Creep-Fatigue Crack Growth

  • Hermann Riedel
Part of the Materials Research and Engineering book series (MATERIALS)

Abstract

In this chapter, the technologically important subject of fatigue at high temperatures is taken up again. In Chapter 18, fatigue failure due to more or less homogeneous cavitation of grain boundaries in the whole specimen was discussed, whereas now failure by the growth of cracks under cyclic-loading conditions will be investigated.

Keywords

Fatigue Crack Crack Growth Rate Fatigue Crack Growth Crack Closure Fatigue Crack Growth Rate 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Copyright information

© Springer-Verlag Berlin Heidelberg 1987

Authors and Affiliations

  • Hermann Riedel
    • 1
    • 2
  1. 1.Max-Planck-Institut für EisenforschungDüsseldorfFR Germany
  2. 2.Fraunhofer-Institut für WerkstoffmechanikFreiburgFR Germany

Personalised recommendations