Reflection Crack Assessment Using Digital Image Analysis

  • Sireesh SarideEmail author
  • V. Vinay Kumar
Chapter
Part of the Developments in Geotechnical Engineering book series (DGE)

Abstract

The current research aims to understand and assess the reflection crack mechanism in two-layered asphalt beam system, consisting of an old pavement (bottom) layer and a hot mix asphalt (HMA) overlay reinforced with geosynthetic-interlayers. The beam fatigue tests were adopted to understand the crack mechanism and the assessment of crack phenomenon was done by means of a digital image analysis program. In this regard, two different notch conditions such as 25 and 40 mm notch depths and a notch-less case were considered in the study. In addition, a polyester grid (PET) and a glass-grid composites (GGC) were adopted as geosynthetic-reinforcements in the study. Results indicate that the digital image analysis is effective in assessing the cracking mechanism and phenomenon efficiently. The geosynthetic-interlayers have enhanced the fatigue life, against the reflection cracking phenomenon, irrespective of notch depth. The performance of specimens with 40 mm notch depth is superior than that of specimens with 25 mm notch depth, irrespective of the geosynthetic type. The digital image analysis suggests that an average reduction in tensile strain of about 35% and 70% was achieved in grid and composite-reinforced specimens, against the control specimens, irrespective of notch depths.

Keywords

Reflection cracks Asphalt overlays Digital image correlation Grids and composites 

