Loading Rate Effect on Tensile Failure Behavior of Gelatins under Mode I

  • Paul Moy
  • Mark Foster
  • C. Allan Gunnarsson
  • Tusit Weerasooriya
Conference paper
Part of the Conference Proceedings of the Society for Experimental Mechanics Series book series (CPSEMS)

Abstract

For decades, ballistic gelatin has been used as a tissue surrogate to test and evaluate bullets and firearms due to its similar viscosity to natural tissue. However, the high water content in ballistic gelatin makes it unstable at room temperature, and therefore causes it to have a poor shelf life. The development of polymer-based gels has shown promise as an alternative tissue surrogate. Polymer gels such as Perma-Gel are stable at room temperature and can be stored for long periods of time. Gels often fail due to tensile stresses during penetration. The failure behavior in tension is highly influenced by the presence of defects, such as cracks and voids, in the bulk material. A mode I experimental method was developed to obtain tensile failure criteria for the initiation and propagation behavior of these types of soft materials. Digital image correlation is used to determine the full-field surface strains around the crack tip to obtain a quantitative measure of the critical strain-field required for initiation and propagation of failure due to a defect. This systematic study utilizes these experimental techniques to determine the critical criteria for crack growth initiation and crack propagation of ballistic gelatins and a polymer gel as a function of loading rate. This paper presents experimental methodologies and results from Mode I fracture experiments including measured critical energy and strain-based criteria for failure initiation and growth, as well as their dependence on the rate of loading.

Keywords

Mold Rubber Dehydration Gelatin 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    Peterson, B. Ballistic Gelatin Lethality Performance of 0.375-in Ball Bearings and MAAWS 401B Flechettes. Army Research Laboratory Technical Report. ARL-TR-4153. 2007Google Scholar
  2. 2.
    Nicolas, N. C. and Welsch, J. R. Ballistic Gelatin, Institute for Non-Lethal Defense Technologies Report, The Pennsylvania State University Applied Research Laboratory.Google Scholar
  3. 3.
    MacPherson, D. Bullet Penetration: Modeling the Dynamics and the Incapacitation Resulting from Wound Trauma. Ballistic Publications. 1994.Google Scholar
  4. 4.
    Fackler, M. L. Ordnance Gelatin for Ballistic Studies. Association of Firearm and Toolmark Examiners Journal. 4:403-5. 1987.Google Scholar
  5. 5.
  6. 6.
    Moy, P., Weerasooriya, T., Juliano, T.F., VanLandingham, M.R., and Chen, W. Dynamic Response of an Alternative Tissue Simulant, Physically Associating Gels (PAG). Proceedings of the 2006 SEM Annual Conference. St. Louis, MO. 2006.Google Scholar
  7. 7.
    Salisbury, C.P. and Cronin, D.S., Mechanical Properties of Ballistic Gelatin at High Deformation Rates, Experimental Mechanics. 2009.Google Scholar
  8. 8.
    Juliano, T.F., Forster, A. M., Drzal, P.L., Weerasooriya, T., Moy, P., and VanLandingham, M.R., Multiscale Mechanical Characterization of Biomimetic Physically Associating Gels. J. Mater. Res., Vol 21, No. 8, Aug 2006.Google Scholar
  9. 9.
    Moy, P., Weerasooriya, T., and Gunnarsson, C. A., Tensile Deformation of Ballistic Gelatin as a Function of Loading Rate. Proceedings of the 2008 SEM Annual Conference. Orlando, FL. 2008.Google Scholar
  10. 10.
    Zhang, H. P., Niemczura, J., Dennis, G., Ravi-Chandar, K., and Marder, M. Toughening Effect of Strain-Induced Crystallites in Natural Rubber. Physical Review Letters, Vol. 102, Issue 24, id. 245503. June 2009.Google Scholar
  11. 11.
    Moy, P., Weerasooriya, T., and Gunnarsson, C. A., Tensile Deformation and Fracture of Ballistic Gelatin as a Function of Loading Rate. Proceedings of the 2009 SEM Annual Conference. Albuquerque, NM. June 2009.Google Scholar
  12. 12.
    Chu, T. C., Ranson, W. F., Sutton, M. A., and Peters, W. H. Applications of Digital-Image-Correlation Techniques to Experimental Mechanics. Experimental Mechanics. September 1995.Google Scholar
  13. 13.
    Sutton, M. A., Wolters, W. J., Peters, W. H., Ranson, W. F., and McNeill, S. R. Determination of Displacements Using an Improved Digital Image Correlation Method. Computer Vision. August 1983.Google Scholar
  14. 14.
    Bruck, H. A., McNeill, S. R., Russell S. S., Sutton, M. A. Use of Digital Image Correlation for Determination of Displacements and Strains. Non-Destructive Evaluation for Aerospace Requirements. 1989.Google Scholar
  15. 15.
    Sutton, M. A., McNeill, S. R., Helm, J. D., Schreier, H. Full-Field Non-Contacting Measurement of Surface Deformation on Planar or Curved Surfaces Using Advanced Vision Systems. Proceedings of the International Conference on Advanced Technology in Experimental Mechanics. July 1999.Google Scholar
  16. 16.
    Sutton, M. A., McNeill, S. R., Helm, and Chao, Y. J. Advances in Two-Dimensional and Three-Dimensional Computer Vision. Photomechanics. Volume 77. 2000.Google Scholar

Copyright information

© Springer Science+Business Media, LLC 2011

Authors and Affiliations

  • Paul Moy
    • 1
  • Mark Foster
    • 1
  • C. Allan Gunnarsson
    • 1
  • Tusit Weerasooriya
    • 1
  1. 1.Weapons and Materials Research DirectorateArmy Research LaboratoryCollege ParkUSA

Personalised recommendations