Asphaltenes pp 177-189 | Cite as

Asphalt Emulsion for Environmental Coating and Encapsulation

  • Hsienjen Lian
  • Teh Fu Yen


In this new era, people are more concerned about their living environment. Environmental problems become a global issue in this world, and many of the environmental problems come from material corrosion such as underground storage tank corrosion, buried pipe line corrosion, etc., which can cause soil and groundwater contamination. Such contaminations directly threaten human health and human life when the underground water is contaminated or when the seepage of volatile organic compounds from underground contaminated soil becomes explosive.


Emulsion Polymerization Toxicity Characteristic Leach Procedure Hydroxyl Free Radical Asphaltene Content Environmental Coating 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.


Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.


  1. 1.
    Uhlig, H.H.; and Revie, R.W., 1985. Corrosion and Corrosion Control: An Introduction to Corrosion Science and Engineering, Third Edition, John Wiley and Sons, Inc., 1–5.Google Scholar
  2. 2.
    Bennett L.H., 1978. Economic Effects of Metallic Corrosion in the United States, A Report to the Congress by the National Bureau of Standards, NBS Spec. Publ. 511:1, Washington, D.C.Google Scholar
  3. 3.
    ASTM D8, 1989. Standards on Petroleum Products and Lubricants, American Society for Testing and Materials, Philadelphia, Pa.Google Scholar
  4. 4.
    Lian, H.J., Lin, J.R., and Yen, T.F., 1994. Peptization studies of asphaltene and solubility parameter spectra, FUEL, 73, 423–428.CrossRefGoogle Scholar
  5. 5.
    Yen, T.F., 1988, Asphaltic Materials. Encyclopedia of Polymer Science and Engineering, I-10, Wiley and Sons, New York.Google Scholar
  6. 6.
    Iatroscan Lab. Inc., 1982. Iatroscan TH-10 Instrument Application:Optimising Reproducibility with the Iatroscan TLC/FID analysis, ANCAL 5.Google Scholar
  7. 7.
    The Asphalt Institute, 1992. A Basic Asphalt Emulsion Manual:Manual Aeries No. 19, 2nd Edition, College Park, MD.Google Scholar
  8. 8.
    Haber, F.; and Weiss, J., 1932. Naturwissenschaften 20: 948.CrossRefGoogle Scholar
  9. 9.
    Medalia, A.I.; and Kolthoff, I.M., 1949. The reaction between hydrogen peroxide and ferrous iron, J. Polymer Sci. 4: 377.CrossRefGoogle Scholar
  10. 10.
    Weiss, J., 1952. The Reaction between Hydrogen Peroxide and Ferrous Iron, in Advances in Catalysis, Academic Press, New York, 4: 343.Google Scholar
  11. 11.
    Baxendale, J.H., 1954. The reaction between hydrogen peroxide and ferrous iron, ibid., 31.Google Scholar
  12. 12.
    Masterton, W.L.; Slowinski, E.J.; and Stanitski, C.L., 1986. Chemical Principles: CBS College Publishing, 356.Google Scholar
  13. 13.
    Lin, J.R., 1992. Dissertation:Asphalt Waste Minimization, chapter 5. Department of Civil and Environmental Engineering, University of Southern California, Los Angeles.Google Scholar
  14. 14.
    California Code of Regulations, 1993. Title 22. Social Security: Division 4. Environmental Health, vol. 29A, published by Barclays Law Publishers, S. San Francisco.Google Scholar
  15. 15.
    Roadway International Corp., 1976. Coating Composition for Protecting Metal against Corrosion, Neth. Appl. NL 7605185, 10 pp.Google Scholar
  16. 16.
    Sekiyu, K.K., 1985. Two-Component Coating Compositions, shell, Jpn. KoKai Tokkyo Koho JP 60008373 A2, 5 pp.Google Scholar
  17. 17.
    Masaru, M., 1985. Asphalt Coating Compositions, Jpn. Kokai Toyyko Koho JP 60133067 A2, 2 pp.Google Scholar
  18. 18.
    Roediger,J.C.; Tompkins, E.E; and Schoenbam, G.H.,1969. Undercoating Automobiles with an Asphalt Emulsion, U.S. US 3427172, 3 pp.Google Scholar
  19. 19.
    Ladislav, N., 1978. Anticorrosion Paint, Czech. CS 171859, 2 pp.Google Scholar
  20. 20.
    Fumiaki, F.; Tasuku, S.; Kohei, K.; Hiroshi, A.; and Arata, 0., 1976. Solidification of Sludges Containing Heavy Metals and Arsenic, Nichireki Chemical Industry Co., Japan, Japan Kokai JP 51069483 15.Google Scholar
  21. 21.
    Tsunco, M., 1979. Fixation Treatment of Electrostatically Collected Dust from an Incineration Plant, JP 54057468,Showa 3.Google Scholar
  22. 22.
    Tomizo, O.; Katsumi, F.; Noriyuki, S.; and Nobuaki, S., 1980. Reduction Treatment of Chromium (VI) Discharged from Chromium Slag, Hokkaidoritsu Kogyo Shikenjo Hokoku 279: 155–163.Google Scholar
  23. 23.
    Akira, I.; Mitsuhiko, N.; and Hideo, K., 1985. Solidification of detergent-containing radioactive waste solution, Jpn. Tokkyo Koho JP 60046680, B4, Showa, 5.Google Scholar
  24. 24.
    Conner, J.R., 1986. Method for rendering hazardous wastes less permeable and more resistant to leaching, Chem-Technics Inc.. USA, U.S. US 4623469 A 7.Google Scholar

Copyright information

© Springer Science+Business Media New York 1995

Authors and Affiliations

  • Hsienjen Lian
    • 1
  • Teh Fu Yen
    • 1
  1. 1.Department of Civil EngineeringUniversity of Southern CaliforniaLos AngelesUSA

Personalised recommendations