Abstract
In the PbO rich part of the System PbO — SiO2 — GeO2 the equilibrium phase diagram of the section Pb3SiO5. — Pb3GeO5 was found to be partially binary and partially ternary, with extended solid solutions of all phases observed.Over a wide composition range glasses can be quenched, which show rather complicated devitrification effects.All the various crystalline phases obtained during DTA up to 600 C turned out to be metastable.
This is a preview of subscription content, log in via an institution to check access.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Preview
Unable to display preview. Download preview PDF.
References
W. Eysel, Proc.Third ICTA, Davos 1971, Vol.II, p.179–192
R. M. Smart and F. P. Glasser, J.Amer.Ceram.Soc. 57, 378–382 (1974)
M. Mydlar, H. Nowotny and K.J. Seifert, Mh.Chem. 100, 191–202 (1969)
H.H. Otto, Z. Kristallogr. 149, 227–240(1979)
T. Furukawa, Mater.Res.Lab.Pennsylvania State University Diss.Abstr.Int.B 1978, 38(12, Pt.1), 6091–2.
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 1980 Springer Basel AG
About this chapter
Cite this chapter
Breuer, KH., Eysel, W. (1980). DTA-Investigations in the System PbO — SiO2 — GeO2 . In: Hemminger, W. (eds) Thermal Analysis. Birkhäuser, Basel. https://doi.org/10.1007/978-3-0348-6736-8_41
Download citation
DOI: https://doi.org/10.1007/978-3-0348-6736-8_41
Publisher Name: Birkhäuser, Basel
Print ISBN: 978-3-0348-6737-5
Online ISBN: 978-3-0348-6736-8
eBook Packages: Springer Book Archive