and Cracks, Teddington 1984. (TurnbuU, A. ed.). HMSO, London, 1987Google Scholar
  14. Proc. Conf. Fundamental Aspects of Stress Corrosion Cracking, Columbus 1967. (Staehle, R.W., Forty, AJ., and Van Rooyen, D., eds.). NACE, Houston, 1969Google Scholar
  15. Comprehensive Treatise on Electrochemistry. (Bockris, J-O’M., Conway, B.E., Yeager, E., White, R.E., eds.). Vol. IV: Electrochemical Materials Science. Plenum Press, New York, London, 1981Google Scholar
  16. Recent Advances in Stress Corrosion. (Bresle, A., ed.). Esslete AB, Stockholm, 1961Google Scholar
  17. Proc. Symp. Environment-Sensitive Fracture of Engineering Materials, Chicago 1977. (Fouroulis, Z.A., ed.). The Metallurgical Soc. of AIME, Warrendale, 1977Google Scholar
  18. High Strength Materials. (Zackay, V.F., ed.). J. Wiley, New York, 1965Google Scholar
  19. Electrodeposition and Corrosion Processes. Van Nostrand. New York 1965Google Scholar
  20. Physical Metallurgy of Stress Corrosion Failure. (Rhodin, T.N., ed.). Interscience Pubis., New York, London 1959Google Scholar
  21. Modern Aspects of Electrochemistry (Bockris, J.O’M., Conway, B.E., and White, R., eds.). Vol.27. Plenum Press, New York 1995Google Scholar
  22. Proc. Meeting Modeling Environmental Effects on Crack Growth Processes, Toronto 1985. (Jones, R.H. and Gerberich, W.W., eds.). TMS-AIME, Warrendale, 1986Google Scholar
  23. Hydrogen Degradation of Ferrous Alloys. (Oriani, R.A., Hirth, J.P., and Smialowski, M., eds.). Noyes Pubhcations, Park Ridge, 1985Google Scholar
  24. Moderne Stähle. (Uggowitzer, P.J., ed.). Schweizer Akademie der Wissenschaften Zürich 1987Google Scholar
  25. Spannungsrißkorrosion von Stahl in Wasser. (Speidel, M., Magdowski, R.M., and Uggowitzer, P.J., eds.). Schweizer Akademie der Wissenschaften Zürich 1987Google Scholar
  26. Proc. Int. Conf. Environment-Induced Cracking of Metals, Kohler, 1988. (Gangloff, R.P. and Ives, M.B., eds.). NACE, Houston 1990Google Scholar
  27. Proc. Int. Conf. Life Prediction of Corrodible Structures, Cambridge 1994. (Parkins, R.N., ed.). NACE, Houston, 1994Google Scholar
  28. Proc. Int. Conf. Corrosion- Deformation Interactions, Fontainebleau 1992.(Magnin, F. and Gras, J.M., eds.). Les Éditions de Physique, Les Ulis, 1993Google Scholar
  29. Proc. Int. Conf. Hydrogen Transport and Cracking in Metals, Teddington 1994Google Scholar
  30. 3.
    Meysenbug, C.M. and Litzkendorf, M.: Werkstoffe u. Korr. 19 (1970) 901CrossRefGoogle Scholar
  31. a) Herbsleb, G.: private communication 1989Google Scholar
  32. Münster, Gräfen, H.: Archiv Eisenhüttenwesen em 36(1965) 277Google Scholar
  33. Mattson, E.: Electrochim. acta 3 (1961) 279CrossRefGoogle Scholar
  34. Brauns, E. and Ternes, W.: Werkstoffe u. Korr. 19 (1968) 1CrossRefGoogle Scholar
  35. Ternes, W.: Doctoral thesis. University Clausthal, 1963Google Scholar
  36. 5.
