Abstract
In this study, changes in mechanical properties and hot tearing properties were investigated by adding 0.2 wt% Ni and 2 wt% Cu to Al–Si–Mg alloy . In addition, the porosity formation with regard to liquid metal cleanliness was investigated. Casting experiments have been carried out in certain compositions. The melt was degassed and up-gassed slowly. Micro100 alloy was added to the melt to investigate the effect of the distribution of porosity on the mechanical properties . A ring permanent mould was used to test the hot tearing characteristic and a tensile test bars were poured into permanent mould to test the mechanical properties.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
References
Di Giovanni MT (2014)The Influence of Nİ and V trace elements on the high temperature tensile properties of A356 aluminum foundry. Norwegian University of Science and Technology
Casari D, Ludwig TH, Merlin M (2014) The effect of Ni and V trace elements on the mechanical properties of A356 aluminum foundry alloy in as-cast and T6 heat treated conditions. Mater Sci Eng A 610:414–426
Campbell J, Harding RA (1994) Solidification defects in casting. TALAT, European Aluminum Association
Dispinar D, Campbell J (2004) Critical assessment of reduced pressure test. Part 1: porosity phenomena. The University of Birmingham
Dispinar D, Campbell J (2011) Porosity, hydrogen and bifilm content in Al alloy casting. Mat Sci Eng A 528:3860–3865
Akhtar S, Arnberg L, Di Sabatino M, Dispinar D, Syvertsen M (2008) A comparative study of porosity and pore morphology in a directionally solidified A356 alloy. Int J Metalcasting. Winter 09
BEST Collection 08 (2018) Oberflächenbehandlung-2018, BEST Collection 21; DIN komplett-2018
Ludwig T, Dispinar D, Di Sabatino M, Arnberg L (2012) Influence of oxide additions on the porosity development and mechanical properties of A356 aluminium alloy castings. Int J Metalcasting 6(2):41–50
Dispinar D, Akhtar S, Nordmark A, Syvertsen F, Di Sabatino M, Arnberg L (2012) Tensile properties, porosity and melt quality relation of A356. Suppl Proc 2:201–208
Acknowledgements
I am very grateful to Dr.-Ing. Uwe Vroomen for giving me the opportunity and great support to this study.
I would like to thank Johannes Brachmann for guidance and support through the course of my thesis, and for his excellent supervision during the entirety of this study.
I would like to express my gratitude to Associate Professor Dr. Derya Dispinar for his scientific opportunities, and for his enthusiastic support and advice.
Author information
Authors and Affiliations
Corresponding authors
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2019 The Minerals, Metals & Materials Society
About this paper
Cite this paper
Yildirim, K., Brachmann, J., Dispinar, D., Bührig-Polaczek, A., Vroomen, U. (2019). Effect of Copper and Nickel Addition on Mechanical Properties of A356 Alloy and Assessment of Mechanism of Pore Formation. In: Tiryakioğlu, M., Griffiths, W., Jolly, M. (eds) Shape Casting. The Minerals, Metals & Materials Series. Springer, Cham. https://doi.org/10.1007/978-3-030-06034-3_32
Download citation
DOI: https://doi.org/10.1007/978-3-030-06034-3_32
Published:
Publisher Name: Springer, Cham
Print ISBN: 978-3-030-06033-6
Online ISBN: 978-3-030-06034-3
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)