Abstract
The influence of Cr2O3 and basicity on the viscosity of CaO–SiO2-15 wt% Al2O3-9 wt% MgO-22 wt% TiO2–Cr2O3 slag was investigated in the temperature range of 1673–1773 K. The viscosity decreased with increasing basicity at fixed content of Cr2O3 due to the depolymerization of silicon structure. At a fixed content of basicity , the viscosity decreased with increasing Cr2O3 when the mass percentage of Cr2O3 was below 1%. Different models were also used to predict the effect of Cr2O3 on the viscosity of blast furnace slag, and the results show that the optical basicity model agrees well with the experimental values. With the initial addition of Cr2O3 content, the slag melting temperature increased from 1660 to 1673 K. When the basicity increased from 1.0 to 1.2, the slag melting temperature increased from 1655 to 1720 K.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
References
Yang Y (2014) Northeastern University
Deng J, Xue X, Liu G (2007) J Mater Metall 6:83–86
Peng B, Wu G, Dai B, Zhang P, Zhang L (2012) Metal materials and metallurgical engineering, pp 18–21
Zhang YZ, Yan MS, Xiang L, Yin JC, Tao W (2005) J Mater Metall 253–255
Sunahara K, Nakano K, Hoshi M, Inada T, Komatsu S, Yamamoto T (2008) ISIJ Int 48:420–429
Banya S (1988) Iron and steel institute of Japan, Tokyo, vol 4
Fang L, Guofan Z (2006) Henan Metall 14:11–13
Park JH, Min DJ, SH S (2004) Metall Mater Trans B 35:269–275
Ohno A,. Ross HU (1963) Canadian metallurgical quarterly, pp 259–279(221)
Saito N, Hori N, Nakashima K, Mori K (2003) Metall Mater Trans B 34:509–516
Xu RZ, Zhang JL, Wang ZY, Jiao KX (2017) Steel Res Int 88
Qiu G, Chen L, Zhu J, Lv X, Bai C (2015) Trans Iron Steel Inst Jpn 55:1367–1376
Acknowledgements
The work described in this paper was supported by a grant from the Natural Science Foundation of China (Project no. 51674055).
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2019 The Minerals, Metals & Materials Society
About this paper
Cite this paper
Qiu, G., Wang, J., Liu, S., Li, Q. (2019). Influence of Cr2O3 and Basicity on Viscosity of Ti-Bearing Blast Furnace Slag. In: Li, B., et al. Characterization of Minerals, Metals, and Materials 2019. The Minerals, Metals & Materials Series. Springer, Cham. https://doi.org/10.1007/978-3-030-05749-7_36
Download citation
DOI: https://doi.org/10.1007/978-3-030-05749-7_36
Published:
Publisher Name: Springer, Cham
Print ISBN: 978-3-030-05748-0
Online ISBN: 978-3-030-05749-7
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)