Abstract
In this work, the failure analysis of a bellows expansion joint installed in a heat exchanger is shown. The analysis was performed using the techniques of visual inspection, chemical analysis, mechanical tests, metallographic and fractographic examination. The results show that the chemical composition, mechanical properties and microstructure correspond to the material design specification. While the macroscopic fractographic analysis revealed the presence of circumferential cracking, adjacent to the weld bead and expansion joint. The trajectory of the crack is simple without secondary ramifications or cracks, nor was plastic deformation associated with the fracture observed. The scanning electron microscopy results, show the presence of thin lines in the form of grooves, parallel to the crack propagation front, that are identified as microscopic striations, typical of fatigue fractures. Thus, the bellows expansion joint failure was identified as a fatigue fracture, due these accessories work in the presence of fluctuating loads. Although, fatigue failure is common in this type of components, after a long time of service; However, the results of this research demonstrate that the movements and vibrations in the heat exchanger, in combination with the expansion joint installation by fillet welding in the overlapping sleeve and misalignment of the joint, are able to generate the level of stress required to drive the fatigue failure, even though the heat exchanger was not in service.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
References
PACIFIC HOSEFLEX. Expansion Joint. Recovery from https://www.hoseflex.com/wp-content/uploads/2014/07/Expansion-Joints.pdf2.
ASTM B127-05(2014) “Standard Specification for Nickel-Copper Alloy (UNS N04400) Plate, Sheet, and Strip”.
ASTM E2332-04 “Standard Practice for Investigation and Analysis of Physical Component Failures (Withdrawn 2004)”.
ASTM E384 “Standard Test Method for Knoop and Vickers Hardness of Material”. 5. ASTM B127-05(2014) “Standard Specification for Nickel-Copper Alloy (UNS N04400) Plate, Sheet, and Strip”.
ASTM E18-17 “Standard Test Methods for Rockwell Hardness of Metallic Materials”.
ASTM A106/A106 M-15 “Standard Specification for Seamless Carbon Steel Pipe for High-Temperature Service”.
Acknowledgements
The authors would like to acknowledge the National Polytechnic Institute (IPN), the National Council of Science and Technology (CONACYT) and the Analysis Integrity of Pipelines Group (GAID-IPN) for the support to carry out this research.
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2018 Springer International Publishing AG
About this paper
Cite this paper
Villagómez, I., González, J.L., Trujillo, J.J., Rivas, D. (2018). Fatigue Analysis in a Bellow Expansion Joint Installed a Heat Exchanger. In: Ambriz, R., Jaramillo, D., Plascencia, G., Nait Abdelaziz, M. (eds) Proceedings of the 17th International Conference on New Trends in Fatigue and Fracture. NT2F 2017. Springer, Cham. https://doi.org/10.1007/978-3-319-70365-7_19
Download citation
DOI: https://doi.org/10.1007/978-3-319-70365-7_19
Published:
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-70364-0
Online ISBN: 978-3-319-70365-7
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)