Abstract
Industrial waste has been considered as an option in the initiative to promote green and sustainable construction. Oil palm shell (OPS) is one of the industrial wastes produced from the processing of palm oil and its ability to be used as a lightweight aggregate in concrete mixes has been tested. OPS has a high porosity content, which means that it is a good heat insulation material in concrete. This study focuses on the OPS volume fraction in concrete and its effects on the thermal insulation concrete. The volume fractions used are 30, 32, 34, 36, and 38 % from concrete density. Density decreases with the increase of volume fraction. The highest reduction from air dry to oven density is 13 %, which is obtained from a volume fraction of 34 % OPS. The volume fraction affected compressive strength and thermal conductivity. All mixes achieved for the requirement for load-bearing strength based on compressive strength were obtained. The highest strength was 22 Mpa by volume fraction, 30 % used. Volume fractions used are within the range of the semi-structure which has the same capacity as thermal insulation materials, below 0.75 W/m K (according to RILEM requirements) except for the volume fraction, 30 %. The thermal properties increased according to the increase in density except for the specific heat result, and they have a strong relationship within the thermal conductivity and compressive strength results. Thus the OPS lightweight concrete (OPSLC) capacity as a heat insulation material is proven and it can reduce energy use in buildings.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Abbreviations
- k :
-
Thermal conductivity, W/m K
- fcu:
-
Compressive strength, Mpa
- OPS:
-
Oil palm shell
- OPSLC:
-
Oil palm shell lightweight concrete
- UPV:
-
Ultrasonic pulse velocity
- Sp:
-
Superplasticizer
- SSD:
-
Saturated dry density
References
Abullah N, Sulaiman F, Gerhouser H, Shariff A (2011) An outlook of Malaysian energy, oil palm industry and its utilization of waste as useful resources. Biomass Bioenergy 35:3775–3786
Pankhurst RNW (1993) Construction. In: Clarke JL (ed) Structural lightweight aggregate concrete. Chapman & Hall, London; chapter 4
Shafigh P, Zamin Jumaat M, Mahmud H, Johnsom Alengaram U (2011) A new method of producing high strength oil palm shell lightweight concrete. Mater Des 32:4839–4843
Husain Z, Zainac Z, Abdullah Z (2002) Briqutting of palm fibre and shell from the processing of palm nuts to palm oil. Biomass Bioenergy 22:505–509
Sahu JN, Abnisa F, Daud WMA, Husin WMW (2011) Utilization possibilities of palm shell as a source of biomass energy in Malaysia by producing bio-oil in pyrolysis process. Biomass Bioenergy 35:1863–1872
Johnson Alengaram U, Al Muhhit BA, bin Jumaat MZ (2013) Utilization of oil palm kernel as lightweight aggregate in concrete—a review. Construct Build Mater 38:161–172
Teo DCL, Mannan MA, Kurian VJ (2006) Structural concrete using oil palm shell (OPS) as lightweight aggregate. Turk J Eng Environ Sci 30:251–257
Okpala DC (1990) Palm kernel shell as lightweight aggregate in concrete. Build Environ 25:291–296
Demirboˇga R, Gul R (2003) Thermal conductivity and compressive strength of expanded perlite aggregate concrete with mineral admixtures. Energy Build 35:1155–1159
Al-sibahy A, Edward R (2012) Mechanical and thermal properties of novel lightweight concrete mixtures containing recycled glass and metakaolin. Construct Build Mater 31:157–167
Lee HK, Kim HK, Jeon JH (2012) Workability and mechanical, acoustic and thermal properties of lightweight aggregate concrete with volume of entrained air. Construct Build Mater 29:193–200
Narayanan N, Ramamurthy K (2000) Structure and properties of aerated concrete: a review. Cem Concr Compos 22:321–329
Bouguerra A, Laurent JP, Goual MS, Queneudec M (1997) The measurement of the thermal conductivity of solid aggregate using the transient plane source technique. J Phys D Appl Phys 30:2900–2904
ASTM 332-99. Standard specification for lightweight aggregates for insulating concrete. ASTM, West Conshohocken
Solis-Carcano R, Moreno EI (2008) Evaluation of concrete made with crushed lime stone aggregate based on ultrasonic pulse velocity. Construct Build Mater 30:1225–1231
Serri E, Zailan Suleiman M, Md Azree OM (2014) The effect of oil palm shell aggregate shape on the thermal properties and density of concrete. Adv Mater Res 935:172–175
Serri E, Zailan Suleiman M, Md Azree OM (2014) Thermal properties of oil palm shell lightweight concrete with different mix design. Jurnal Teknologi 70(1):155–159
Demirboğa R, Gül R (2013) The effects of expanded perlite aggregate, silica fume and fly ash on the thermal conductivity of lightweight concrete. Cem Concr Res 33:723–727
Acknowledgment
The author would like to thank the Universiti Sains Malaysia for awarding the Research University grant (1001/PPBGN/814213) to carry out the present research.
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2015 Springer International Publishing Switzerland
About this chapter
Cite this chapter
Serri, E., Suleman, M.Z., Othuman, M.A. (2015). The Effects of Oil Palm Shell Volume Fractions on Thermal Conductivity for Insulation Concrete. In: Dincer, I., Colpan, C., Kizilkan, O., Ezan, M. (eds) Progress in Clean Energy, Volume 1. Springer, Cham. https://doi.org/10.1007/978-3-319-16709-1_30
Download citation
DOI: https://doi.org/10.1007/978-3-319-16709-1_30
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-16708-4
Online ISBN: 978-3-319-16709-1
eBook Packages: EnergyEnergy (R0)