Samples of hot-pressed silicon nitride were tested in 3-point bend impact loading at ambient temperature, 1100°C, 1250°C, and 1400°C under isothermal conditions. Dynamic stress intensity factors (KIC) were calculated from the fracture load and the dimensions of an induced surface flaw, produced by a Knoop hardness indenter. Dynamic stress intensities of about 5.25 MN/m3/2 were determined for all temperatures up to 1250°C. A 20% drop in KIC was found at 1400°C. This drop in KIC coincides with a change in the fracture surface at the same temperature, indicating a change in the micromechanics of fracture at 1400°C.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Preview
Unable to display preview. Download preview PDF.
References
R. L. Bertolotti, “Strength and Absorbed Energy in Instrumented Impact Tests of Polycrystalline Al2O3”, J. Am. Ceram. Soc. 57 [7] 300 (1974).
H. Abe, “Instrumented Charpy Impact Testing of Silicon Carbide”, PhD Dissertation, Pennsylvania State University, May 1976.
H. C. Chandan, H. Abe, and R. C. Bradt, “Elevated Temperature Charpy Impact Test of Silicon Carbide”, Abstract, Am. Ceram. Soc. Bul. 56 [3] 289 (1977).
J. M. Wimmer, I. Bransky, “Impact Resistance of Structural Ceramics”, Am. Ceram. Soc. Bui. .56 [6] 552 (1977).
M. G. Mendiratta, J. Wimmer, I. Bransky, “Dynamic KIC 6c Dynamic Flexural Strength of HS-130 Si3N4”, J. Mat. Sci. 12 212 (1977).
J. J. Petrovic, L. A. Jacobson, P. K. Talty, and A. K. Vasudevan, “Controlled Surface Flaws in Hot-Pressed Si3N4, J. Am. Ceram. Soc. 58 [3–4] 113 (1975).
J. J. Petrovic, L. A. Jacobson, “Controlled Surface Flaws in Hot-Pressed SiC”, J. Am. Ceram. Soc. 59 [l-2] 34 (1976).
Y. W. Mai, “Thermal Shock Resistance and Fracture Strength Behavior of Two Tool Carbides”, J. Am. Ceram. Soc. 59 [11–12] 491 (1976).
G. R. Marrs and C. W. Smith, “A Study of Local Stresses Near Surface Flaws in Bending Fields”, p. 23 in Stress Analysis and Growth of Cracks, Am. Soc. of Test. Mat., Spec. Tech Publ. #513, 1972.
H. P. Kirchner, R. M. Gruever, and W. A. Sotter, “Use of Fracture Mirrors to Interpret Impact Fractures in Brittle Materials” J. Am. Ceram. Soc. 58 [5–6] 188 (1975).
A. G. Evans and S. M. Wiederhorn, “Crack Propagation and Failure Prediction in Silicon Nitride at Elevated Temperatures”, J. Mat. Sci. 9 [2] 270 (1974).
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 1978 Plenum Press, New York
About this chapter
Cite this chapter
Gonczy, S.T., Johnson, D.L. (1978). Impact Fracture of Ceramics at High Temperature. In: Bradt, R.C., Hasselman, D.P.H., Lange, F.F. (eds) Flaws and Testing. Fracture Mechanics of Ceramics, vol 3. Springer, Boston, MA. https://doi.org/10.1007/978-1-4615-7017-2_29
Download citation
DOI: https://doi.org/10.1007/978-1-4615-7017-2_29
Publisher Name: Springer, Boston, MA
Print ISBN: 978-1-4615-7019-6
Online ISBN: 978-1-4615-7017-2
eBook Packages: Springer Book Archive