High Temperature Polymer Nanocomposites

  • Chapter
  • First Online:
Book cover Structural Nanocomposites

Part of the book series: Engineering Materials ((ENG.MAT.))

Abstract

The chapter on High Temperature Polymer Nanocomposites mainly covers the advancements made in the research on varied composite materials and their novel innovations for high temperature applications. The chapter begins with a prelude on existing polymers of thermoplastic or thermosets and also a combination of the two to exploit the dual advantage of both high temperature thermoplastics and thermosets. The polymer composites are developed and implemented for varied temperature regimes in the range of 120–250°C, 250–350°C specially suited for aerospace applications. Further research work is under progress to explore the material suitable for temperatures above 350°C. The initial section explains on the applicability of polymer composites having matrices such as either liquid crystalline polymer, cyanates, polyimides or bismaleimides which are reinforced with either the carbon, glass or aramid fibres especially continuous fibre which provides improved material and physical properties. The polymer-composites are assessed for performance of the matrices and the composites not only for their strength or stiffness but also for their resistance to cracking, minimum loss of weight, brittleness due to cross-linking and other properties that may degrade the performance of the composites over the long period of high temperature applications. This section mentions on the literature reviews having come up with research in progress on other types of resins for high temperature applications namely the oligomers such as the acetylene terminated polyimides or the norbornene terminated polyimides. The second section is concerned with the polymer-nanocomposites for high temperature applications. In this section, the role of nanofillers in the enhancement of composite properties is discussed. The various forms of nanofillers are the nanoclay, nanofibres, carbon nanotubes, Polyhedral OligoSilsesquioxanes (POSS) and nano-oxides where they reinforce polymer chain at molecular scale as against the carbon fibres of macroscopic scale seen in polymer-composites. In a nanocomposite the thermal properties depends on the filler’s nature, rate and dispersion in a matrices. The applications have been as fire retardant materials or for re-entry applications in aerospace vehicles. Research on nanofillers is still at its nascent stage that ample scope is available for exploring the potential of various nanofillers for high temperature applications and as fire retardant materials. Some polymer thermosets such as PMR-15 (Polymerization from Monomeric Reactants) are the most extensively used resin for applications where long term thermal stability is required at 300°C. This section dwells on other progress under way in the field of nanocomposites as high temperature nanocomposites. The last section presents a review on advanced materials for high temperature applications, especially applicable for the next generation aerospace vehicles. The issues concerning adhesives for joining of surfaces exposed to high temperatures, the effective role of nano-fillers for improving fracture toughness at high temperature etc. It is seen that the most promising resin for high temperatures has been the polyimides (315°C). This resin has high Tg (400°C) and other good characteristics such as good micro cracking resistance, low moisture absorption and low toxicity. There are various grades of polyimides under development. Overall, the chapter provides a glimpse on the effective developments in the field of polymer-composites and nanocomposites for high temperature applications especially for aerospace vehicle and automotives.

This is a preview of subscription content, log in via an institution to check access.

Access this chapter

Log in via an institution
Chapter
USD 29.95
Price excludes VAT (USA)
  • Available as PDF
  • Read on any device
  • Instant download
  • Own it forever
eBook
USD 84.99
Price excludes VAT (USA)
  • Available as EPUB and PDF
  • Read on any device
  • Instant download
  • Own it forever
Hardcover Book
USD 109.99
Price excludes VAT (USA)
  • Durable hardcover edition
  • Dispatched in 3 to 5 business days
  • Free shipping worldwide - see info

Tax calculation will be finalised at checkout

Purchases are for personal use only

Institutional subscriptions

References

  1. Cuppoletti, J.: Metal, ceramic and polymeric composites for various uses, ISBN 978-953-307-353-8, InTech, 20 July (2011)

    Google Scholar 

  2. Gan, M., et al.: Degradation of high temperature composites under thermal spike loads, Sampe Europe Conference & Exhibition

    Google Scholar 

  3. Dimitrienko, Y.I.: Thermomechanics of Composites under High Temperatures. Kluwer Academic Publishers, Dordrecht (1999)

    Book  Google Scholar 

  4. Hoebergen, A., Holmberg, J.A.: Vacuum Infusion, ASM Handbook, vol. 21, pp. 501–515. Composite, Materials Park (OH) (2001)

    Google Scholar 

  5. Mangalgiri, P.D.: Polymer-matrix composites for high-temperature applications. Defence Sci. J. 55(2), 175–193 (2005)

    Google Scholar 

  6. Boyd, J.D., Chang, G.E.C.: Bismaleimide composites for advanced high-temperature applications. Int. SAMPE Symp. 38, 357–369 (1993)

