Tensile and Impact Properties of 7075-T6 and 7079-T6 Plate, Hand Forgings, and Tensile Properties of Plate MIG Weldments between 75° and -320°F
In selecting an aluminum alloy for cryogenic service, the design engineer must consider the form of the mill product, its thickness, and the type of service condition it will encounter. All factors must be properly weighed, and the alloy selected should be that which has the best properties at the operating cryogenic temperature.
KeywordsTensile Property Cryogenic Temperature Impact Property Notch Toughness Single Shear
Unable to display preview. Download preview PDF.
- 1.K.O. Bogardus, G. W. Stickley, and F.M. Howell, “A Review of Information on the Mechanical Properties of Aluminum Alloys at Low Temperatures,” NACA Tech. Note 2082 (May 1950).Google Scholar
- 2.L.M. Smith, “Tensile Properties of Light Alloys at Low Temperature,” PB 151843, U.S. Department of Commerce, Office of Technical Services (December 1958).Google Scholar
- 3.R. Fellom, Jr., “Aluminum in Cryogenics” in Light Metal Age (February 1960).Google Scholar
- 4.R. L. McGee, J. E. Campbell, R.L. Carlson, and G.E. Manning, “The Mechanical Properties of Certain Aircraft Structural Metals at Very Low Temperatures,” WADC Tech. Report 58–386 (June 1958).Google Scholar
- 5.The Aluminum Association, “Standards for Wrought Aluminum Mill Products,” 3rd Revision (March 1960).Google Scholar
- 6.E.T. Wessel and R.D. Qlleman, “Apparatus for Tension Testing at Subatmospheric Temperatures,” ASTM Bulletin (January 1953).Google Scholar
- 7.H. Neuber, Theory of Notch Stresses, Edwards Brothers, Ann Arbor, Michigan (1946).Google Scholar
- 8.R. D. Olieman and G. C. Wolfer, “The Tensile and Impact Properties of Plate and Welds of Aluminum Alloy 5083-H113 Between 75° and -320°F,” Advances in Cryogenic Engineerings Vol. 5, K.D. Timmerhaus (ed.), Plenum Press, Inc., New York (1960) p. 430.Google Scholar