Concrete Durability pp 109–137Cite as

The Effect of Nitrogen-Doped Mesoporous Carbon Spheres (NMCSs) on the Electrochemical Behavior of Carbon Steel in Simulated Concrete Pore Water

  • Chapter
  • First Online:

Abstract

The influence of highly nitrogen-doped mesoporous carbon spheres (NMCSs) (internal pore size of 5.4–16 nm) on the electrochemical response of low carbon steel (St37) in model alkaline solutions of pH 13.9 and 12.8 was studied, using Open Circuit Potential (OCP) monitoring, Electrochemical Impedance Spectroscopy (EIS) and Cyclic Voltammetry (CV). Prior to adding the NMCSs in the relevant solutions, they were characterized in the same model medium by measuring their Zeta-potential, hydrodynamic radius and particle size distribution, using dynamic light scattering (DLS) and transmission electron microscopy (TEM). In alkaline environment of pH 13.9 and 12.8, which simulates the concrete pore water of fresh and mature concrete, the DLS measurements indicated that the hydrodynamic radius of NMCSs particle varied from 296 nm to 183, respectively. According to the Zeta-potential measurements in the same solutions, the NMCSs were slightly positively charged.

The addition of 0.016 wt.% of NMCSs to the model medium induced certain variation in the electrochemical response of the tested steel. In alkaline solutions of pH 12.8, the presence of NMCSs in the passive film/solution interface induced a delay in the formation of a stable passive film. On the other hand, in solutions of pH 13.9, the higher corrosion activity on the steel surface, enhanced by high pH, was limited by adsorption of NMCSs on the film/substrate interface. In addition competing mechanisms of active state, i.e., enhanced oxidation on the one hand, and particles adsorption on anodic sites and oxidation limitation, on the other hand, was relevant in solution of pH 13.9 inducing larger fluctuations in impedance response and stabilization only towards the end of the testing period.

Except steel electrochemical response, the properties of the cement-based bulk matrix were investigated in the presence of the aforementioned additives. The mortar bulk matrix properties were highly affected by NMCSs. The lowest electrical resistivity values were recorded in mortar specimens with mixed-in 0.025 wt.% NMCSs (with respect to dry cement weight). Furthermore, the addition of 0.025 wt.% NMCSs increased the compressive strength when compared to control specimens. The presence of F127 as a dispersing agent for NMCSs was found to be not suitable for reinforced concrete applications, which is in view of the reduced mechanical strength and electrical resistivity of the cement-based bulk matrix. This is in addition to the adverse effect on the formation of electrochemically stable passive layer on steel surface in alkaline medium in its presence.

This is a preview of subscription content, log in via an institution.

Chapter
USD   29.95
Price excludes VAT (USA)
  • Available as PDF
  • Read on any device
  • Instant download
  • Own it forever
eBook
USD   79.99
Price excludes VAT (USA)
  • Available as EPUB and PDF
  • Read on any device
  • Instant download
  • Own it forever
Softcover Book
USD   99.99
Price excludes VAT (USA)
  • Compact, lightweight edition
  • Dispatched in 3 to 5 business days
  • Free shipping worldwide - see info
Hardcover Book
USD   139.99
Price excludes VAT (USA)
  • Durable hardcover edition
  • Dispatched in 3 to 5 business days
  • Free shipping worldwide - see info

Tax calculation will be finalised at checkout

Purchases are for personal use only

Learn about institutional subscriptions

References

  1. Bertolini L, Elsener B, Pedeferri P, Polder R (2004) Corrosion of steel in concrete: prevention, diagnosis, repair, 1st edn. Wiley, Weinheim, pp 71–121

    Google Scholar 

  2. American Concrete Institute (1985) Committee 222, corrosion of metals in concrete. ACI J 81:3–32

    Google Scholar 

  3. Broomfield JP (2007) Corrosion of steel in concrete: understanding, investigation and repair. Spons Architecture Price Book, London

