Abstract

Portland cement is produced by intergrinding cement clinker with ca. 5% gypsum to a high surface area. The cement clinker is composed of various calcium minerals, e.g. calcium silicates, aluminates, ferrites, etc. with the principal minerals being tricalcium silicate, Ca3SiO5, dicalcium silicate, β-Ca2SiO4, tricalcium aluminate, Ca3Al2O6, and a calcium alumino-ferrite solid solution, having a composition between Ca4Fe4O10 and Ca4FeAl3O10.

Keywords

Portland Cement Calcium Silicate Cementitious Hydrate Calcium Silicate Hydrate Cement Clinker 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    R. Turriziani and G. Schippa, Ricerca Sci. 26 (1956), 2792.Google Scholar
  2. 2.
    E. T. Carlson and H. A. Berman, J. Research NBS 64A (1960), 333.CrossRefGoogle Scholar
  3. 3.
    W. Dosch, H. Keller and H. zur Strassen, Chemistry of Cement, Vol.11, 72 Proc. Vth Int. Symp., Tokyo, 1968.Google Scholar
  4. 4.
    G. Schippa, Ricerca Sci. 28 (1957), 2120.Google Scholar
  5. 5.
    J. Farran, Rev. Materiaux Construct, et Trav, Publ., C, 490, 155; 492, 191 (1956).Google Scholar
  6. 6.
    S. Brunauer, J. Skalny, I. Odler add M. Yudenfreund, Cement Concrete Res. 3 (1973), 279.CrossRefGoogle Scholar
  7. 7.
    H. F. W. Taylor (Editor), The Chemistry of Cements, Academic Press, London & New York, 1964.Google Scholar
  8. 8.
    H. G. Midgley and D. Rosaman, Chemistry of Cement, Vol. 1, 205, Proc. IVth Int. Symp., Washington, 1960.Google Scholar
  9. 9.
    A. E. Moore and H. F. W. Taylor, Acta Cryst. B26 (1970), 386.CrossRefGoogle Scholar
  10. 10.
    G. Snitzer and E. H. Bailey, Amer. 38 (1953), 629.Google Scholar
  11. 11.
    L. Heller and H. F. W. Taylor, J. Chem. Soc. (1952), 1018, 2535.CrossRefGoogle Scholar
  12. 12.
    S. Brunauer, L. E. Copeland and R. H. Bragg, J.Phys.Chem. 60 (1956), 112.CrossRefGoogle Scholar
  13. 13.
    D. L. Kantro, S. Bruanuer, C. H. Weise, J. Colloid Science 14 (1959), 363.CrossRefGoogle Scholar
  14. 14.
    H. F. W. Taylor, Chemistry of Cement, Vol.11, 1, Proc. Vth Int. Symp., Tokyo, 1968.Google Scholar
  15. 15.
    N. G. Dave and S. K. Chopra, J. Amer. Ceram. Soc. 49 (1966), 575.CrossRefGoogle Scholar
  16. 16.
    R. Sh. Mikhail, S. Bruanuer and L. E. Copeland, J. Colloid Interface Sci. 21 (1966), 394.CrossRefGoogle Scholar
  17. 17.
    H. T. S. Britton, S. J. Gregg and G. W. Winsor, Trans. Faraday Soc. 48 (1952), 63.CrossRefGoogle Scholar
  18. 18.
    J. N. Maycock and J. Skalny, Thermochimica Acta 5 (1973).Google Scholar
  19. 19.
    A. B. Carpenter, R. A. Chalmers, J. A. Gard, K. Speakman and H. F. W. Taylor, Amer. Min. 51, (1966), 56.Google Scholar
  20. 20.
    L. Heller, H. F. W. Taylor, Crystallographic Data for the Calcium Silicates, H. M. S. O., London, 1956.Google Scholar
  21. 21.
    L.E. Copeland and J. C. Hayes, ASTM Bull. 149 (1953), 70.Google Scholar
  22. 22.
    L. Heller, Chemistry of Cements, Proc. IIIrd Int. Symp.,77, 237, London, (1952).Google Scholar
  23. 23.
    D. Lawrence, Nature 201 (1964), 607.CrossRefGoogle Scholar
  24. 24.
    D. Lawrence, Proc. 7th Conf. Silicate Ind., 259, Budapest (1963).Google Scholar
  25. 25.
    R.N. Rogers and E. D. Morris, Anal. Chem., 38, (1966),412.CrossRefGoogle Scholar
  26. 26.
    H.E. Kissinger, Anal. Chem. 29, (1957), 1702.CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media New York 1974

Authors and Affiliations

  • J. N. Maycock
    • 1
  • J. Skalny
    • 1
  • R. S. Kalyoncu
    • 1
  1. 1.Martin Marietta LaboratoriesBaltimoreUSA

Personalised recommendations