Effect of Various Additives on the Properties of Fly Ash Based Geopolymer Mortar

  • Rashik Mustafa
  • K. N. Shivaprasad
  • Bibhuti Bhusan DasEmail author
Conference paper
Part of the Lecture Notes in Civil Engineering book series (LNCE, volume 25)

Abstract

In the present study, setting time and variation in strength of fly ash based geopolymer mortar prepared from natural sand as fine aggregates. Blast furnace slag (GGBS), micro silica and lime dust used as additives to fly ash based geopolymer mortar at 5, 10 and 15% of weight of fly ash. Alkaline activator used in the present study is combination of sodium silicate solution and sodium hydroxide solution. Concentration of sodium hydroxide solution was maintained 10 M and sodium silicate to sodium hydroxide ratio was fixed as 2.5:1 by weight. From the test results, it is observed that setting time and compressive strength geopolymer samples were significantly influenced by the type of additive added in the preparation of the geopolymer mortar.

Keywords

Setting time Compressive strength Geopolymer mortar Blast furnace slag Micro silica Lime 

References

  1. 1.
    Shiva Prasad, K. N., & Das, B. B. (2016). Effect of liquid to solid ratio on the fly ash based geopolymer: A review. In International Conference on Advances in Concrete Technology Materials and Construction Practices, pp. 331–338.Google Scholar
  2. 2.
    de Vargas, A. S., Denise, D. M., Ângela, B. M., Antônio, V., Joao, C. G., & Ruby, M. G. (2014). Strength development of alkali-activated fly ash produced with combined NaOH and Ca(OH)2 activators. Cement and Concrete Composites, 53, 341–349.CrossRefGoogle Scholar
  3. 3.
    Dimas, D., Giannopoulou, I., & Panias, D. (2009). Polymerization in sodium silicate solutions: A fundamental process in geopolymerization technology. Journal of materials science, 44(14), 3719–3730.CrossRefGoogle Scholar
  4. 4.
    Hardjito, D., Chua, C. C., & Carrie, H. L. (2008). Strength and setting times of low calcium fly ash-based geopolymer mortar. Modern Applied Science, 2(4), 3.CrossRefGoogle Scholar
  5. 5.
    Atiş, C. D., Görür, E. B., Karahan, O., Bilim, C., İlkentapar, S., & Luga, E. (2015). Very high strength (120 MPa) class F fly ash geopolymer mortar activated at different NaOH amount, heat curing temperature and heat curing duration. Construction and Building Materials, 96, 673–678.CrossRefGoogle Scholar
  6. 6.
    Hardjito, D., Steenie, E. W., Dody, M. J. S., & Rangan, B. V. (2004). On the development of fly ash-based geopolymer concrete. ACI Materials Journal-American Concrete Institute, 101(6), 467–472.Google Scholar
  7. 7.
    IS: 1727. (1967). Indian standard for methods of test for pozzolanic materials, New Delhi.Google Scholar
  8. 8.
    IS: 4031 (Part 6). (1988). Indian standard for methods of physical tests for hydraulic cement, part 6 determination of compressive strength of hydraulic cement other than masonry cement, New Delhi.Google Scholar
  9. 9.
    IS: 8142. (1976). Indian standard for method of test for determining setting time of concrete by penetration resistance, New Delhi.Google Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2019

Authors and Affiliations

  • Rashik Mustafa
    • 1
  • K. N. Shivaprasad
    • 1
  • Bibhuti Bhusan Das
    • 1
  1. 1.Department of Civil EngineeringNational Institute of Technology Karanataka, SurathkalMangaloreIndia

Personalised recommendations