    Google Scholar 

  4. Balaguru PN, Shah SP (1992) Fiber reinforced cement composite. McGraw-Hill Inc., New York

    Google Scholar 

  5. Kowald T (2004) Influence of surface modified carbon nanotubes on ultra-high performance concrete. In: Schmidt M, Fehling E (eds) Proceedings international symposium on ultra-performance concrete. Kassel University Press GmbH, pp 195–202

    Google Scholar 

  6. Angst U, Elsener B, Larsen KC, Vennesland Ø (2009) Critical chloride content in reinforced concrete – a review. Cem Concr Res 39:1122–1138

    Article  Google Scholar 

  7. Chernin L, Val DV (2011) Prediction of corrosion-induced cracking in reinforced concrete structures. Constr Build Mater 25:1854–1869

    Article  Google Scholar 

  8. Lui Y, Weyers RE (1998) Modelling the time to corrosion cracking in chloride contaminated reinforced concrete structures. ACI Mater J 95:675–681

    Google Scholar 

  9. Koleva DA, de Wit JHW, van Breugel K, Lodhi ZF, van Wesring E (2007) Investigation of corrosion and cathodic protection in reinforced concrete. J Electrochem Soc 154:52–61

    Article  Google Scholar 

  10. Mahmoud H, Alonso MC, Sanchez M (2012) Service life extension of concrete structures by increasing the chloride threshold using stainless steel reinforcements. In: Alexander MG et al (eds) Concrete repair, rehabilitation and retrofitting III. Taylor & Francis Group, London, pp 497–503

    Google Scholar 

  11. Pan Z, He L, Qiu L, Korayem AH, Li G, Zhu JW, Collins F, Li D, Duan WH, Wang MC (2015) Mechanical properties and microstructure of a graphene oxide-cement composite. Cem Concr Compos 58:140–147

    Article  Google Scholar 

  12. Collins F, Lambert J, Duan WH (2012) The influence of admixtures on the dispersion, workability, and strength of carbon nanotuble-OPC past mixtures. Cem Concr Compos 34:201–207

    Article  Google Scholar 

  13. Jo BW, Kim CH, Tea GH, Park JB (2007) Characteristics of cement mortar with nano-SiO2 particles. Constr Build Mater 21:1351–1355

    Article  Google Scholar 

  14. Refait P, Jeannin M, Sabot R, Antony H, Pineau S (2013) Electrochemical formation and transformation of corrosion products on carbon steel under cathodic protection in seawater. Corros Sci 71:32–36

    Article  Google Scholar 

  15. Carmona J, Garcés P, Climent MA (2015) Efficiency of a conductive cement-based anodic system for the application of cathodic protection, cathodic prevention and electrochemical chloride extraction to control corrosion in reinforced concrete structures. Corros Sci 96:102–111

    Article  Google Scholar 

  16. Duwell EJ, Todd JW, Butzke HC (1964) The mechanism of corrosion inhibition of steel by ethynylcyclohexanol in acid solution. Corros Sci 4:435–441

    Article  Google Scholar 

  17. Yang W, Li Q, Xiao Q, Liang J (2015) Improvement of corrosion protective performance of organic coating on low carbon steel by PEO pretreatment. Prog Org Coat 89:260–266

    Article  Google Scholar 

  18. EN 1990 (2002) Eurocode- basis of structural design. European Committee for Standardization, Brussels

    Google Scholar 

  19. Sanchez F, Sobolev K (2010) Nanotechnology in concrete- a review. Const Build Mater 24:2060–2071

    Article  Google Scholar 

  20. Tang J, Liu J, Li C, Li Y, Tade MO, Dai S, Yamauchi Y (2014) Synthesis of nitrogen-doped mesoporpous carbon spheres with extra-large pores through assembly of diblock copolymer micelles. Angew Chem Int Edn 53:588–593

