Effect of Silica Fume on Fly Ash Based Geopolymer Mortar with Recycled Aggregates

  • Kumar S. Vaibhav
  • Manish Nagaladinni
  • M. Madhushree
  • B. P. PriyaEmail author
Conference paper
Part of the Lecture Notes in Civil Engineering book series (LNCE, volume 25)

Abstract

Geopolymer mortar is obtained by replacing cement by a cementatious material like fly ash, ground granulated blast furnace slag or silica fume with the addition of alkaline solution and silicate solution as activators for binding instead of water. In the current study, effect of silica fume on fly ash based geopolymer mortar using recycled aggregates is studied in two series. In the first series, only fine aggregates are replaced by recycled fine aggregates in various percentages and in the second series, along with replacement of M Sand by recycled fine aggregates in various percentages silica fume (10%) is added. In both the cases, compressive strength and tensile strengths are determined for 7 and 28 days where the samples are cured at 32 °C, i.e., ambient temperature. The 7-day compressive strength had an increasing and decreasing pattern for 0% silica fume. The tensile strength increased till 50% replacement by recycled aggregates and decreased with further increase in replacement of recycled aggregates. For 28 days, the compressive strength increased for control mix and decreased with further increase in replacement of recycled fine aggregates. The tensile strength shows the same pattern as in the 7-day strength. These patterns may be due to high water absorption in recycled aggregates which does not permit the liquid content to be available for geopolymerization. As the ambient temperature was preferred to cure the specimens, in the initial stages high temperature was not available for aiding geopolymerization which may also be a probable reason for the strength pattern. Addition of silica fume did not considerably increase the strength as expected initially. The mortar mix considered for the current study can be used as medium grade masonry mortar.

Keywords

Geopolymer mortar Fly ash Silica fume Recycled fine aggregates Compressive strength Tensile strength 

References

  1. 1.
    Kaur, M., Singh, J., & Kaur, Manpreet. (2018). Synthesis of fly ash based geopolymer mortar considering different concentrations and combination of alkaline activator solution. Ceramics International, 44, 1534–1537.CrossRefGoogle Scholar
  2. 2.
    Temuujin, J., Williams, R.P., & van Riessen, A. (2009). Effect of mechanical activation of fly ash on the properties of geopolymer cured at ambient temperature. Journal of Materials Processing Technology, 209, 5276–5280.CrossRefGoogle Scholar
  3. 3.
    Thokchom, S., Dutta, D., & Ghosh, S. (2011). Effect of incorporating silica fume in fly ash geopolymers. International journal of Civil and Environmental Engineering 5(12).Google Scholar
  4. 4.
    Okoye, F. N., Durgaprasad, J., & Singh, N. B. (2016). Effect of silica fume on the mechanical properties of fly ash based geopolymer concrete. Ceramics International, 42, 3000–3006.CrossRefGoogle Scholar
  5. 5.
    Wagih, A. M., El-Karmoty, H. Z., Ebid, M., Okba, S. H. (2013). Recycled construction and demolition concrete waste as aggregate for structural concrete. Housing and Building National Research Center, pp. 193–200.Google Scholar
  6. 6.
    Adam A. A., & Horianto (2014). The effect of temperature and duration of curing on the strength of fly ash based geopolymer mortar. 2nd International Conference on Sustainable Civil Engineering Structures and Construction Materials 2014, Procedia Engineering 95, 410–414.CrossRefGoogle Scholar
  7. 7.
    ASTM C618 - 08. Standard specification for coal fly ash and raw or calcined natural pozzolan for use in concrete.Google Scholar
  8. 8.
    IS 2386 Part III. (1963). Methods of test for aggregates for concrete.Google Scholar
  9. 9.
    IS 2250. (1981). Code of practice for preparation and use of masonry mortars.Google Scholar
  10. 10.
    IS 383. (1970). Specification for coarse and fine aggregates from natural sources for concrete.Google Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2019

Authors and Affiliations

  • Kumar S. Vaibhav
    • 1
  • Manish Nagaladinni
    • 1
  • M. Madhushree
    • 1
  • B. P. Priya
    • 1
    Email author
  1. 1.Department of Civil EngineeringPES UniversityBangaloreIndia

Personalised recommendations