    a) Scully, J.C. and Powell, D.T.: Corr. NACE 25 (1969) 483Google Scholar
  37. Watkinson, P.E. and Scully, J.C., in: loc. cit. [5f], p. 140Google Scholar
  38. Hoar, T.P. in: loc. cit. [2n], p.98Google Scholar
  39. Scully, J.C. and Hoar, T.P., in: Proc. 2nd Int. Congress Metallic Corrosion, New York 1963. NACE, Houston, 1966, p. 66Google Scholar
  40. Hoar, T.P. and Ford, P.J.: J. Electrochem. Soc. 120 (1973) 1013CrossRefGoogle Scholar
  41. Scully, J.C., in: loc. cit. [2e], 127Google Scholar
  42. id., in: loc. cit. [2h], p. 496Google Scholar
  43. Hines, J.C. and Hoar, T.P.: J. Appi. Chem. (1958) 764Google Scholar
  44. Hoar, T.P. and West, I.M.: Proc. Ro. Soc. A268 (1962) 304CrossRefGoogle Scholar
  45. a) Herbsleb, G. and Pöpperling, R., in: loc. cit. [2a], p. 740Google Scholar
  46. Herbsleb, G. and Schwenk, W. Corr. NACE 41 (1985) 431CrossRefGoogle Scholar
  47. Schwenk, W., in: loc. cit. [2a], p. 740Google Scholar
  48. iid.: Werkstoffe u. Korr. 31 (1984) 171Google Scholar
  49. iid. in: loc.cit. [2c], p. 536Google Scholar
  50. Wendler-Kalsch, E. in: loc. cit. [2a], p. 703Google Scholar
  51. id.: Werkstoffe u. Korr. 31 (1980) 534CrossRefGoogle Scholar
  52. Krägeloh, E. and Navab-Motlagh, M.M.: Z. Werkstofftechnik 9 (1979) 400CrossRefGoogle Scholar
  53. Haumann, W., Heller, H., Jungblut, H.-A., Pircher, H., Pöpperling, R., and Schwennk, W.: Stahl u.Eisen 107 (1987) 585Google Scholar
  54. Pöpperling, R., Schwenkm, W., and Venketesvarlu, J.: Werkstoffe u. Korr. 36 (1985) 389CrossRefGoogle Scholar
  55. Herbsleb, G., Pfeiffer, G., and Ternes, H.: Werkstoffe u. Korr. 30 (1979) 322;CrossRefGoogle Scholar
  56. Herbsleb, G. and Pfeiffer, B.: ibid. 35 (1984) 254Google Scholar
  57. Herbsleb, G. and Schwenk, W.: ibid. 18 (1967) 521Google Scholar
  58. Frölich, Th., Schwenk, W., and Dahl, W.: Materials and Corrosion 48 (1997) 207CrossRefGoogle Scholar
  59. a) Kessler, K.J. and Kaesche, H., in: loc.cit. [2b]Google Scholar
  60. iid.: Werkstoffe u. Korr. 35 (1985) 171Google Scholar
  61. iid., in: loc. cit. [2c], p.536Google Scholar
  62. Berggreen, J., Engell, H.J., and Kaesche, H.: Werkstoffe u. Korr. 26 (1975) 599CrossRefGoogle Scholar
  63. Richter, J. and Kaesche, H.: ibid. 28 (1977) 602Google Scholar
  64. Kaesche, H.: Z. Metallkunde 67 (1976) 439Google Scholar
  65. Stellwag, B. and Kaesche, H.: Werkstoffe u. Korr. 33 (1982) 274, 323Google Scholar
  66. iid.: ibid. 35 (1979) 397Google Scholar
  67. Kaesche, H.: Archiv Eisenhüttenwesen 36 (1965) 911Google Scholar
  68. Stoll, Fand Kaesche, H., in: loc. cit. [2c], p.530Google Scholar
  69. iid., in: Proc. Asian Pacific CorrosionControl Conf., Taipei 1983. APMACA, Taipeh, 1983, p.l9Google Scholar
  70. Schneider, M., Kessler, K.J., and Kaesche, H.: Archiv Eisenhüttenwesen 50 (1979) 379Google Scholar
  71. Kessler, K.J. and Kaesche, H.: Werkstoffe u. Korr. 31 (1980) 907CrossRefGoogle Scholar
  72. iid., in: Wasserstoff in Metallen. Ergebnisse eines Schwerpunktprogramms. Deutsche Forschungsgemeinschaft. Bad Godesberg 1985, p. 427Google Scholar
  73. Grötsch, F., Wendler-Kalsch, E., and Kaesche, H., in: loc. cit. [11] p. 301Google Scholar
  74. Rippstein, K. and Kaesche, H.: Corr. sci. 29 (1989) 517CrossRefGoogle Scholar
  75. Gladen, H. and Kaesche, F: Nuclear Engng. and Design 151 (1994) 463CrossRefGoogle Scholar
  76. Kaesche, H., in: loc. cit. [2z]Google Scholar
  77. id.: Z. Metallkunde 64 (1973) 593Google Scholar
  78. Vogelhuber, G.: Diploma thesis. University Erlangen, 1981Google Scholar
  79. Kaiser, H. and Kaesche, H., in: Proc. 9th Eur. Congr. Corrosion, Utrecht 1989. NCC Stichting Nederlands Corrosie centrum. Vol.2, PL 118Google Scholar
  80. Fiebiger, C., Kilian, R., Degelmann, E., Kaiser, H., and Kaesche, H.: Werkstoffe u. Korr. 40 (1989) 695CrossRefGoogle Scholar
  81. Hack, T., Popp, W., and Kaesche, H.: ibid. 42 (1991) 396Google Scholar
  82. Habermann, M.E., Doctoral Thesis, University Erlangen-Nürnberg 1995Google Scholar
  83. 8.
    a) Engell, H.J., Bohnenkamp, K., and Bäumel, A.: Archiv Eisenhütten-wesen 33 (1962) 285Google Scholar
  84. Engell, H.J. and Speidel, M.O., in: loc. cit.[2j]Google Scholar
  85. Engell, H.J., in: loc. cit. [If], p.68Google Scholar
  86. id.: Stahl u. Eisen 98 (1978) 637Google Scholar
  87. Engell, H.-J. and Bäumel, a., in: loc. cit. [2s], p. 341Google Scholar
  88. Bäumel, A. and Engell, H.-J.: Archiv Eisenhüttenwesen 32 (1961) 379Google Scholar
  89. Bohnenkamp, K.: ibid. 39 (1968) 361Google Scholar
  90. Schreiber, F. and Enge, U. H.-J.: Werkstoffe u. Korr. 23 (1972) 175CrossRefGoogle Scholar
  91. Speidel, M.O., in: loc.cit. [2f], p.l40Google Scholar
  92. id.: Corr. NACE 33 (1977) 199Google Scholar
  93. Speidel, M.O. and Hyatt, M.V., in: loc. cit. [2h], p. 115Google Scholar
  94. Speidel, M.O.: Corr. NACE 33 (1977) 199Google Scholar
  95. Speidel, M.O. and Magdowski, R.M.: Corrosion 86, Houston 1986, Paper No. 329Google Scholar
  96. iid.: Corrosion 88, St.Louis 1988, Paper No. 283Google Scholar
  97. Magdowski, R.M. and Speidel, M.O., in: loc. cit. [ly], p. 117Google Scholar
  98. 11.
