Chapter

Abstract

In cathodic etching by ion bombardment, we find ourselves concerned with several problems. One of these is the temperature of the specimen. In the absence of effective cooling the temperature rise can be quite large. At 6 W/cm2 on the specimen in a particular experimental arrangement patterned after those of other investigators such as Padden and Cain, and Bieklein and Mastel, the author has observed a temperature rise of 700° C. Merely permitting the small specimen to rest on a water-cooled base does not always eliminate the rise; it is necessary to clamp it to the base to reduce the rise to a few degrees. The ion bombardment power is large because of the current-voltage characteristic of the glow discharge — it required about 2 kV to obtain 20 mA at an argon pressure of about 75 μ.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Bibliographie

  1. 1.
    Fert, Cil: C. R. Acad. Sci. (Paris) 238, 233 (1954).Google Scholar
  2. 2.
    Trillat, J. J.: J. Chim. physique 53, 570 (1956).Google Scholar
  3. 3.
    Ladage, A.: Z. Physik 144, 354 (1956).ADSCrossRefGoogle Scholar
  4. 4.
    Gribi, M., u. L. Wegmann: Seite 403 dieses Bandes.Google Scholar
  5. 5.
    Moore, W.J., C. D. O’Briain and Amelie Lindner: Ann. N. Y. Acad. Sci. 67, 600 (1957).ADSCrossRefGoogle Scholar

Literatur

  1. 1.
    Steinemann, S., et J. J. Trillat: Seite 401 dieses Bandes.Google Scholar
  2. 2.
    Steinemann, S.: Experientia (Basel) 13, 417 (1957).CrossRefGoogle Scholar
  3. 3.
    Gribi, M., u. L. Wegmann: Ionenätzung als Materialuntersuchungsmethode im Elektronendiffraktographen. Dechema-Monogr. Frankfurt 1958 (im Druck).Google Scholar
  4. 4.
    Moore, W. J., C. D. O’Briain and Amelie Linder: Ann. N. Y. Acad. Sci. 67, 600 (1957).ADSCrossRefGoogle Scholar
  5. 5.
    Vgl. auch E. Bauer: Elektronenbeugung 1958. München: Verlag Moderne Industrie.Google Scholar
  6. 6.
    Gribi, M., M. Thürkauf, W. Villiger u. L. Wegmann: Ein 70 kV-Elektronenmikroskop mit kalter Kathode und elektrostatischem Objektiv. Optik 16, 65 (1959)Google Scholar
  7. 1.
    Bethge, H.: Fortschr. Mineral. 35, 156 (1957).Google Scholar
  8. 2.
    Amelinckx, S.: Acta metallurgica 2, 848 (1954);CrossRefGoogle Scholar
  9. Gilman, J. J., W. G. Johnston and G. W. Sears: J. appl. Physics 29, 747 (1958).ADSCrossRefGoogle Scholar
  10. 3.
    van der Vorst, W., W. Dekeyser and O. Goche: Naturwissenschaften 41, 116 (1954).ADSCrossRefGoogle Scholar
  11. 4.
    Bethge, H.: Z. wiss. Mikrosk. 62, 122 (1954).Google Scholar
  12. 5.
    Kern, E., u. H. Pick: Z. Physik 134, 610 (1953).ADSCrossRefGoogle Scholar
  13. 1.
    Schrader, A.: Arch. Eisenhüttenwes. 29, 793 (1958)Google Scholar
  14. 2.
    Schrader, A.: Z. wiss. Mikrosk. 60, 309 (1952);Google Scholar
  15. Wever, F., u. A. Schrader: Arch. Eisenhüttenwes. 26, 475 (1955).Google Scholar
  16. Schrader, A., Rev. univ. Mines 9 Sér. 99, 537 (1956);Google Scholar
  17. Koch, W., A. Krisch u. A. Schrader: Arch. Eisenhüttenwes. 28, 445 (1957).Google Scholar
  18. 3.
    Fisher, R. M.: A. S. T. M., Spec. Techn. Publ. Nr. 155, 49 (1953).Google Scholar
  19. 4.
    Koch, W., A. Schrader, A. Krisch und H. Rohde: Stahl und Eisen 78, 1251 (1958).Google Scholar
  20. 5.
    Fischer, W. A., u. A. Hoffmann: Arch. Eisenhüttenees. 29, 107 (1958).Google Scholar
  21. 6.
    Pitsch, W., Schrader A.: Arch. Eisenhüttenwes. 29, 715 (1958).Google Scholar
  22. 7.
    Engell, H. J.: Arch. Eisenhüttenwes. 29, 73 (1958).Google Scholar
  23. Koch, W., u. H. Sundermann: Elektrochemische Grundlagen der Isolierung von Gefügebestandteilen in metallischen Werkstoffen. Forschungsber. 599 des Wirtschaftsministeriums Nordrhein-Westfalen (1958).Google Scholar

Bibliographie

  1. 1.
    Eguchi, I., et C. Asada: Métaux, Corrosion, Industries, n°376 483 (1956).Google Scholar

Copyright information

© Springer-Verlag OHG. Berlin · Göttingen · Heidelberg 1960

Authors and Affiliations

  • C. J. Calbick
    • 1
  • S. Steinemann
    • 2
    • 3
  • J. J. Trillat
    • 2
    • 3
  • M. Gribi
    • 4
  • L. Wegmann
    • 4
  • H. Bethge
    • 5
  • K. Mihama
    • 6
  • Angelica Schrader
    • 7
  • I. Eguchi
    • 8
  1. 1.Bell Telephone LaboratoriesIncorporated Murray HillNew JerseyUSA
  2. 2.Laboratoire Suisse de Recherches HorlogèresNeuchâtelSuisse
  3. 3.Centre National de la Recherche ScientfiqueBellevue (S. et O.)France
  4. 4.Abteilung für ElektronengeräteFirma Trüb, Täuber Co. AGZürichSchweiz
  5. 5.Institut für Experimentelle PhysikMartin-Luther-Universiät Halle-WittenbergDeutschland
  6. 6.Centre National de la Recherche ScientifiqueBellevue, (S-et-O)France
  7. 7.Aus dem Max-Planck-Institut für EisenforschungDüsseldorfDeutschland
  8. 8.Laboratoire des RecherchesDaidô Steel Co.NagoyaJapon

Personalised recommendations