Powder Metallurgy Processing of Rapidly Solidified Alloyed Cast Iron Powders for Machine Components

  • S. K. KhuntiaEmail author
  • B. B. Pani
Conference paper
Part of the Lecture Notes in Mechanical Engineering book series (LNME)

Abstract

Cast iron powders containing little amount of Al, Cr, and Si were produced via water atomization technique and then got annealed at 900 °C for removing oxygen in hydrogen atmosphere. The advantages of rapid solidification remained undisturbed in spite of high temperature. The powders after pre-compaction studies were cold compacted up to 700 MPa pressure and then sintered at different temperatures like 720, 850, and 1000 °C. Growth like dimensional changes was observed in all the samples. The sample which was compacted at 700 MPa and sintered at 1000 °C showed 48 HRC hardness. High hardness values could enable these materials for manufacturing high-strength machine components.

Keywords

Water atomization Cast iron powders Compaction Sintering 

References

  1. 1.
    Sherby, O.D.: Ultra high carbon steels and ancient blacksmiths. Iron Steel Inst. Jpn. Int. 39(7), 637–648 (1999)CrossRefGoogle Scholar
  2. 2.
    Serby, O.D.: Superplastic ultra high carbon steel. Scr. Metall. 9, 569–574 (1975)CrossRefGoogle Scholar
  3. 3.
    Mordike, B.L., Kainer, K.U.: Consolidation of rapidly solidified powders. Solid State Phenom. 8, 9, 135–148 (1989)CrossRefGoogle Scholar
  4. 4.
    Lesuer, D.R., Syn, C.K., Goldberg, A., Wadsworth, J., Serby, O.D.: The case for ultra high carbon steels as structural materials. JOM 45, 40–46 (1993)CrossRefGoogle Scholar
  5. 5.
    Mohanty, O.N.: Rapid solidification of cast iron-some new observations. Trans. Tech. Publ. 18, 19, 65–82 (1989)Google Scholar
  6. 6.
    Pani, B.B.: Studies on production of water atomised white cast iron and iron powders from sponge iron fines and composite manufacturing. Ph.D. thesis. IIT, Kharagpur (2001)Google Scholar
  7. 7.
    Pani, B.B., Mukunda, P.G., Mohanty, O.N.: Processing and microstructural analysis of rapidly solidified white cast iron powders. Trans. Powder Metall. Assoc. India 28, 1–4 (2002)Google Scholar
  8. 8.
    Walser, B., Kayali, E.S., Serby, O.D.: Warm working and superelasticity in plain ultra high carbon steels. In: 4th International Conference on the Strength of Metals and Alloys, vol. 1(8), pp. 266–270 (1976)Google Scholar
  9. 9.
    Serby, O.D.: Superplastic boarding of ferrous laminates. Scr. Metall. 13(10), 941–946 (1979)CrossRefGoogle Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2020

Authors and Affiliations

  1. 1.College of Engineering BhubaneswarBhubaneswarIndia
  2. 2.Veer Surendra Sai University of TechnologyBurlaIndia

Personalised recommendations