The Effect of Aluminum Content on the Microstructures of Single-Phase γ-TiAl-Based Alloy

  • Yaodong Xuanyuan
  • Yan Long
  • Yinbiao Yan
  • Sen YangEmail author
Conference paper
Part of the Springer Proceedings in Physics book series (SPPHY, volume 217)

Abstract

TiAl-based alloys have not only excellent high-temperature strength, high-temperature creep and oxidation resistance, but also low density and high strength-to-weight ratio, having extensive application prospect in the aerospace and automobile industry. In this paper, the single-phase γ-TiAl-based alloys were studied. In order to refine the coarse microstructures of single-phase γ-TiAl-based alloys, three different kinds of γ-TiAl-based alloys, including Ti–54Al (at.%), Ti–52Al (at.%), and Ti–50Al (at.%), were melted and homogenized at 1150 °C for 36 h. The effect of composition on grain refinement and grain boundary distribution of single-phase γ-TiAl-based alloys were investigated. The results showed that the grain size of the alloys was refined with the increase of aluminum content after homogenizing treatment. In addition, the grain boundary character distribution was non-uniform. Inside the columnar crystals, there were a large number of coherent Σ3 grain boundaries. The derived capacity of Σ3 grain boundaries was poor, and general high-angle grain boundaries were connected to each other.

Keywords

Γ-TiAl-based alloys Aluminum content Grain boundary character distribution 

References

  1. 1.
    G. Welsch, R. Boyer, E.W. Collings, Materials Properties Handbook: Titanium Alloys (ASM international, 1993)Google Scholar
  2. 2.
    F. Appel, J.D.H. Paul, M. Oehring, Gamma Titanium Aluminide Alloys: Science and Technology (Wiley, 2011)Google Scholar
  3. 3.
    J.C. Schuster, M. Palm, Reassessment of the binary aluminum-titanium phase diagram. J. Phase Equilib. Diffus. 27(3), 255–277 (2006)CrossRefGoogle Scholar
  4. 4.
    T. Watanabe, An approach to grain-boundary design for strong and ductile polycrystals. Res. Mech. 11(1), 47–84 (1984)Google Scholar
  5. 5.
    G. Palumbo, E.M. Lehockey, P. Lin, Applications for grain boundary engineered materials. JOM 50(2), 40–43 (1998)CrossRefGoogle Scholar
  6. 6.
    C. Cheung, U. Erb, G. Palumbo, Application of grain boundary engineering concepts to alleviate intergranular cracking in alloys 600 and 690. Mater. Sci. Eng. A 185(1–2), 39–43 (1994)CrossRefGoogle Scholar
  7. 7.
    E.M. Lehockey, G. Palumbo, P. Lin, Improving the weldability and service performance of nickel-and iron-based superalloys by grain boundary engineering. Metall. Mater. Trans. A 29(12), 3069–3079 (1998)CrossRefGoogle Scholar
  8. 8.
    G. Palumbo, Thermomechanical Processing of Metallic Materials. U.S. Patent No. 5,702,543 (1997)Google Scholar
  9. 9.
    G. Palumbo, Metal Alloys Having Improved Resistance to Intergranular Stress Corrosion Cracking. U.S. Patent No. 5,817,193 (1998)Google Scholar
  10. 10.
    D. Shechtman, M.J. Blackburn, H.A. Lipsitt, The plastic deformation of TiAl. Metall. Trans. 5(6), 1373–1381 (1974)CrossRefGoogle Scholar
  11. 11.
    R.G. Baligidad, U. Prakash, V.R. Rao et al., Effect of addition of β-phase stabilizing elements (Nb, Mo and V) on plastic behaviour of Ti3Al single crystals with the D019 structure. Metall. Trans. A 6(11), 1991 (1975)CrossRefGoogle Scholar
  12. 12.
    G. Hug, A. Loiseau, A. Lasalmonie, Nature and dissociation of the dislocations in TiAl deformed at room temperature. Philos. Mag. A 54(1), 47–65 (1986)CrossRefGoogle Scholar
  13. 13.
    V. Randle, Mechanism of twinning-induced grain boundary engineering in low stacking-fault energy materials. Acta Mater. 47(15), 4187–4196 (1999)CrossRefGoogle Scholar
  14. 14.
    V. Randle, Twinning-related grain boundary engineering. Acta Mater. 52(14), 4067–4081 (2004)CrossRefGoogle Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2019

Authors and Affiliations

  • Yaodong Xuanyuan
    • 1
  • Yan Long
    • 1
  • Yinbiao Yan
    • 1
  • Sen Yang
    • 1
    Email author
  1. 1.School of Material Science and EngineeringNanjing University of Science and TechnologyNanjingChina

Personalised recommendations