Study on Rheology, Crystallinity and Electrical Resistance of Poly(Lactic Acid)/Graphene Oxide Nanocomposites

  • Fatemeh Farhanmoghaddam
  • Azizeh JavadiEmail author
Conference paper
  • 44 Downloads

Abstract

Poly(lactic acid) (PLA)/graphene oxide (GO) nanocomposites containing 0.5 wt% to 2 wt% GO were prepared via solution mixing and the crystallinity, rheological and electrical properties of them were studied. It was found that the incorporation of GO leads to improve the storage modulus, loss modulus, and complex viscosity of the nanocomposite samples significantly. Also differential scanning calorimetry (DSC) results indicated that GO is an effective nucleating agent for PLA and could increase its crystallinity and decrease the crystallinity temperature. Also it was resulted that by introducing the GO in PLA matrix, the electrical resistance of samples are decreased, especially at low frequencies.

Keywords

Nanocomposite Poly(lactic acid) Graphene oxide Biodegradable Electrical resistance 

References

  1. 1.
    Gao, Y., Picot, O.T., Bilottz, E., Peijs, T.: Eur. Polym. 86, 117–131 (2017)CrossRefGoogle Scholar
  2. 2.
    Pinto, A.M., Gonçalves, C., Gonçalves, I.C., Magalhaes, F.D.: Eur. Polym. 85, 431–444 (2016)CrossRefGoogle Scholar
  3. 3.
    Tai, R.K., Hao, Y.M., Da, J.F., Xin, J., Bin, Y.C., Wen, J.M.: Ind. Eng. Chem. Res. 54, 758–768 (2015)CrossRefGoogle Scholar
  4. 4.
    Corre, Y.M., Maazouz, A., Duchet, J., Reignier, J.: J. Supercrit. Fluid 58(1), 177–188 (2011)CrossRefGoogle Scholar

Copyright information

© Springer Nature Switzerland AG 2020

Authors and Affiliations

  1. 1.Department of Polymer Engineering and Color TechnologyAmirkabir University of Technology (Tehran Polytechnic)TehranIran

Personalised recommendations