    Google Scholar 

  7. Manocha, L.M.: High performance carbon–carbon composites. Sadhana 28(1–2), 349–358 (2003)

    Article  Google Scholar 

  8. Potter, K., Foster, S., Batho, Y.: High temperature high performance composites. www.bris.ac.uk/composites (2012). 17 April 2012

  9. Composite materials for space and high temperature applications. www.umeco.com

  10. Simos, N.: Composite materials under extreme radiation and temperature environments of the next generation nuclear reactors. www.intechopen.com (2011)

  11. Bonal, J.-P., Kohyama, K., van der Laan, J., Snead, L.: Graphite, ceramics and ceramic composites for high-temperature nuclear power systems. MRS Bull. 34, 28–34 (2009)

    Article  Google Scholar 

  12. Tomar, V.: Nanotechnology thought leaders series, school of aeronautics and astronautics, Purdue University (2011)

    Google Scholar 

  13. Marquis, D.M.: Properties of nanofillers in polymer. www.intechopen.com (2011)

  14. Morgan, A.B.: Polymer-clay nanocomposites: Design and application of multi-functional materials. Mater. Matters 2, 20–25 (2007)

    Google Scholar 

  15. Frank, K.: Book review: Polymer nanocomposites—processing, characterization, and applications. J. Eng. Fibers Fabr. 3(3) (2008)

    Google Scholar 

  16. Tzeng, S.S.: Evolution of microstructure and properties of phenolic resin-based carbon/carbon composites during pyrolysis Mater. Chem. Phys. 73, 162–169 (2002)

    Google Scholar 

  17. Sambarkar, P.P., et al.: Polymer nanocomposites: An overview. Int. J. Pharm. Pharm. Sci 4(2), 60–65 (2012)

    Google Scholar 

  18. Alexandre, M., Dubois, P.: Polymer-layered silicate nanocomposites: Preparation, properties and uses of a new class of materials. Mater Sci. Eng. R 28, 1–63 (2000)

    Article  Google Scholar 

  19. Sheng, X.: Polymer nanocomposites for high-temperature composite repair, Iowa State University Digital Repository @ Iowa State University (2008)

    Google Scholar 

  20. Kurahatti, R.V., et al.: Defence applications of polymer nanocomposites. Defence Sci. J. 60(5), 551–563 (2010)

    Article  Google Scholar 

  21. Hussain, F., et al.: Review article: Polymer-matrix nanocomposites, processing, manufacturing, and application: An overview. J. Compo. Mater. 40(17), 1511–1575 (2006)

    Article  Google Scholar 

  22. Takeichi, T., et al.: High-performance polymer alloys of polybenzoxazine and bismaleimide. Polymer 49, 1173–1179 (2008)

    Article  Google Scholar 

  23. Srikanth, I., Daniel, A., Kumar, S., Padmavathi, N., Singh, V., Ghosal, P., et al.: Nano silica modified carbon—phenolic composites for enhanced ablation resistance. Scr. Mater. 63, 200–203 (2010)

    Article  Google Scholar 

  24. Marshall Space Flight Cen, Application of Ablative Composites to Nozzles for Reusable Solid Rocket Motors, practice no. Pd-ed-1218 page 1 of 8 (1989)

    Google Scholar 

  25. Lao, S., Ho, W., Ngyuen, K., Koo, J.H.: Flammabiltiy, mechanical, and thermal properties of polyamide nanocomposites. In Proceedings of SAMPE 2005, Seattle, WA (2005)

    Google Scholar 

  26. Zhang, Z., Yang, J.L.: Creep resistant polymeric nanocomposites. Polymer 45, 3481–3485 (2004)

    Article  Google Scholar 

  27. Walker, L.S., et al.: Toughening in graphene ceramic composites. ACS Nano. Org. 5(4), 3182–3190 (2011)

    Article  Google Scholar 

  28. Poyato, R., et al.: Aqueous colloidal processing of single-wall carbon nanotubes and their composites with ceramics. Nanotechnology 17, 1770–1777 (2006)

    Article  Google Scholar 

  29. Stankovich, S., Dikin, D.A., Dommett, G.H.B., Kohlhaas, K.M., Zimney, E.J., Stach, E.A., Piner, R.D., Nguyen, S.B.T., Ruoff, R.S.: Graphene-based composite materials. Nature 442, 282–286 (2006)

    Article  Google Scholar 

  30. Tomar, V., Gan, M.: Temperature dependent nanomechanics of si-c-n nanocomposites with an account of particle clustering and grain boundaries. Submitted to. Int. J. Hydrogen Energy (2009)

    Google Scholar 

  31. Niihara, K., Izaki, K., Kawakami, T.: Hot-pressed Si3N4-32%SiC nanocomposites from amorphous Si-C-N powder with improved strength above 1,200 °C. J. Mater Sci. Lett. 10, 112–114 (1990)

