Abstract

The working conditions of the helium operated low temperature field ion microscope are described. The resolution of atom chains of 2,74 Å spacing, and of a two dimensional net of 2,77 Å spacing is shown in photographs, while a visual observation of a net plane resolution of 2,35 Å is reported. Field evaporation at low temperatures produces perfectly clean and regularly built surfaces, which will not be contaminated during observation by even one atom, in spite of the use of a ground joint for easy sample replacement. The rate of field evaporation limits the application to about 8 elements for best image quality, and one other dozen of metals with limited image stability. Field evaporation of the refractory metals yields doubly charged ions. A number of high resolution photographs of wolfram, rhenium, iridium, platinum and nickel crystals are shown, exhibiting atomic details of stacking faults, dislocations, subgrain boundaries and slip bands. The effect of recovery of platinum and iridium crystals is demonstrated. Fatigue experiments are made with platinum crystals, exposing them during the observation in the microscope to a cycling stress of 1000 kg/mm2. Operation of the cycling stress at audio frequencies let to the discovery of resonance vibrations. These seem to be characteristic for the metal, and they may represent energy exchange frequencies between high frequency lattice vibration modes.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Literatur

  1. 1.
    Müller, E. W.: Z. Physik 106, 541 (1937);ADSCrossRefGoogle Scholar
  2. 1a.
    Müller, E. W.: Z. Physik 108, 668 (1938).ADSCrossRefGoogle Scholar
  3. 2.
    Good, jr. R. H., and E. W. Müller: Feldemission, Handbuch der Physik. Bd. XXI, 176, 1956.Google Scholar
  4. 3.
    Müller, E. W.: Naturwissenschaften 29, 533 (1941).ADSCrossRefGoogle Scholar
  5. 4.
    Müller, E. W.: Z. Physik 131, 136 (1951);ADSCrossRefGoogle Scholar
  6. 4a.
    Müller, E. W.: Ergebn. exakt. Naturwiss. 27, 290 (1953).CrossRefGoogle Scholar
  7. 5.
    Müller, E. W.: Physic. Rev. 102, 618 (1956).ADSCrossRefGoogle Scholar
  8. 6.
    Müller, E. W.: J. appl. Physics 27, 474 (1956);ADSCrossRefGoogle Scholar
  9. 6a.
    Müller, E. W.: Z. Naturforsch. 11a, 88 (1956).ADSGoogle Scholar
  10. 7.
    Müller, E. W.: J. appl. Physics 28, 1 (1957).ADSCrossRefGoogle Scholar
  11. 8.
    Müller, E. W.: Ann. Physik 6. Folge 20, 315 (1957).Google Scholar
  12. 9.
    Müller, E. W.: Z. Elektrochem. 61, 43 (1957).Google Scholar
  13. 10.
    Drechsler, M., and G. Pankow: Proc. int. Conf. Electron Microscopy. p. 405 London 1954.Google Scholar
  14. 11.
    Rose, D. J.: J. appl. Physics 27, 215 (1956).ADSCrossRefzbMATHGoogle Scholar
  15. 12.
    Müller, E. W.: Field Emission Symposium, Chicago (June 1958).Google Scholar
  16. 13.
    Müller, E. W. and J. F. Mulson: Bull. Amer. phys. Soc. 3, 69 (Jan. 1958).Google Scholar
  17. 14.
    Drechsler, M.: Z. Elektrochem. 61, 48 (1957).Google Scholar
  18. 15.
    Müller, E. W.: Acta metallurgica 6, 620 (1958).CrossRefGoogle Scholar
  19. 16.
    Lang, A. R.: J. appl. Physics 28, 497 (1957).ADSCrossRefGoogle Scholar
  20. 17.