    Google Scholar 

  21. Yang T, Liu J, Zhou R, Chen Z, Xu H, Qiao SH, Monterio M (2014) N-doped mesoporous carbon shperes as the oxygen reduction catalysts. J Mater Chem A 2:18139–18146

    Article  Google Scholar 

  22. Zhang LL, Gu Y, Zhao XS (2013) Advanced porous carbon electrodes for electrochemical capacitor. J Mater Chem A 1:9395–9408

    Article  Google Scholar 

  23. Parveen S, Rana S, Fangueiro R (2013) A review on nanomaterial dispersion, microstructure and mechanical properties of carbon nanotube and nanofiber reinforced cementitious composites. Nanomaterials 2013:1–19

    Article  Google Scholar 

  24. Yazdenbakhsh A, Grasley Z (2012) The theoretical maximum achievable dispersion of nanoinclusions in cement paste. Cem Concr Res 42:798–804

    Article  Google Scholar 

  25. Konsta-Gdoutos MS, Metaxa ZS, Shah SP (2010) Highly dispersed carbon nanotube reinforced cement based materials. Cem Concr Res 40:1052–1059

    Article  Google Scholar 

  26. Peng H, Alemany LB, Margrave JL, Khabashesku VN (2003) Sidewall carboxylic acid functionalization of single-walled carbon nanotubes. J Am Chem Soc 125:15174–15182

    Article  Google Scholar 

  27. Xin X, Xu G, Zhao T (2008) Dispersing carbon nanotubes in aqueous solutions by a starlike block copolymer. J Phys Chem C 112:16377–16384

    Article  Google Scholar 

  28. Bystrzejewski M, Huczko A, Lange H, Gemming T, Büchner B, Rümmeli MH (2010) Dispersion and diameter separation of multi-wall carbon nanotubes in aqueous solutions. J Colloid Interface Sci 345:138–142

    Article  Google Scholar 

  29. Liao YH, Marietta-Tondin O, Liang Z, Zhang C, Wang B (2004) Investigation of the dispersion process of SWNTs/SC-15 epoxy resin nanocomposites. Mater Sci Eng A 385:175–181

    Article  Google Scholar 

  30. Li J, Li Z, Tong J, Xiaa C, Li F (2015) Nitrogen-doped ordered mesoporous carbon sphere with short channel as an efficient metal-free catalyst for oxygen reduction reaction. RSC Adv 5:70010–70016

    Article  Google Scholar 

  31. Susanto A, Koleva DA, Copuroglu O, van Beek K, van Breugel K (2013) Mechanical, electrical, and microstructural properties of cement-based materials in condition of stray current flow. J Adv Concr Technol 11:119–134

    Article  Google Scholar 

  32. Stern M, Geary AL (1957) A theoretical analysis of the shape of polarization resistance curves. J Electrochem Soc 104:56–63

    Article  Google Scholar 

  33. Andrade C, Alonso C (1996) Corrosion rate monitoring in the laboratory and on-site. Constr Build Mater 10:315–328

    Article  Google Scholar 

  34. Zornoza E, Paya J, Garces P (2008) Chloride-induced corrosion of steel embedded in mortars containing fly ash and spent cracking catalyst. Corros Sci 50:1567–1575

    Article  Google Scholar 

  35. Basak R, Bandynopadhyay R (2013) Encapsulation of hydrophobic drugs in pluronic F127 micelles: effect of drug hydrophobicity, solution temperature, and pH. Langmuir 29:4350–4356

    Article  Google Scholar 

  36. Eliseeva OV, Besseling NAM, Koopal LK, Cohen Stuart MA (2005) Influence of NaCl on the behavior of PEO-PPO-PEO triblock copolymers in solutions, at interface, and in asymmetric liquid films. Langmuir 21:4954–4963

    Article  Google Scholar 

  37. Eliseeva OV, Fokkink RG, Besseling NAM, Koopal LK, Cohen Sturat MA (2006) Thinning of wetting films formed from aqueous solutions of non-ionic surfactant. J Colloid Interface Sci 301:210–216

