This paper introduces the effects of Mo content on microstructure and mechanical property of PH13-8Mo martensitic precipitation-hardened stainless steel which is used for LP last stage blade in steam turbine. Thermodynamic software Thermo-Calc has been used to calculate precipitation temperature and the mass fraction of precipitated phases in PH13-8Mo steel with different Mo content. The result shows that when the mass of Mo is below 0.6wt.%, chi-phase mu-phase and sigma-phase could disappear. The microstructure and mechanical property of high Mo PH13-8Mo (Mo=0.57wt.%) and low Mo PH13-8Mo (Mo=2.15wt.%)have been investigated in different heat treatments. The investigations reveal that austenitizing temperature decrease with the reduce of Mo content, so the optimum solution temperature for low Mo PH13-8Mo is lower than that for high Mo PH13-8Mo.The influence of solution temperature on grain size is weakened with the increase of Mo content, Mo rich carbides could retard coarsening of grain. An enormous amount of nano-size uniformly distributed β-NiAl particles are found in both kinds of steels using transmission electron microscopy, they are the most important strengthening phase in PH13-8Mo.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Preview
Unable to display preview. Download preview PDF.
Reference
D.H.Ping, et al.“Microstructural evolution in 13Cr-8Ni-2.5Mo-2Al martensitic precipitation-hardened stainless steel”, Materials Science and Engineering A, 394(2005), 285–295
V.SEETHARAMAN, M.SUNDARARAMA, R KRISHNAN. “Precipitation Hardening in a PH 13–8 Mo stainless steel”, Materials Science and Engineering, 47(1981):1–11
Z.GUO et al. “Improving Toughness of PH13-8 Stainless Steel through Intercritical Annealing”, ISIJ International, 43 (2003):1622–1629
W.Xu, D.San Martin etal. Materials Science and Engineering A, 467(2007):24–32
Author information
Authors and Affiliations
Rights and permissions
Copyright information
© 2014 TMS
About this paper
Cite this paper
Yubing, P., Tianjian, W., Zhenhuan, G., Hua, F., Gongxian, Y. (2014). Effects of Mo Content on Microstructure and Mechanical Property of PH13-8Mo Martensitic Precipitation-Hardened Stainless Steel. In: Energy Materials 2014. Springer, Cham. https://doi.org/10.1007/978-3-319-48765-6_36
Download citation
DOI: https://doi.org/10.1007/978-3-319-48765-6_36
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-48598-0
Online ISBN: 978-3-319-48765-6
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)