    Eremias, B. and Maricev, V.V.: Corr. sci. 20 (1980) 307CrossRefGoogle Scholar
  99. See, e.g., Tatro, C.A., Liptal, R.G., and Moon, D.W. in: loc. cit. [2h], p. 509Google Scholar
  100. 13.
    a) Bhatt, H.J. and Phelps, E.H.: Corr. NACE 17 (1961) 430tGoogle Scholar
  101. Wilde, B.E.: ibid. 27 (1961) 602Google Scholar
  102. 14.
    a) Buhl, H.: Corr. sci. 13 (1973) 639CrossRefGoogle Scholar
  103. Rätzer-Scheibe, H.: Werkstoffe u. Korr. 26 (1975) 2CrossRefGoogle Scholar
  104. 15.
    Pickering, H.W. and Frankenthal, R.P.: J. Electrochem. Soc. 119 (1972) 1297CrossRefGoogle Scholar
  105. 16.
    a) Shuck, R.R. and Swerdlow, J.L. in: loc. cit. [2k], p.l90, 208Google Scholar
  106. Doig, P. and Flewitt, P.F., in: loc. cit. [21], p. 113Google Scholar
  107. iid.: Corr. NACE 37 (1981) 378Google Scholar
  108. Melville, P.H.: British Corr. J. 14 (1979) 15Google Scholar
  109. Cherepanov, G.P.: Stress Corrosion Cracking. In loc. cit. [lo]Google Scholar
  110. Beck, T.R., in: loc. cit. [2f], p.64Google Scholar
  111. id.: Corr. NACE 30 (1974)408Google Scholar
  112. id., in: Proc. Conf. Predictive Capabilities in Environmental Assisted Cracking. (Rungta, R., ed.). ASME 1985, p. 177Google Scholar
  113. 19.
    a) Edeleanu, C.: J. Inst. Metals 80 (1952) 187Google Scholar
  114. id., in: loc. cit. [2p], p. 79, see also Forty, A.J., in this volume.Google Scholar
  115. 20.
    McEvily, A.J. and Bond, A.P.: J. Electrochem. Soc. 112 (1965) 131CrossRefGoogle Scholar
  116. a) Pugh, E.N., in: loc. cit.[If], p. 418Google Scholar
  117. Bursle, A., Pugh, E.N., in: loc. cit. [2f], p. 18Google Scholar
  118. Pugh, E.N.: Corr. NACE 41 (1968) 517CrossRefGoogle Scholar
  119. Pugh, E.N. and Westwood, A.R.C.: PhiL Mag. 13 (1966) 167CrossRefGoogle Scholar
  120. Beggs, D.V., Hahn, M.T., and Pugh, E.N., in: Hydrogen Embrittlement and Stress Corrosion Cracking Metals Park. ASTM, 1984, p. 181Google Scholar
  121. Bertocci, K., and Pugh, E.N., in: loc. cit. [2m], p. 144Google Scholar
  122. 22.
    a) West, J.M. and Farman, L.: British Corr. J. 1 (1966) 67CrossRefGoogle Scholar
  123. West, J.M., in: loc. cit. [2q]Google Scholar
  124. 23.
    a) Swann, P.R.: Corr. NACE 19 (1963) 102Google Scholar
  125. Pickering, H. W. and Swann, P.R.: ibid. p. 373Google Scholar
  126. Swann, P.R. and Embury, in: loc.cit. [2q], p. 327Google Scholar
  127. Swann, P.R., in: loc. cit. [2e], p. 113Google Scholar
  128. Sicock, J.M. and Swann, P.R., in: loc. cit. [2p], p.l33Google Scholar
  129. 24.
    a) Staehle, R.W. and Smith, T.J.: Corr. NACE 23(1967) 117Google Scholar
  130. Staehle, R.W., in: loc. cit. [2h], p. 180Google Scholar
  131. Pednakar, S.P., Agrawal, A.K., Chang, H.E., and Staehle, R.W.: J. Electrochem. Soc. 126 (1979) 701CrossRefGoogle Scholar
  132. Latanision, R.M. and Staehle, R.W., in: loc. cit. [2n], p. 214Google Scholar
  133. 25.
    a) Sieradzki, K., Sabatini, R.L., and Newman, R.C.: Met. Trans. 15A (1984) 1941Google Scholar
  134. Sieradzki, K. and Friedersdorf, F.J.: Corr. sci. 36 (1994) 669CrossRefGoogle Scholar
  135. 26.
    Meletis, E.I. and Hochman, R.F.: Cor. sci. 24 (1984) 843CrossRefGoogle Scholar
  136. 27.