    Article  Google Scholar 

  32. Wan, J., Duan, R.-G., Gasch, M.J., Mukherjee, A.K.: Highly creep-resistant silicon nitride/silicon carbide nano–nano composites. J. Am. Ceram. Soc. 89(1), 274–280 (2006)

    Article  Google Scholar 

  33. Niihara, K.: New design concept for structural ceramics-ceramic nanocomposites. J. Ceram. Soc. Jpn: Centennial Memorial Issue 99(10), 974–982 (1991)

    Article  Google Scholar 

  34. Trick, K.A., Saliba, T.E.: Mechanisms of the pyrolysis of phenolic resin in a carbon/phenolic composite. Carbon 33, 1509–1515 (1995)

    Article  Google Scholar 

  35. Chen, Y., Chen, P., Hong, C., Zhang, B., Hui, D.: Improved ablation resistance of carbon–phenolic composites by introducing zirconium diboride particles. Compos. B 47, 320–325 (2013)

    Article  Google Scholar 

  36. Vaia, R.A., Price, G., Ruth, P.N., Nguyen, H.T., Lichtenhan, J.: Polymer/layered silicate nanocomposites as high performance ablative materials. Appl. Clay Sci. 15, 67–92 (1999)

    Article  Google Scholar 

  37. Abdalla, M.O., Ludwick, A., Mitchell, T.: Boron-modified phenolic resin for high performance application. Polymer 44, 7353–7359 (2003)

    Article  Google Scholar 

  38. Corral, E.L., Walker, L.S.: Improved ablation resistance of C–C composites using zirconium diboride and boron carbide. J. Eur. Ceram. Soc. 30(11), 2357–2364 (2010)

    Article  Google Scholar 

  39. Pulci, G., Tirillò, J., Fossati, F., Bartuli, C., Valente, T.: Carbon–phenolic ablative materials for re-entry space vehicle: Manufacturing and properties. Compos. Part A: Appl. Sci. Manuf. 41(10), 1483–1490 (2010)

    Article  Google Scholar 

  40. Bahramian, A.R., et al.: High temperature ablation of kaolinite layered silicate/phenolic resin/asbestos cloth nanocomposite. J. Hazard. Mater. 150, 136–145 (2008)

    Article  Google Scholar 

  41. Kashiwagi, T., Harris, R.H., Zhang, X., Briber, R.M., Cipriano, B.H., Raghavan, S.R., Awad, W.H., Shields, J.R.: Flame retardant mechanism of polyamide 6-clay nanocomposites. Polymer 45, 881–891 (2004)

    Article  Google Scholar 

  42. Vaia, R.A., Price, G., Ruth, P.N., Nguyen, H.T., Lichtenhan, J.: Polymer/layered silicate nanocomposites as high performance ablative materials. Appl. Clay Sci. 15, 67–92 (1999)

    Article  Google Scholar 

  43. Collins, TJ, et al.: High-temperature structures, adhesives, and advanced thermal protection materials for next-generation Aeroshell design

    Google Scholar 

  44. Golub, M.A., Parker, J.A.: Polymeric materials for unusual service conditions. J. App. Poly. Sci., Appl. Poly. Symp. No. 22 Board (1973)

    Google Scholar 

  45. Srikanth, I., et al.: Mechanical, thermal and ablative properties of zirconia, CNT modified carbon/phenolic composites. Compos. Sci. Technol. 80, 1–7 (2013)

    Article  Google Scholar 

  46. Zhang, X., Xu, L., Du, S., Han, W., Han, J.: Crack-healing behavior of zirconium diboride composite reinforced with silicon carbide whiskers. Scripta Mater. 59, 1222–1225 (2008)

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Head: Materials Engineering, DIAT(DU), Girinagar, Pune, Maharashtra, 411025, India

    K. Balasubramanian

  2. Department of Airforce, MILIT, Girinagar, Pune, Maharashtra, 411025, India

    Manoj Tirumalai

Authors
  1. K. Balasubramanian
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Manoj Tirumalai
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to K. Balasubramanian .

Editor information

Editors and Affiliations

  1. Institute for Innovation, Design & Susta School of Engineering, Robert Gordon University, Aberdeen, United Kingdom

    James Njuguna

Rights and permissions

Reprints and permissions

Copyright information

© 2013 Springer-Verlag Berlin Heidelberg

About this chapter

Cite this chapter

Balasubramanian, K., Tirumalai, M. (2013). High Temperature Polymer Nanocomposites. In: Njuguna, J. (eds) Structural Nanocomposites. Engineering Materials. Springer, Berlin, Heidelberg. https://doi.org/10.1007/978-3-642-40322-4_7

Download citation

Publish with us

Policies and ethics

Search

Navigation