Dislocation loops in quenched aluminium and gold

  • J. Silcox

Abstract

When pure metals are rapidly cooled from temperatures near their melting points, considerable numbers of vacant lattice sites in excess of the equilibrium concentrations may be quenched in. Attempts have therefore been made to interpret the changes in physical properties which arise as the result of quenching, as being due largely to the influence of vacancies. Thus the increase in yield stress (1) has been interpreted in terms of the jogging of dislocation lines already in the crystal (2), the creation of small dislocation loops or stacking faults by the disc-like condensation of the vacancies (3, 4) and the formation of cavities on the dislocations (5). The annealing of electrical resistivity (6) has also been interpreted on the second model (4).
Fig. 1.

A micrograph of a specimen of aluminium quenched from ~ 600° C into iced brine showing a distribution of dislocation loops. The large loops X are thought to arise from the smaller loops by a process of coalescence by slip. The complicated configurations of the dislocations other than loops suggest that climb has taken place

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    Maddin, R., and A. H. Cottrell: Philosophic. Mag. 46, 735 (1955).Google Scholar
  2. 2.
    Cottrell, A. H.: Institute of metals monograph and report series N. 23, 1 (1957).MathSciNetGoogle Scholar
  3. 3.
    Kuhlmaxx-Wusdorf, D.: Philosophic. Mag. 3, 125 (1958).ADSCrossRefGoogle Scholar
  4. 4.
    Kimura, H., R. Maddin and D. Kuhlmann-Wilsdorf: Acta metall (a) 7,145.CrossRefGoogle Scholar
  5. 4.
    Kimura, H., R. Maddin and D. Kuhlmann-Wilsdorf: Acta metall (b) 7, 154 (1958).CrossRefGoogle Scholar
  6. 5.
    Coulomb, P., and J. Friedel: Report of Lake Placid Conference on Dislocations and Mechanical Properties of Crystals. p. 555. New York: Wiley 1957.Google Scholar
  7. 6.
    Bauerle, J. E., and J. S. Koehler: Physic. Rev. 107, 1493 (1957).ADSCrossRefGoogle Scholar
  8. 7.
    Hirsch, P. B., J. Silcox, R. E. Smallman and K. H. Westmacott: Philosophic. Mag. 3, 897 (1958)ADSCrossRefGoogle Scholar
  9. 8.
    Whelan, M. J., and P. B. Hirsch: I. Philosophic. Mag. 2,1121 (1957).ADSCrossRefGoogle Scholar
  10. 8.
    Whelan, M. J., and P. B. Hirsch: II. Philosophic. Mag. 2, 1303 (1957).ADSCrossRefGoogle Scholar
  11. 9.
    Wintenberger, M.: C. R. Acad. Sci. (Paris) 242, 128 (1956).Google Scholar
  12. 9.
    Wintenberger, M.: Rev. Métall. 54, 942 (1957).Google Scholar
  13. 10.
    Bradshaw, F. J., and S. Pearson: Philosophic. Mag. 2, 570 (1957).ADSCrossRefGoogle Scholar
  14. 11.
    Murphy-Tomlinson, H., reported by M. J. Whelan: Electron optical transmission studies of metals. p. 307. Ph. D. Dissertation, University of Cambridge 1958.Google Scholar
  15. 12.
    Silcox, J., and P. B. Hirsch: Direct observation of defects in quenched gold. Philosophic. Mag. 4, 72 (1958)ADSCrossRefGoogle Scholar
  16. 13.
    Thompson, N.: Proc. phys. Soc. 66 B, 481 (1953).ADSCrossRefGoogle Scholar

Copyright information

© Springer-Verlag Berlin Heidelberg 1960

Authors and Affiliations

  • J. Silcox
    • 1
  1. 1.Cavendish LaboratoryUniversity of CambridgeEngland

Personalised recommendations