    Flis, J.: Brit. Corr. J. 3 (1968) 183Google Scholar
  137. a) See e.g. Graf, L., in: loc. cit. [2f], p. 399Google Scholar
  138. Graf, L. and Budke, J.: Z. Metallkunde 46 (1955) 378Google Scholar
  139. Frank, W. and Graf, L.: ibid. 66 (1975) 555Google Scholar
  140. Graf, L. and Klatte, H.: ibid. 46 (1955) 673Google Scholar
  141. Graf, L. and Becker, H.: Z. f. Metallkunde 62 (1971) 685Google Scholar
  142. Graf, L. and Springe, G.: Werkstoffe u. Korr. 20 (1969) 323CrossRefGoogle Scholar
  143. a) Uhlig, H.H., in: loc. cit. [2t], p. 1; b) id., in: loc. cit. [2n], p. 86Google Scholar
  144. Uhlig, H.H., Gupta, K., and Lang, W.: J. Electrochem. Soc. 122 (1975) 343CrossRefGoogle Scholar
  145. Uhlig, H.H and Cook, E.W.: ibid. 116 (1969) 173Google Scholar
  146. Lee, H.H. and Uhlig, H.H.: ibid. 117 (1969) 18Google Scholar
  147. 30.
    a) Galvele, J.R.: J. Electrochem. Soc. 133 (1986) 953CrossRefGoogle Scholar
  148. id.: Corr. sci. 35 (1993) 419CrossRefGoogle Scholar
  149. id., in: loc. cit. [[2ut], p. 233Google Scholar
  150. id.: Corr. scL 36 (1994) 901CrossRefGoogle Scholar
  151. Montoto, M.L., Duffò, G. S., and Galvele, J. R.: ibid. p. 1805Google Scholar
  152. Galvele, J.R. and Duffó, G.S.: ibid. 39 (1997) 605Google Scholar
  153. Giordano, C.M., Duffó, G.S., and Galvele, J.R.: ibid. p. 1915Google Scholar
  154. Galvele, J.R.: ibid. 40 (1998) 3537Google Scholar
  155. Alvarez, M.G., Fernandez, S.A., and Galvele, J.R.: ibid. 42 (2000) 739Google Scholar
  156. Manfredi, C., Maier, I.A., and Galvele, J.R.: Corr. sci. 22 (1987) 887CrossRefGoogle Scholar
  157. Maier, I.A., Manfredi, C., and Galvele, J.R.: ibid.25 (1985) 15Google Scholar
  158. Maier, I.A., López-Pérez, E., and Galvele, J.R.: ibid. 22 (1982) 537Google Scholar
  159. Nelson, H.G. and Williams, D.P., in: loc. cit. [2h], p. 390Google Scholar
  160. 32.
    Jaberi, J.: Brit. Corr. J. 20 (1985) 133Google Scholar
  161. 33.
    a) Riecke, E.: Archiv Eisenhüttenwesen 44 (1973) 647Google Scholar
  162. id.: Werkstoffe u. Korr. 30 (1979) 610Google Scholar
  163. Richards, W.: Zement, Kalk, Gips 22 (1969) 447Google Scholar
  164. Nürnberger, U.: Forschung Straßenbau u. Verkehrstechnik Nr. 308 (1980)Google Scholar
  165. Riecke, E. and Johnen, B.: Werkstoffe u. Korr. 37 (1986) 310CrossRefGoogle Scholar
  166. McGuinn, K. and Griffith, J.R.: Brit. Corr. J. 12 (1977) 152Google Scholar
  167. Eickemeyer, J.: Corr. sci. 18 (1973) 397CrossRefGoogle Scholar
  168. Nürnberger, U.: Korrosion und Korrosionsschutz im Bauwesen, Band I. Bauverlag, Wiesbaden, Berlin, 1995Google Scholar
  169. 34.
    a) Mietz, J., Fischer, J., and Isecke, B.: Materials and Corr. 50 (1999) 535CrossRefGoogle Scholar
  170. Mietz, J.: ibid. 51 (2000 80)Google Scholar
  171. Nürnberger, U.: ibid. 48 (1997)602Google Scholar
  172. Menzel, K. and Onuseit, G.: ibid. 47 (1996) 42Google Scholar
  173. Okada, H., Yukawa, K.-T., and Tamura, H.: Corr. NACE 32 (1976)201Google Scholar
  174. 36.
    a) Münster, R. and Gräfen, H.: Archiv Eisenhüttenwesen 36 (1965) 111Google Scholar
  175. Gräfen, H.: Corr. sci. 7 (1967) 177CrossRefGoogle Scholar
  176. Gräfen, H. and Kuron, D.: Archiv Eisenhüttenwesen 36 (1965) 285Google Scholar
  177. Rädecker, W. and Gräfen, H.: Stahl u. Eisen 76 (1958) 1616Google Scholar
  178. a) Parkins, R.N., in: loc. cit. [2n], p. 361Google Scholar
  179. id., in: loc. cit. [2f], p. 167Google Scholar
  180. id., in: loc. cit. [2h], p. 601Google Scholar
  181. Humphries, M.J. and Parkins, R.N., in: loc. cit. [2m], p. 384Google Scholar
  182. Parkins, R.N. and Fessler, R.R.: Engng. Appi. 1 (1978) 80Google Scholar
  183. Fessler, R.R., Markworth, A.J., and Parkins, R.N.: Corr. NACE 39 (1983) 20CrossRefGoogle Scholar
  184. Parkins, R.N., O’Dell, C.S., and Fessler, R.R.: Corr. sci. 24 (1984) 343CrossRefGoogle Scholar
  185. Parkins, R.N. and Zhou, S.: ibid. 39 (1997) 159Google Scholar
  186. Congleton, J., Shoji, T. and Parkins, R.N.: ibid. 25 1986) 633Google Scholar
  187. Parkins, R.N.: ibid. 29 (1989) 1019Google Scholar
  188. Congleton, J., Zheng, W., and Hua, H.: ibid. 30 (1990) 555, 651Google Scholar
  189. Yang, W., Zhao, M., and Congleton, J.: Corr. sci. 33 (1992) 89CrossRefGoogle Scholar
  190. Yang, W., Congleton, J., Kohnen-Chari, O., and Sajdl, P.: ibid. p. 375Google Scholar
  191. Congleton, J. and Yang, W.: ibid. 37 (1995) 429Google Scholar
  192. Ebtehaj, K., Hardie, D., and Parkins, R.N.: ibid. 25 (1985) 415Google Scholar
  193. Simon, W. and Schwarz, W.: Ber. Bunsenges. phys. Chemie 67 (1963)108Google Scholar
  194. 39.
