Direct Epitaxial Lateral Overgrowth of GaN on Sapphire

  • Viswas SadasivanEmail author
  • Manish Mathew
Conference paper
Part of the Springer Proceedings in Physics book series (SPPHY, volume 215)


A regrowth-free direct epitaxial lateral overgrowth method for MOCVD GaN on Sapphire is demonstrated here. The mask used is 2 μm thick SiO2 stripes with 5 μm separation and 19 μm period, formed on c-plane sapphire substrate. An uninterrupted two step growth process has been developed to obtain appropriate growth rates in vertical and horizontal directions. Coalescence has been achieved when the stripes were aligned perpendicular to the primary cut. The AFM image revealed ~1.4° surface tilt in the regrown regions. Photoluminescence study showed uniformity in the central region of the wafer and slight broadening of the spectrum, possibly due to defects in the coalescence region.



This work is funded by SERB grant number: PDF/2016/003757 and the facilities are provided by CEERI Pilani.


  1. 1.
    H. Morkoç, Handbook of Nitride Semiconductors and Devices Vol 1 Material Properties Physics and Growth, vol. 1, 3 vols. (WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim)Google Scholar
  2. 2.
    M. Takeya, K. Yanashima, T. Asano, T. Hino, S. Ikeda, K. Shibuya, S. Kijima, T. Tojyo, S. Ansai, S. Uchida, Y. Yabuki, T. Aoki, T. Asatsuma, M. Ozawa, T. Kobayashi, E. Morita, M. Ikeda, AlGaInN high-power lasers grown on an ELO-GaN layer. Proc. Tenth Int. Conf. Met. Vap. Phase Epitaxy 221(1), 646–651 (2000)ADSCrossRefGoogle Scholar
  3. 3.
    Q. Ji, L. Li, W. Zhang, J. Wang, P. Liu, Y. Xie, T. Yan, W. Yang, W. Chen, X. Hu, Dislocation reduction and stress relaxation of GaN and InGaN multiple quantum wells with improved performance via serpentine channel patterned mask. ACS Appl. Mater. Interfaces 8(33), 21480–21489 (2016)CrossRefGoogle Scholar
  4. 4.
    F. Bertram, T. Riemann, J. Christen, A. Kaschner, A. Hoffmann, K. Hiramatsu, T. Shibata, N. Sawaki, Epitaxial lateral overgrowth of GaN structures: spatially resolved characterization by cathodoluminescence microscopy and micro-Raman spectroscopy. Mater. Sci. Eng., B 59(1), 117–121 (1999)CrossRefGoogle Scholar

Copyright information

© Springer Nature Switzerland AG 2019

Authors and Affiliations

  1. 1.Department of Electronics and Communication EngineeringAmrita Vishwa VidyapeethamAmritapuriIndia
  2. 2.Optoelectronics and MOEMS GroupCSIR-CEERIPilaniIndia

Personalised recommendations