Electrochemically Obtained Information Concerning the Atomistics of Fracture in the Presence of Moisture

  • J. O’M. Bockris

Abstract

There are three types of cracking: (1) pure cracking, e.g., glass; (2) metal-metal embrittlement, e.g., sodium-steel; (3) stress corrosion cracking, e.g., most cracks.

Keywords

Stress Corrosion Stress Corrosion Crack Hydrogen Embrittlement Partial Molar Volume Cathodic Side 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    C. F. Barth, A. R. Troiano, Corrosion,28 259 (1972).Google Scholar
  2. 2.
    F. G. Hanna, A. R. Troiano, E. A. Steigerwald, Trans. Am. Soc. Metals, 57, 658 (1964).Google Scholar
  3. 3.
    M. Devanathan and Z. Stachurski, Proc. of Roy. Soc., A270, 90 (1962).CrossRefADSGoogle Scholar
  4. 4.
    W. Beck, J. O. M. Bockris, J. McBreen, L. Nanis, Proc. Roy. Soc., A290, 220 (1966).Google Scholar
  5. 5.
    R. Heindersbach, J. Jones, Report for U.S. Army Research Office, University of Rhode Island (1976).Google Scholar
  6. 6.
    J. McBreen, Ph.D. Dissertation University of Pennsylvania (1965).Google Scholar
  7. 7.
    R. M. Barber, “Diffusion in and through Solids,” MacMillan Co., New York (1941).Google Scholar
  8. 8.
    J. O. M. Bockris, J. McBreen, L. Nanis, J. Electrochem. Soc., 112, 1025 (1965).CrossRefGoogle Scholar
  9. 9.
    J. Chene, J. Galland, P. Azou, 4A4 Proc. Conf. 2nd Int. Congress Hydrogen in metals, Paris, France (1977).Google Scholar
  10. 10.
    J. O. M. Bockris and P. K. Subramanyan, Electrochim. Acta, 16, 2169 (1971).CrossRefGoogle Scholar
  11. 11.
    J. O. M. Bockris, P. K. Subramanyan, J. Electrochem. Soc., 118, 114 (1971).CrossRefGoogle Scholar
  12. 12.
    B. Marandet (1977), Proc. Conf. Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys. NACE-5, 774 (Unieux-Firminy, France (1973)).Google Scholar
  13. 13.
    R. D. McCright (1977) ibid. NACE-5, 306.Google Scholar
  14. 14.
    B. V. Tilak, C. G. Rader, B. E. Conway, Electrochim. Acta, 1167 (1977).Google Scholar
  15. 15.
    P. K. Subramanyan, Medical Technological Publication, Ine. Rev. Sci. Phys. Chem. Ser., One (1973) 6 181–238, ed., J. O. M. Bockris, Butterworth.Google Scholar
  16. 16.
    H. J. Flitt, W. R. Revie, J. O. M. Bockris, Corrosion Australase, 1, 3 (1976).Google Scholar
  17. 17.
    H. J. Flitt, Ph.D. Dissertation, Flinders University of South Australia.Google Scholar
  18. 18.
    R. R. Sayano and K. Nobe, Corrosion, 25, 260 (1969).Google Scholar

Copyright information

© Plenum Press, New York 1983

Authors and Affiliations

  • J. O’M. Bockris
    • 1
  1. 1.Department of ChemistryTexas A&M UniversityCollege StationUSA

Personalised recommendations