Microstructure and Mechanical Properties of Sintered Reaction Bonded Silicon Nitride (SRBSN)

  • M. Herrmann
  • S. Kessler
  • Ch. Taut
  • G. A. Gogotsi
  • V. P. Zavada
Chapter

Abstract

The distribution of grain size and aspect ratio of the β — Si3N4-grains in SRBSN were estimated. These microstructural parameters and the amount of glassy phase were correlated with mechanical properties of the materials at room and high temperatures.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    G. Ziegler, J. Heinrich, G. Wotting, Rev. Relationships Between Processing, Microstructure and Properties of Dense and Reaction Bonded Silicon Nitride, J. Mat. Sci., 22, (1987), 304CrossRefGoogle Scholar
  2. 2.
    M. Herrmann, Chr. Schubert, P. Obenaus, W. Kreher, S. Hess, W. Hermel in: Technische keramische Werkstoffe Editor: J. Kriegesmann, DWD, Koln, (1989), 5.1.2.1Google Scholar
  3. 3.
    P. Obenaus, M. Herrmann, Methode zur quantitativen Charakterisierung von Stengelkristalliten in Siliciumnitridkeramik, Praktische Metallographie, 27, (1990), 503Google Scholar
  4. 4.
    G. Gogotsy L. Grushevsky V. P. Zavada, Attestaziya Kera-miki po mechanicheskim svoistvam, Oqneupory, 9, (1988), 33Google Scholar
  5. 5.
    G. A. Gogotsy, Deformation behaviour of ceramics, Journ. of the Eur. Cer. Soc., in pressGoogle Scholar
  6. 6.
    P. L. Swanson, C. J. Fairbanks B. R. Lawn at al J. Am. Ceram. Soc., 70, (1987), 279CrossRefGoogle Scholar

Copyright information

© Elsevier Science Publishers Ltd and MPA Stuttgart 1992

Authors and Affiliations

  • M. Herrmann
    • 1
  • S. Kessler
    • 1
  • Ch. Taut
    • 1
  • G. A. Gogotsi
    • 2
  • V. P. Zavada
    • 2
  1. 1.Institute of Ceramic Technology and Materials Science in the Central Institute of Solid-State Physics and Materials ResearchDresdenGermany
  2. 2.Institute of Problems of StrengthKievUSSR

Personalised recommendations