Fatigue Behavior and Failure Analysis of Ti-6Al-4V Forging with High Oxygen Content

  • Yunxi Liu
  • Wei Chen
  • Zhiqiang Li
  • Bin Tang
  • Gang Yao
Conference paper

Abstract

The microstructure, texture and HCF (high cycle fatigue) behavior of a Ti–6Al–4V forging with 0.20 wt% oxygen were investigated. The material was composed of 80 vol% of equiaxed αp grains and 20 vol% of transformed β (βT). Average size of the αp phase was about 14 μm. EBSD analysis indicated a weak basal texture with intensity of 2 times random. The forging billet exhibited a good combination of ductility and strength performance and the mechanical properties did not show obvious anisotropy. The fatigue life had a large scatter and the mean life increased as the stress level decreased. The minimum life and POF = 0.1% life of the samples increased with the decrease of stress level. The difference of the feature of facets at the fatigue crack initiation region is considered to be the main cause of fatigue life scatter. The formation of the faceted area in fatigue crack initiation area results from the nucleation site of fatigue crack located in grain clusters with similar orientation.

Keywords

Ti–6Al–4V alloy Basal texture High cycle fatigue Life distribution High oxygen content 

References

  1. 1.
    Leyens C, Peters M, Titanium and Titanium Alloys, WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim, 2003.Google Scholar
  2. 2.
    Lütjering G, Williams J C., Titanium, Springer Berlin Heidelberg, 2007.Google Scholar
  3. 3.
    Beijing Aeronautical Materials Research Institute, Aeronautical Materials Technology, Aviation Industry Press, 2013.Google Scholar
  4. 4.
    Liu Zhicheng, Zhang Lijun, Zhang Chenhui, Effects of oxygen content on mechanical Properties of TC4 Titanium Alloy, World Non. Metals. 16 (2016)151–153.Google Scholar
  5. 5.
    Wei Qianqian, Oxygen content on microstructure and mechanical properties of Ti-Nb-Ta-Zr alloy. Shanghai: Shanghai Jiao Tong University, 2011.Google Scholar
  6. 6.
    Gong Minli, Li Shuying, The influence of oxygen content on the mechanical properties of TA5 sheet, Cas. technol. 4 (2016) 647–648.Google Scholar
  7. 7.
    Wang Hai, Wei Fen, Deng Jiabin, et al., Study on the factors affecting the strength ratio of titanium alloy and its action mechanism, Hot working technol. 22 (2016) 109–111.Google Scholar
  8. 8.
    Shen Rui, Chen Feng, Yu Xinquan, et al., The effect of oxygen content on Microstructure and mechanical properties of Ti-35Nb-3.7Zr-1.3Mo-xO alloy, J. Sou. Uni. (Natural Science Edition). 3 (2015) 478–483.Google Scholar
  9. 9.
    Schijve J, Fatigue of structures and materials, Dordrecht: Kluwer Academic, 2001.Google Scholar
  10. 10.
    Bai Xin, Xie Liyang, Ren Jungang, et al., Fatigue test and data processing method of metallic materials, Phy. Tes. and Che. Ana. Phy. 51 (2015) 375–380.Google Scholar
  11. 11.
    Gao Zhen Tong, Xiong Junjiang, Fatigue Reliability, Beijing: Beijing University of Aeronautics and Astronautics Press, 2000.Google Scholar
  12. 12.
    Schijve J, Wu Xueren, Fatigue of structures and materials, Beijing: Avi. Ind. Press, 2014.Google Scholar
  13. 13.
    Larsen J M, Jha S K, Szczepanski C J, et al., Reducing uncertainty in fatigue life limits of turbine engine alloys, Int. J. Fatigue. 57 (2013) 103–112.Google Scholar
  14. 14.
    Zhong Qunpeng, Zhao Zihua, Fractography, Beijing: Higher Education Press, 2006.Google Scholar
  15. 15.
    Bache M R, Evans W J, Davies H M, Electron back scattered diffraction (EBSD) analysis of quasi-cleavage and hydrogen induced fractures under cyclic and dwell loading in titanium alloys, J. Mater. Sci. 32 (1997) 3435–3442.Google Scholar
  16. 16.
    Bridier F, Villechaise P, Mendez J., Slip and fatigue crack formation processes in an α/β titanium alloy in relation to crystallographic texture on different scales, Acta Mater. 56 (2008) 3951–3962.Google Scholar
  17. 17.
    Jha S K, Szczepanski C J, John R, et al., Deformation heterogeneities and their role in life-limiting fatigue failures in a two-phase titanium alloy, Acta Mater. 82 (2015) 378–395.Google Scholar
  18. 18.
    Jha S K, Szczepanski C J, Golden P J, et al., Characterization of fatigue crack-initiation facets in relation to lifetime variability in Ti–6Al–4V, Int. J. Fatigue. 42 (2012) 248–257.Google Scholar
  19. 19.
    Pilchak A L, Williams J C., Observations of Facet Formation in Near-α, Titanium and comments on the role of hydrogen, Metall. Mater. Trans. A. 42 (2011) 1000–1027.Google Scholar
  20. 20.
    Bantounas I, Dye D, Lindley T C., The effect of grain orientation on fracture morphology during high-cycle fatigue of Ti–6Al–4V, Acta Mater. 57 (2009) 3584–3595.Google Scholar
  21. 21.
    Pilchak A L, Szczepanski C J, Shaffer J A, et al., Characterization of microstructure, texture, and microtexture in near-alpha titanium mill products, Metall. Mater. Trans. A. 44 (2013) 4881–4890.Google Scholar
  22. 22.
    Liu Y X, Chen W, Li Z Q, et al. The HCF behavior and life variability of a Ti-6Al-4V alloy with transverse texture, Int. J. Fatigue. 97 (2017) 79–87.Google Scholar

Copyright information

© Springer Nature Singapore Pte Ltd. 2018

Authors and Affiliations

  • Yunxi Liu
    • 1
    • 2
  • Wei Chen
    • 1
  • Zhiqiang Li
    • 1
    • 2
  • Bin Tang
    • 3
  • Gang Yao
    • 1
  1. 1.AVIC Manufacturing Technology InstituteBeijingChina
  2. 2.Aviation Key Laboratory of Science and Technology on Plastic FormingBeijingChina
  3. 3.Northwestern Polytechnical UniversityXi’anChina

Personalised recommendations