References

  1. 1.
    Cleveland, G.S., Button, J.W., Lytton, R.L.: Geosynthetic in Flexible and Rigid Pavement Overlay. Texas Transportation Institute, Texas A&M University System. Report, pp. 1777–1781 (2002)Google Scholar
  2. 2.
    De Bondt, A.: Effect of reinforcement properties. In: Proceedings of 4th International RILEM Conference on Reflective Cracking in Pavements, pp. 13–22Google Scholar
  3. 3.
    Kim, J., Buttlar, W.G.: Analysis of reflective crack control system involving reinforcing grid over base-isolating interlayer mixture. J. Trans. Eng. 128(4), 375–385 (2002)CrossRefGoogle Scholar
  4. 4.
    Bandaru, R.: Cost-Effective Prevention of Reflective Cracking in Composite Pavements. MS thesis Submitted to Louisiana State University, Baton Rouge (2010)Google Scholar
  5. 5.
    Button, J.W., Lytton, R.L.: Guidelines for using geosynthetics with HMA overlays to reduce reflective cracking. Report 1777–P2. Texas Department of Transport Austin, Texas (2003)Google Scholar
  6. 6.
    Saride, S., Kumar, V.V.: Influence of geosynthetic-interlayers on the performance of asphalt overlays on pre-cracked pavements. Geotext. Geomemb. 45(3), 184–196 (2017)CrossRefGoogle Scholar
  7. 7.
    Zamora-Barraza, D., Calzada-Perez, M.A., Castro-Fresno, D., Vega-Zamanillo, A.: Evaluation of anti-reflective cracking systems using geosynthetics in the interlayer zone. Geotext. Geomemb. 29(2), 130–136 (2011)CrossRefGoogle Scholar
  8. 8.
    Ogundipe, O.M., Thom, N., Collop, A.: Investigation of crack resistance potential of stress absorbing membrane interlayers (SAMIs) under traffic loading. Constr. Build Mater. 38, 658–666 (2012)CrossRefGoogle Scholar
  9. 9.
    Kumar, V.V., Saride, S.: Use of digital image correlation for the evaluation of flexural fatigue behavior of Asphalt beams with geosynthetic interlayers. Trans. Res. Rec. J. Transp. Res. Board 2631, 55–64 (2017)Google Scholar
  10. 10.
    Kumar, V.V., Saride, S.: Evaluation of cracking resistance potential of geosynthetic-reinforced asphalt overlays using direct tensile strength tests. Constr. Build. Mater. 162, 37–47 (2018)CrossRefGoogle Scholar
  11. 11.
    Sanders, P.J.: Reinforced Asphalt Overlays for Pavements. Ph.D. Thesis Ssubmitted to University of Nottingham (2001)Google Scholar
  12. 12.
    Virgili, A., Canestrari, F., Grilli, A., Santagata, F.A.: Repeated load test on bituminous systems reinforced by geosynthetics. Geotext. Geomemb. 27, 187–195 (2009)CrossRefGoogle Scholar
  13. 13.
    Ferrotti, G., Canestrari, F., Pasquini, E., Virgili, A.: Experimental evaluation of the influence of surface coating on fiberglass geogrid performance in asphalt pavements. Geotext. Geomemb. 34, 11–18 (2012)CrossRefGoogle Scholar
  14. 14.
    Pasquini, E., Bocci, M., Canestrari, F.: Laboratory characterisation of optimised geocomposites for asphalt pavement reinforcement. Geosynth. Intl. 21(1), 24–36 (2014)CrossRefGoogle Scholar
  15. 15.
    Pasquini, E., Pasetto, M., Canestrari, F.: Geocomposites against reflective cracking in asphalt pavements: laboratory simulation and field application. Road Mater. Pavement Des. 16(4), 815–835 (2015)CrossRefGoogle Scholar
  16. 16.
    Saride, S., Kumar, V.V.: Estimation of service life of geosynthetic-reinforced asphalt overlays from beam and large-scale fatigue tests. J. Test. Eval. 47(4), 20170605 (2019)CrossRefGoogle Scholar
  17. 17.
    Livneh, M., Ishai, I., Kief, O.: Bituminous pre-coated geotextile felts for retarding reflection cracks. In: Proceedings of 2nd International RILEM Conference on Pavements, pp. 343–350Google Scholar
  18. 18.
    De Benedetto, H., Neji, J., Antonie, J., Pasquier, M.: Apparatus for laboratory study of cracking resistance. In: Proceedings of 2nd International RILEM Conference on Pavements, pp. 179–186 (1993)Google Scholar
  19. 19.
    Francken, L., Vanelstraete, A.: On the thermorheological properties of interface systems. In: Proceedings of 2nd International RILEM Conference on Pavements, pp. 206–219 (1993)Google Scholar
  20. 20.
    Prieto, J.N., Gallego, J., Perez, I.: Application of the wheel reflective cracking test for assessing geosynthetics in anti-reflection pavement cracking systems. Geosynth. Int. 14(5), 287–297 (2007)CrossRefGoogle Scholar
  21. 21.
    Moreno-Navarro, F., Rubio-Gamez, M.C.: UGR-FACT test for the study of fatigue cracking in bituminous mixes. Constr. Build. Mater. 53, 182–189 (2014)CrossRefGoogle Scholar
  22. 22.
    Grediac, M.: The use of full-field measurement methods in composite material characterization: interest and limitations. Compos. A Appl. Sci. Manuf. 35, 751–761 (2004)CrossRefGoogle Scholar
  23. 23.
    Romeo, E.: Two-dimensional digital image correlation for asphalt mixture characterization: interest and limitations. Road Mater. Pavement Des. 14(4), 747–763 (2013)CrossRefGoogle Scholar
  24. 24.
    Choi, S., Shah, S.P.: Measurement of deformations on concrete subjected to compression using image correlation. Exp. Mech. 37, 307–313 (1997)CrossRefGoogle Scholar
  25. 25.
    Kim, Y.R., Wen, H.: Fracture energy from indirect tension test. J. Ass. Asph. Pav. Technol. 71, 779–793 (2002)Google Scholar
  26. 26.
    Safavizadeh, S.A., Wargo, A., Guddati, M., Kim, Y.R.: Investigating reflective cracking mechanisms in grid-reinforced asphalt specimens. Transp. Res. Rec. J. Transp. Res. Board 2507, 29–38CrossRefGoogle Scholar
  27. 27.
    Wargo, A, Safavizadeh, S.A., Kim, Y.R.: Comparing the performance of fiberglass grid with composite interlayer systems in asphalt concrete. Transp. Res. Rec. J. Transp. Res. Board 2631, 123–132CrossRefGoogle Scholar
  28. 28.
    MORTH. Specifications for Road and Bridge works. Ministry of Road Transport and Highways, Government of IndiaGoogle Scholar
  29. 29.
    ASTM D6927. Standard Test Method for Marshall Stability and Flow of Asphalt Mixtures. Annual Book of ASTM Standards, ASTM International, West Conshohocken, PAGoogle Scholar
  30. 30.
    ASTM D4595. Standard Test Method for Determining Tensile Properties of Geotextiles by the Wide-Width Strip Method. Annual Book of ASTM Standards, ASTM International, West Conshohocken, PAGoogle Scholar
  31. 31.
    Caltabiano, M.A.: Reflection Cracking in Asphalt Overlays. Master of Philosophy Thesis submitted to the University of Nottingham (1990)Google Scholar
  32. 32.
    Khodaii, A., Fallah, S., Nejad, F.M.: Effects of geosynthetics on reduction of reflection cracking in asphalt overlays. Geotext. Geomemb. 27, 1–8 (2009)CrossRefGoogle Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2019

Authors and Affiliations

  1. 1.Department of Civil EngineeringIIT HyderabadKandiIndia

Personalised recommendations