    Article  Google Scholar 

  38. Nita LE, Chiriac AP, Bercea M (2012) Effect of pH and temperatura upon self-assembling process between ploy(aspartic acid) and pluronic F127. Colloid Surf B Biointer 119:6539–6545

    Google Scholar 

  39. Alexander S, de Vos WM, Castle TC, Cosgrove T, Prescott SW (2014) Growth and shrinkage of pluronic micelles by uptake and release of flurbiporfen: variation of pH. Langmuir 28:47–57

    Google Scholar 

  40. Gong K, Du F, Xia ZH, Durstock M, Dai LM (2009) Nitrogen-doped carbon nanotube arrays with high Electrocatalytic activity for oxygen reduction. Science 323:760–764

    Article  Google Scholar 

  41. Deng DH, Pan XL, Yu LA, Cui Y, Jiang YP, Qi J, Li WX, Fu QA, Ma XC, Xue QK, Sun GQ, Bao XH (2011) Toward N-doped graphene via solvothermal synthesis. Chem Mater 23:1188–1193

    Article  Google Scholar 

  42. Wan K, Yu ZP, Li XH, Liu MY, Yang G, Piao JH, Liang ZX (2015) pH effect on electrochemistry of nitrogen-doped carbon catalyst for oxygen reduction reaction. Catalysis 5:4325–4432

    Google Scholar 

  43. Koleva DA, Denkova AG, Boshkov N, van Breguel K (2013) Electrochemical performance of steel in cement extract and bulk matric properties of cement past in presence of pluronic 123 micelles. J Mater Sci 48:2490–2503

    Article  Google Scholar 

  44. Hu J, Koleva DA, de Wit JHW, Kolev H, van Breugel K (2011) Corrosion performance of carbon steel in simulated pore solutions in presence of micelles. J Electrochem Soc 158:C76–C87

    Article  Google Scholar 

  45. Diaz B, Joiret S, Keddam M, Novoa XR, Perez MC, Takenouti H (2004) Passivity of iron in mud’s water solution. Electrochim Acta 49:3039–3048

    Article  Google Scholar 

  46. Joiret S, Keddam M, Novoa XR, Perez MC, Rangel C, Takenouti H (2002) Use of EIS, ring-disk electrode, EQCM and Raman spectroscopy to study the film of oxides formed on iron in 1M NaOH. Cement Concr Comp 24:7–15

    Article  Google Scholar 

  47. Freire L, Nóvoa XR, Montemor MF, Carmezim MJ (2009) Study of passive films formed on mild steel in alkaline media by the application of anodic potentials. Mater Chem Phys 114:962–972

    Article  Google Scholar 

  48. Alonso C, Andrade C, Izquierdo M, Novoa XR, Perez MC (1998) Effect of protective oxide scales in macrogalvanic behavior of concrete reinforcement. Corros Sci 40:1379–1389

    Article  Google Scholar 

  49. Antony H, Legrand L, Marechal L, Perrin S, Dillmann P, Chausse A (2005) Study of lepidorcrocite γ-FeOOH electrochemical reduction in natural and slightly alkaline solutions at 25 °C. Electrochem Acta 51:745–753

    Article  Google Scholar 

  50. Freire L, Carmezima MJ, Ferreiraa MGS, Montemora MF (2010) The passive behaviour of AISI 316 in alkaline media and the effect of pH: a combined electrochemical and analytical study. Electrochim Acta 55:6174–6181

    Article  Google Scholar 

  51. Koleva DA, Boshkov N, van Breugel K, de Wit JHW (2011) Steel corrosion resistance in model solutions, containing waste materials. Electrochim Acta 58:628–646

    Article  Google Scholar 

  52. Andrade C, Merino P, Nóvoa XR, Pérez MC, Soler L (1995) Passivation of reinforcing steel in concrete. Mater Sci Forum 192-194:891–898

