High calcium/aluminum ratio (C/A=12:7) is one of the main problems which inhibit the development of lime sinter process. Decrease the C/A of clinker is studied in this paper. 12CaO•7Al2O3 (C12A7) and CaO•Al2O3 (CA) were synthesized at 1350 °C by analytical pure reagents. The phase composition of sinters was analyzed by XRD and the alumina leaching experiments were carried out. The results show that the optimal alumina leaching ratio of C12A7 and CA are 93.40% and 73.18%. The leaching experiments of the mixture of C12A7 and CA with different proportions were carried out. The alumina leaching ratio of the mixture reaches 91.12% when the content of C12A7 is 40% (in mass). Above this proportion, the alumina leaching ratio increases little. The results show that the existence of C12A7 can promote the leaching property of CA.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Preview
Unable to display preview. Download preview PDF.
Similar content being viewed by others
References
P. Smith, “The processing of high silica bauxites-review of existing and potential processes,” Hydrometallurgy, 98(1)(2009), 162–176.
R. Paramguru, P. Rath, V. Misra, “Trends in red mud utilization-A review,” Mineral Processing & Extractive Metall Rev, 26(1)(2004), 1–29.
J. Grzymek, et al. The new way of alumina lixiviation from sinters containing 12CaO.7 Al2O3 in J. Grzymek’s Method [M]. Light Metals 1988: 129–133.
W. Bo, et al., “Effect of material ratio on leaching and self-disintegrating property of calcium aluminate slag,” Journal of Northeastern University: Natural Science, 29(11)(2008), 1593–1596.
Eva Selic, Jan-Dirk Herbell. “Utilization of Fly Ash from Coal-fired Power Plants in China,” Journal of Zhejiang University(Science A), 9(5)(2008): 681–687.
T. Zhi-fang, B. Shi-wen, Y. Hai-yan, “Leaching kinetics of non-constant temperature process of calcium aluminate slag under microwave radiation,” The Chinese Journal of Nonferrous Metals, 16(2)(2006), 357–362.
X. Wei, et al., “Study on the process of extracting alumina from the middling grade bauxite using lime sinter,” Journal of Guizhou University of Technology(Natural Science Edition), 05)(2008), 41–43.
L. Zhi-ying, et al., “Research on the intensified sintering mechanism of middle-grade bauxite and its digestion performances,” Light Metals, 12)(2009), 14–17.
Z. Wu. “Phase composition and leaching law of the sinter of CaO-Al2O3-SiO2 system”. Shenyang; Northeastern University, 2011.
B. M. Mohamed, J. H. Sharp. Kinetics and mechanism of formation of monocalcium aluminate, CaAl2O4. Journal of material chemistry, 7(8)(1997), 1595–1599.
Z. Bai-yong, Z. Feng-lu, “The limestone sintering process to produce alumina with fly ash”. Light Metals, (6)2007, 17–19.
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2015 TMS (The Minerals, Metals & Materials Society)
About this chapter
Cite this chapter
Bo, W., Jiajia, L., Huilan, S., Yubing, Z., Dongdong, L. (2015). Synergistic Effect of C12A7 and CA on Alumina Leaching Property Under Low Calcium/Aluminum Ratio. In: Hyland, M. (eds) Light Metals 2015. Springer, Cham. https://doi.org/10.1007/978-3-319-48248-4_11
Download citation
DOI: https://doi.org/10.1007/978-3-319-48248-4_11
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-48610-9
Online ISBN: 978-3-319-48248-4
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)