    Pourbaix, M.: Atlas d’Équilibres Électrochimiques. Gauthier-Villars, Paris, 1963Google Scholar
  195. 40.
    Venczel, J. and Wranglen, G.: Corr. Sci. 4 (1964) 137CrossRefGoogle Scholar
  196. 41.
    Paulekat, F.: Comment on Herbsleb, G. and Schwenk, W.: Stahl u. Eisen 90 (1970) 903Google Scholar
  197. a) Stenzel, H., Vehoff, H., and Neumann, P., in: loc. cit. [2v], p.225Google Scholar
  198. Vehoff, H. and Neumann, P., in: loc. cit. [2w], p. 686Google Scholar
  199. Vehoff, H., Stenzel, H., and Neumann, P.: Z. f. Metallkunde 78 (1987) 550Google Scholar
  200. Gröschel, F.: Doctoral thesis, RWTH Aachen, 1981Google Scholar
  201. 43.
    a) Andresen, P.L.: Corr. NACE 44(1988) 450CrossRefGoogle Scholar
  202. Andresen, P.L. and Ford, F.P.: Mat. Sci. Engng. AIOÒ (1988) 167Google Scholar
  203. Ford, F.P., in: loc. cit. [2y], p. 139Google Scholar
  204. Ford, F. P. and Andresen, P.L., in: Corrosion 89, New Orleans 1989. NACE, Houston 1989, Paper No. 498Google Scholar
  205. Ford, F.P.: Corr. NACE 52 (1996) 375CrossRefGoogle Scholar
  206. Ford, F.P. and Hickling, J., in: loc. cit. [2z], p. 855Google Scholar
  207. Andresen, P.L., Angeliu, Th.M., Catlin, W.R., Young, L.M., and Horn, R.M., in: Corrosion 2000. NACE, Houston, 2000, Paper No. 203Google Scholar
  208. Andresen, P.L., Angehu, Th.M., and Young, L., in: Corrosion 2001, NACE, Houston, 1991, paper 1228Google Scholar
  209. Angeliu, T.M., in: Corrosion 2001, NACE, Houston 2001, Paper 1121Google Scholar
  210. Andresen, P.L., Angeliu, Th.M., and Young, L.M.: ibid. Paper 1228Google Scholar
  211. Andresen, P.L., in: EPRI International Workshop on Low Temperature Sensitation, Palo Alto 1982, Paper No. 1Google Scholar
  212. Ford, F.P. and Andresen, P.L., in: loc. cit. [60e], p.789Google Scholar
  213. Andresen, P.L., in: Corrosion 1996. NACE, Houston 1996Google Scholar
  214. 44.
    a) Wei, R.P., Gao, M., and Xu, P.Y.: J. Electrochem. Soc. 136 (1989) 1835Google Scholar
  215. Wei, R.P, and Dao, M.: ibid. US (1991)2601Google Scholar
  216. Burstein, G.T. and Gao, G: ibid. p. 2627Google Scholar
  217. 45.
    a) Kelly, R.G. and Newman, R.C.: J. Electrochem. Soc. J37 (1990) 357CrossRefGoogle Scholar
  218. Newman, R.C., Corderman, R.R., and Sieradzki, K.: Brit. Corr. J. 24 (1989) 143Google Scholar
  219. Sieradzki, K. and Newman, R.C.: Phil. Mag. A 51 (1985) 95CrossRefGoogle Scholar
  220. Newman, R.C.and Sieradzki, K., in: loc. cit. [2n], p. 199Google Scholar
  221. iid.: Proc. NATO Advanced Research Workshop Chemistry and Physics of Fracture. (Latanision, E.M. and Jones, R.H., eds.). ASI Series E. No. 130. Martinus Nijhoff, Dordrecht, Dordrecht, 1987Google Scholar
  222. Sieradzki, K., Kim, J.S., Cole, A.T., and Newman, R.C.: J. Electrochem. Soc. 134 (1987) 1635CrossRefGoogle Scholar
  223. 46.
    a) Turnbull, A.: Corr. sci. 34 (1993) 921CrossRefGoogle Scholar
  224. id.: ibid. 39 (1997) 189; e) id.: ibid. 43 (2001) 193Google Scholar
  225. 47.
    a) EMPA; Schweizer Ingenieur u. Architektur 21 (1985) 509Google Scholar
  226. Herbsleb, G. and Theiler, F.: Werkstoffe u. Korr. 40 (1989) 467CrossRefGoogle Scholar
  227. Arnold, N., Gümpel, P., and Heitz, T.W.: Materials and Corr. 49 (1998); 50 (1999) 140Google Scholar
  228. 48.