    Article  Google Scholar 

  53. Mahmoud H, Sanchez M, Alonso MC (2015) Ageing of the spontaneous passive state of 2304 duplex stainless steels in high-alkaline conditions with the presence of chloride. J Solid State Electrochem 19:2961–2972

    Article  Google Scholar 

  54. Andrade C, Keddam M, Novoa XR, Perez MC, Rangel CM, Takenouti H (2001) Electrochemical behavior of steel rebars in concrete: influence of environmental factors and cement chemistry. Electrochim Acta 46:3905–3912

    Article  Google Scholar 

  55. Abreu CM, Covelo A, Daiz B, Freire L, Novoa XR, Perez MC (2007) Electrochemical behavior of iron in chlorinated alkaline media; the effect of slurries form granite processing. J Braz Chem Soc 18:1156–1163

    Article  Google Scholar 

  56. Flis J, Oranowska H, Smialowska ZS (1990) An ellipsometric study of surface films grown on iron and iron carbon alloys in 0.05 M KOH. Corros Sci 30:1085–1099

    Article  Google Scholar 

  57. Li WS, Luo JL (1999) Electronic properties and pitting susceptibility of passive films on ferrite and pearlite in chloride-containing solution. Proc Electrochem Soc 27:161–170

    Google Scholar 

  58. Macdonald DD (1992) The point defect model for passive state. J Electrochem Soc 139:3434–3449

    Article  Google Scholar 

  59. Castro EB (1994) Analysis of the impedance response of passive iron. Electrochim Acta 39:2117–2123

    Article  Google Scholar 

  60. Liu L, Xu J, Xie ZH, Munroe P (2013) The roles of passive layers in regulating the electrochemical behaviour of Ti5Si3-based nanocomposite films. J Mater Chem A 1:2064–2078

    Article  Google Scholar 

  61. Xia Y, Cao F, Liu W, Chang L, Zhang H (2013) The formation of passive films of carbon steels in borate buffer and their degradation behavior in NaCl solution by SECM. Int J Electrochem Sci 8:3057–3073

    Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Faculty of Civil Engineering and Geosciences, Delft University of Technology, Section of Materials and Environment, Stevinweg 1, 2628 CN, Delft, The Netherlands

    H. Mahmoud & Dessi A. Koleva

  2. National Institute for Materials Science (NIMS), 1-1 Namiki, Tsukuba, Ibaraki, 305-0044, Japan

    J. Tang & Y. Yamauchi

  3. Faculty of Science and Engineering, Department of Chemical & Petroleum Engineering, Curtin University of Technology, U1987, Perth, WA, Australia

    J. Liu & M. Tade

Authors
  1. H. Mahmoud
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. J. Tang
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Dessi A. Koleva
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. J. Liu
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Y. Yamauchi
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. M. Tade
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to H. Mahmoud .

Editor information

Editors and Affiliations

  1. Universidad Internacional (UNINTER), Cuernavaca, Morelos, Mexico

    Luis Emilio Rendon Diaz Miron

  2. Faculty of Civil Engineering and Geosciences, Section Materials and Environment, Delft University of Technology, Delft, Zuid-Holland, The Netherlands

    Dessi A. Koleva

Rights and permissions

Reprints and permissions

Copyright information

© 2017 Springer International Publishing AG

About this chapter

Cite this chapter

Mahmoud, H., Tang, J., Koleva, D.A., Liu, J., Yamauchi, Y., Tade, M. (2017). The Effect of Nitrogen-Doped Mesoporous Carbon Spheres (NMCSs) on the Electrochemical Behavior of Carbon Steel in Simulated Concrete Pore Water. In: Rendon Diaz Miron, L., Koleva, D. (eds) Concrete Durability. Springer, Cham. https://doi.org/10.1007/978-3-319-55463-1_6

Download citation

Publish with us

Policies and ethics

Search

Navigation