Determination of Subcritical Crack Growth Threshold in Ceramics with Indentation Flaws

  • J. H. Gong
  • Z. D. Guan
Chapter

Abstract

A technique for determining high temperature subcritical crack growth threshold in ceramics with indentation flaws is presented. This technique requires prior knowledge of the residual stress field about the indentation. Detailed analysis shows that the residual stress is the only driving force for crack growth of indentation flaws in absence of any applied stress. Under certain conditions, it can cause a spontaneous extension or healing of the indentation flaw. Making the duration from just indented to measurement of crack dimension long enough, an equilibrium configuration for the indentation flaw system may be obtained and the threshold can be calculated with parameters which are used to characterize this configuration. This technique is then applied to a pressureless sintered Si3N4. It is shown that this technique may be a simple and reliable method for the determination of subcritical crack growth threshold of ceramics at elevated temperatures.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    S.M. Wiederhom and L.H. Bolz, “Stress Corrosion and Static Fatigue of Glass; J. Am. Ceram. Soc., 53 (1970) 543–48CrossRefGoogle Scholar
  2. [2]
    E.J. Minford, D.M. Kupp, and R.E. Tressler, “Static Fatigue Limit for Sintered Silicon Carbide at Elevated Temperatures”, J. Am. Ceram. Soc., 66 (1983) 769–73CrossRefGoogle Scholar
  3. [3]
    R.F. Cook,“ Crack Propagation Thresholds: A Measure of Surface Energy; J. Mater. Res., 1 (1986) 852–60CrossRefGoogle Scholar
  4. [4]
    T. Fett, D. Munz, and K. Keller, “Determination of Subcritical Crack Growth on Glass in Water from Lifetime Measurements on Knoop-Cracked Specimens; J. Mater. Sci., 23 (1988) 798–803CrossRefGoogle Scholar
  5. [5]
    J.H. Gong and Z.D. Guan, “Effect of Residual Stress due to Knoop Indentation on Subcritical Crack Growth Behavior in Ceramics”; presented at Conference on Fracture Mechanics of Ceramics (Nagoya, Japan, 1991)Google Scholar
  6. [6]
    D.B. Marshall and B.R. Lawn, “Residual Stress Effects in Sharp Contact Cracking: Part I.Indentation Fracture Mechanics; J. Mater. Sci., 14 (1979) 2001–12CrossRefGoogle Scholar
  7. [7]
    J.J. Petrovic, “Effect of Indenter Geometry on Controlled-Surface-Flaw Fracture Toughness,” J. Am. Ceram. Soc., 66 (1983) 277–83CrossRefGoogle Scholar
  8. [8]
    J.H. Gong and Z.D. Guan, “A Modified Indented Bending Beam Method for the Determination of Fracture Toughness of Ceramics,” J. Chinese Ceram. Soc., 19 (1991) 234–41Google Scholar
  9. [9]
    Z.D. Guan, J.H. Gong, Y.Y. Zhao and X.F. Zhao, “The Characteristic Stress Between Two Kinds of Delayed Failure for Ceramics at Elevated Temperature”; this volume (B84).Google Scholar
  10. [10]
    B.J. Hockey; pp.637–58 in Fracture Mechanics of Ceramics, Vol. 5. Edited by R.C. Bradt, A.G. Evans, D.P.H. Hasselman, and F.F. Lange. Plenum, New York, 1983Google Scholar
  11. [11]
    D.B. Marshall, “Controlled Flaws in Ceramics: A Comparison of Knoop and Vickers Indentation,” J. Am. Ceram. Soc., 66 (1983) 127–31CrossRefGoogle Scholar

Copyright information

© Elsevier Science Publishers Ltd and MPA Stuttgart 1992

Authors and Affiliations

  • J. H. Gong
    • 1
  • Z. D. Guan
    • 1
  1. 1.Department of Materials Science and EngineeringTsinghua UniversityBeijingP. R. China

Personalised recommendations