    Barnartt, S. and Van Rooyen, D.: J. Electrochem. Soc. 108 (1961) 222CrossRefGoogle Scholar
  229. 49.
    Smith, J.A., Peterson, M.H., and Brown, B.F.: Corr. NACE 26 (1970) 540Google Scholar
  230. 50.
    Stalder, F. and Duquette, D.J.: Corr. NACE 33 (1976) 67Google Scholar
  231. 51.
    a) Takano, M., in: Proc. 5th Int. Congr. Metallic Corrosion, Tokio 1972. NACE, Houston, 1974Google Scholar
  232. Nakayama, T. and Takano, M.: Corr. NACE 36 (1980) 530Google Scholar
  233. 52.
    a) Engelmann, H.-J. and Mummert, K.: Werkstoffe u. Korr. 43 (1992) 161CrossRefGoogle Scholar
  234. iid.: ibid. 44 (1993) 454Google Scholar
  235. Engelmann, H.-J., in: loc. cit. [2zb], p. 237Google Scholar
  236. Engelmann, H.-J. and Mummert, K., Schwarz, S., and Uhlemann, M., in: loc. cit. [2zc]Google Scholar
  237. Uhlemann, M., Engelmann, H.-J., and Mummert, K.: Materials and Corr. 46 (1995) 63CrossRefGoogle Scholar
  238. 53.
    See e.g. a) Latanision, R.M. and Westwood, A.R.C., in: Advances in Corrosion Science and Technology. (Fontana, M.G. and Staehle, R.W., eds.). Vol. 1. Plenum Press, New York, 1970Google Scholar
  239. Staehle, R.W., in: loc. cit. [2f], p. 223Google Scholar
  240. 54.
    a) Vaughn, D.A., Phalen, D.I., Peteron, C.L., and Boyd, W.K.: Corr. NACE 19 (1963) 315Google Scholar
  241. Birley, S.S. and Tromans, D.: ibid. 27 (1971) 63Google Scholar
  242. Honkasolo, A.: ibid. 29 (1973) 237Google Scholar
  243. 55.
    a) Scott, P.M. and Tice, D.R.: Nuclear Engng. and Design 119 (1990) 399CrossRefGoogle Scholar
  244. Scott, P.M. and LeCalvar, M., in: loc. cit. [60f], p. 657Google Scholar
  245. 56.
    Indig, M.E., Weber, J.E., and Weinstein, D., in: Reviews on Coatings and Corrosion. (Parkins, R.N., ed.). Vol. 5. Freund. Publ. House, Israel 1982, p. 173Google Scholar
  246. 57.
    a) Choi, H., Beck, F.H., Szklarska-Smialowska, S., and Macdonald, D.D.: Corr. NACE 38 (1982) 136CrossRefGoogle Scholar
  247. Rebak, R.B. and Szklarska-Smialowska, Z.: Corr. sci. 38 (1996) 971CrossRefGoogle Scholar
  248. 58.
    a) Läpple, V., Blind, D., and Deimel, P.: VGB Kraftwerkstechnik 74 (1994) 797Google Scholar
  249. Läpple, V. and Deimel, P.: Werkstoffe u. Korr. 45 (1994) 583CrossRefGoogle Scholar
  250. Kussmaul, K., Blind, D., and Läpple, V.: Nuclear Engng. and Design 168(1997) 53CrossRefGoogle Scholar
  251. 59.
    a) Heidt, J. and Seifert, H-P.: Nucl. Engng. and Design 206 (2001) 57CrossRefGoogle Scholar
  252. Hänninen, H., Yagodzinskyy, Y., Tarasenko, O., Seifert, H-P., Ehrnstén, U., Aaltonen, P., in: loc. cit. [60d]Google Scholar
  253. 60.
    Proc. Int. Symposia on Environmental Degradation of Materials in Nuclear Power Systems - Water reactors: a) 7th Symp., Breckenridge 1995. (Andresen, G. and Brown, P., eds.). NACE, Houston 1995Google Scholar
  254. 8th Symp., Ameha Island 1997. NACE Houston 1997Google Scholar
  255. 9th Symp., Newport Beach 1999. (Ford, P., Bruemmer, S.M., and Was, G.S., eds.). TMS Warrendale, 2000Google Scholar
  256. 10th Symp., Lake Tahoe 2001. (Ford, P.P., Was, G., Nelson, J., and Parsons, P., eds.). (in press)Google Scholar
  257. 5th Symp. 1988 (Theus, J.L., Weeks, J.R., eds.). TMS, 1988; f) 6th Symp., San Diego 1993. TMMMS Society, Warrendale 1993Google Scholar
  258. 61.
    Atkinson, J.D. and Yu, J.: Fatigue Fract. Engng. Mater. Struct. 20 (1997) 1CrossRefGoogle Scholar
  259. 62.
    See e.g. Ruscák, A., B. and Dietzel, W., in: loc. cit. [60c], p. 885Google Scholar
  260. 63.