    Müller, E. W.: Bull. Amer. phys. Soc. 3, 265 (1958).Google Scholar
  21. 18.
    Fitzgerald, E. R.: Physics Rev. 108, 690 (1957).ADSCrossRefGoogle Scholar
  22. 19.
    Fermi, E., J. Pasta and S. Ulam: Los Alamos Sci. Lab. Rep. LA1940 (1955).Google Scholar
  23. 1.
    Müller, E. W.: Z. Physik 131, 136 (1951).ADSCrossRefGoogle Scholar
  24. 2.
    Müller, E. W. and K. Bahadur: Physic. Rev. 102, 624 (1956).ADSCrossRefGoogle Scholar
  25. 2a.
    Müller, E. W.: Physic. Rev. 102, 618 (1956).ADSCrossRefGoogle Scholar
  26. 3.
    Müller, E. W.: Z. Naturforsch. 11a, 88 (1956).ADSGoogle Scholar
  27. 4.
    Good, R. H., u. E. W. Müller: Handbuch der Physik 21, 174 (1956).Google Scholar
  28. 5.
    Müller, E. W.: J. appl. Physics 27, 474 (1956).ADSCrossRefGoogle Scholar
  29. 6.
    Müller, E. W.: Z. Elektrochem. 61, 43 (1957).Google Scholar
  30. 7.
    Müller, E. W.: Scient. Amer. 196, 113 (1957).CrossRefGoogle Scholar
  31. 8.
    Müller, E. W.: J. appl. Physics 28, 1 (1957).ADSCrossRefGoogle Scholar
  32. 9.
    Müller, E. W.: Ann. Physik 6. F. 20, 315 (1957).CrossRefGoogle Scholar
  33. 10.
    Drechsler, M., u. G. Pankow: Proc. Conf. Electron Microscopy, London 1954. Erscheinungsjahr 1957; mit Zusätzen bei der Korrektur (Nov. 1955), die sich aus weiteren Experimenten ergeben haben. Weiterhin wurden Ergebnisse über die Feldverdampfung bei Zimmertemperatur und die Bedeutung der Polarisierbar-keit für das Auflösungsvermögen berücksichtigt, die Prof. Müller uns freundlicherweise zur Verfügung gestellt hatte, und die in Physic. Rev. 102, 618, 624 (1956) veröffentlicht sind.Google Scholar
  34. 11.
    Drechsler, M., u. G. Pankow, u. R. Vanselow: Z. physik. Chem. N. F. 4, 249 (1955).CrossRefGoogle Scholar
  35. 12.
    Drechsler, M., u. G. Pankow, u. R. Vanselow: Z. physik. Chem. N. F. 6, 272 (1956).CrossRefGoogle Scholar
  36. 13.
    Drechsler, M., u. G. Pankow, u. R. Vanselow: Z. Metallkunde 47, 305 (1956).Google Scholar
  37. 14.
    Drechsler, M., u. G. Pankow, u. R. Vanselow: Z. Elektrochem. 61, 48 (1957).Google Scholar
  38. 15.
    Becker, J. A., and R. G. Brandes: J. chem. Physics 23, 1323 (1955).ADSCrossRefGoogle Scholar
  39. 16.
    Dyke, W. P., and W. W. Dolan: Advanc. in Electronics 8, 89 (1956).CrossRefGoogle Scholar
  40. 17.
    Müller, E. W.: Ergebn. exakt. Naturwiss. 27, 290 (1953).CrossRefGoogle Scholar
  41. 18.
    Drechsler, M., u. E. Henkel: Z. angew. Physik 6, 341 (1954).Google Scholar
  42. 19.
    Müller, E. W.: Z. Physik 120, 270 (1943).ADSCrossRefGoogle Scholar
  43. 20.
    Müller, E. W.: Z. Physik 126, 642 (1949).ADSCrossRefGoogle Scholar
  44. 21.
    Drechsler, M.: Begleitveröffentlichung für Film C 660 (1955.) Inst. f. d. Wiss. Film. Göttingen.Google Scholar
  45. 22.
    Rose, D. J.: J. appl. Physics 27, 215 (1956).ADSCrossRefzbMATHGoogle Scholar

Copyright information

© Springer-Verlag OHG. Berlin · Göttingen · Heidelberg 1960

Authors and Affiliations

  • Erwin W. Müller
    • 1
  • M. Drechsler
    • 2
    • 3
  • P. Wolf
    • 2
  1. 1.Pennsylvania State UniversityUniversity ParkPa.USA
  2. 2.Fritz-Haber-InstitutMax-Planck-GesellschaftBerlin-DahlemDeutschland
  3. 3.Kernreaktor GmbH.KarlsruheDeutschland

Personalised recommendations