    Ehrnsten, U., Foehl, J., Gomez-Briceno, D., Weissenberg, T., Roth, A., Ritter, S., Seifert, H.P., and Zamboch, M., in: Proc. FISA Conf. EU Research in Reactor Safety, Luxemburg 2001Google Scholar
  261. 64.
    Xiukui, S., Jian, X., and Yiyi, L.: Mats. Sci. and Engng. 114 (1989) 179CrossRefGoogle Scholar
  262. 65.
    a) Kilian, R., Brümmer, G., Hoffmann, H., Ilg, U., Maier, V., Wächter, O., and Widera, M., in: 26th MPA Seminar, Stuttgart 2000Google Scholar
  263. Kihan, R., Eberle, U., Brümmer, G., Hoffmann, H., Ilg, U., and Widera, M., in: loc.cit. [60d]Google Scholar
  264. Kilian, R„ Brümmer, G., Ilg, U., Meier, V., Teichmann, H., and Wächter, O., in: loc. cit. [60a], p. 529Google Scholar
  265. Kihan, R., Eberle, U., Brümmer, G., Hoffmann, H., Ilg, U., Maier, V., and Widera, M., in: loc.cit. [60c]Google Scholar
  266. Kilian, R.: private communication 2001Google Scholar
  267. 66.
    a) Macdonald, D.D. and Urquidi-Macdonald, M.: Corr. sci. 32 (1991) 51CrossRefGoogle Scholar
  268. Manahan, M-P., Sr., Macdonald, D.D., and Peterson, A.J.: ibid. 37 (1995) 189Google Scholar
  269. Macdonald, D.D.: ibid.38 (1996) 1003Google Scholar
  270. Engelhardt, G.R., Macdonald, D.D., and Urquidi-Macdonald, M.: ibid. 41 (1999) 2267Google Scholar
  271. iid.: ibid.43 (2001) 195Google Scholar
  272. 67.
    See e.g. a) Kaesche, H.: loc. cit. [8s]Google Scholar
  273. Wanhill, R.J.H.: British Corr. J. 10(1975) 69CrossRefGoogle Scholar
  274. 68.
    Chen, C., Beck, F.H., and Fontana, M.G.: Corr. NACE: 26 (1970) 135Google Scholar
  275. 69.
    Zhang, X.G., Verecken, J.: Corr. NACE 46 (1990) 136CrossRefGoogle Scholar
  276. 70.
    Haney, E.G. and Wearmouth, W.R.: Corr. NACE 25 (1969) 87Google Scholar
  277. a) Sedriks, A.J., Slattery, P.W., and Pugh, E.N., in: loc.cit. [2m], p.673Google Scholar
  278. Sedriks, A.J., Green, J.A., and Slattery, P.W.: Corr. NACE 24 (1968) 172Google Scholar
  279. Sedriks, A.J.: ibid. 25 (1969) 207Google Scholar
  280. 72.
    Mazza, F.: Werkstoffe u. Korr. 20 (1969) 199CrossRefGoogle Scholar
  281. 73.
    a) Powell, D.T. and Scully, J.C.: Corr. NACE 25 (1969) 483Google Scholar
  282. Sanderson, G., Powell, D., and Scully, J.C., in: loc.cit.[2n], p.638Google Scholar
  283. Scully, J.C. and Powell, D.T.: Corr.sci. 10 (1970) 719CrossRefGoogle Scholar
  284. Scully, J.C., in: loc. cit.[2f], p.l27Google Scholar
  285. Houis, A.C. and Scully, J.C.: ibid. 34 (1993) 837Google Scholar
  286. Simbi, D.J. and Scully, J.C.: Corr. sci. 34 (1993) 1743CrossRefGoogle Scholar
  287. iid.: Corr NACE 53 (1997)Google Scholar
  288. Kermani, M. and Scully, J.C.: Corr. sci. 18 (1978) 883CrossRefGoogle Scholar
  289. 74.
    a) Leith, J.R., Hightower, J.W., and Harkins, C.G.: Corr. NACE 26 (1970) 377Google Scholar
  290. Raymond, L. and Russel, R.J.: Corr. NACE 25 (1969) 250Google Scholar
  291. Boyd, W.K., in: loc. cit. [2m], p. 593Google Scholar
  292. a) Blackburn, M.J. and Williams, J.C., in: loc.cit. [2n], p. 620Google Scholar
  293. Feeney, J.A. and Blackburn, M.J., in: loc. cit. [2f], p.355Google Scholar
  294. Feeney, J.A., Blackburn, M.J., and Beck, T.R., in: Advances in Corrosion Science and Technology. (Fontana, M.G. and Staehle, R.W., eds.). Vol. 3. Plenum Press, New York 1973, p. 67Google Scholar
  295. 76.
    Leckie, H.P.: Corr. NACE: 23 (1967) 187Google Scholar
  296. 77.
    See e.g. Tomashov, N.D., Modestova, S.T., Galuznov, Borisova, E.A., and Zoztov, V.L., in: Corrosion of Metals and Alloys. Coll.l. N.L.L.S.T., Boston Spa 1964Google Scholar
  297. a) Speidel, M.O. and Hyatt, M.V., in: loc. cit. [2h], p.ll5Google Scholar
  298. Speidel, M.O., in: loc. cit. [2f]Google Scholar
  299. Vogt, H. and Speidel, M.O.: Corr. scl 40 (1998) 251CrossRefGoogle Scholar
  300. Holroyd, N.J.H., in: loc. cit. [2z], p.311Google Scholar
  301. 80.
    a) Friedrich, H., Kihan, H., and Kaesche, H., in: Proc. NATO Adv. Res. Workshop Modelling Aqueous Corrosion, Plymouth 1993. (Threthewey, K.R. and Roberge, P.R., eds.). NATO ASI Series E, Vol. 266. Kluwer Acad. Publ., Dordrecht, etc., 1994, p. 239Google Scholar
  302. Berggreen, J., Engell, H.-J., and Kaesche, H.: Werkstoffe u. Korr. 26 (1975) 599CrossRefGoogle Scholar
  303. Richter, J. and Kaesche, H.: ibid. 28 (1977) 602Google Scholar
  304. Stoll, F., Hornig, W., Richter, J., and Kaesche, H.: ibid. 29 (1974) 585Google Scholar
  305. Richter, J., Hornig, W., and Kaesche, H.: ibid. 35 (1984) 23Google Scholar
  306. Rippstein, K., Baumgärtner, M., Konys, J., and Kaesche, H.: Z. Metallkunde 75 (1984) 291Google Scholar
  307. Baumgärtner, M. and Kaesche, H.: Corr. NACE 44 (1988) 231CrossRefGoogle Scholar
  308. Wenzel, G., Knörnschild, G., and Kaesche, H.: Werkstoffe u. Korr. 42 (1991) 449CrossRefGoogle Scholar
  309. iid.: Extended Abstract N3 129, Spring Meeting Electrochem Soc., Honolulu 1993Google Scholar
  310. Nikol, Th. and Kaesche, H.: Preprints Conf. Eurocorr, Karlsruhe 1987. DECHEMA, Frankfurt, 1987, p. 505Google Scholar
  311. David, W., Stellwag, B., and Kaesche, H. 59 (1983) E 147Google Scholar
  312. Roth, A. and Kaesche, H., in: Proc. 5th AlLi Conf., Wilhamsburg 1989, Vol. IIIGoogle Scholar
  313. iid., in: Proc. 6th AlLi Conf., Garmisch-Partenkirchen 1991; n) Kaiser, H., Lenz. E., and Kaesche, H., in: loc. cit. [2k]Google Scholar
  314. Lenz, E.: Doctoral Thesis, University Erlangen-Nürnberg 1978Google Scholar
  315. 81.
    Sugimoto, K., Hoshino, K, Kageyama, M., Kageyama, S., and Sawada, Y.: Corr. scl 15 (1975) 709CrossRefGoogle Scholar
  316. 82.
    a) Gruhl, W.: Metall 17 (1963) 197Google Scholar
  317. id.: Z. Metallkunde 53 (1963) 670Google Scholar
  318. Ratke, L. and Gruhl, W.: Werkstoffe u. Korr. 31 (1980) 768CrossRefGoogle Scholar
  319. iid.: Z. Metallkunde 71 (1980) 568Google Scholar
  320. Brungs, D. and Gruhl, W.: Metall 24 (1970) 217Google Scholar
  321. 83.
    Shastry, C.R., Levy, M., and Joshi, A.: Corr. scL 21 (1981) 673CrossRefGoogle Scholar
  322. a) Haynie, F.H. and Boyd, W.K., in: loc. cit. [2n], p. 580Google Scholar
  323. Gest, R.J. and Trioano, A.R.: Corr. NACE 30 (1974) 274Google Scholar
  324. 85.
    Lynch, S.P.: ibid. 24 (1984) 375Google Scholar
  325. 86.
    a) Pugh, E.N.: Corr. NACE 41 (1985) 517CrossRefGoogle Scholar
  326. Bertocci, U. and Pugh, E.N., in: loc. cit. [2m], p. 273Google Scholar
  327. Bertocci, U., Pugh, E.N., and Ricker, R.E., in: loc. cit. [2z], p. 273Google Scholar
  328. Beggs, D.V., Hahn, M.T., and Pugh, E.N., in: Proc. Conf. Hydrogen Embrittlement and Stress Corrosion Cracking, 1984. ASTM Metals Park 1984Google Scholar
  329. Hahn, M.T. and Pugh, E.N.: Corr. NACE 36 (1980) 380Google Scholar
  330. a) Wendler-Kalsch, E., in: loc. cit. [21), p. 102Google Scholar
  331. Pinchback, T.R., Clough, S.P., and Heidt, L.A.: Metal Trans. 6A (1975) 1479Google Scholar
  332. Takano, M., Teramoto, K., and Nakayama, T.: Corr. scL 21 (1981) 459CrossRefGoogle Scholar
  333. 88.
    a) Cassagne T.B., Flanagan, W.F., and Lichter, B.D.: Metal Trans. 17A (1986) 703Google Scholar
  334. Lichter, G.B., Flanagan, W.F., Lee, J.B., and Zhu, M., in: loc. cit. [2z], p. 251Google Scholar

Copyright information

© Springer-Verlag Berlin Heidelberg 2003

Authors and Affiliations

  • Helmut Kaesche
    • 1
  1. 1.Institute for Materials SciencesUniversity Erlangen-NürnbergErlangenGermany

Personalised recommendations