Experimental Study of Defects and Mechanical Properties During Under-Water Friction Stir Welding of Al6061-6063 Alloys

  • Rahul B. Dhabale
  • Vijaykumar S. Jatti
Conference paper

Abstract

In this study, welding samples were attributed with reduced welding defects such as a tunnel, onion ring, exit pinhole, surface flash and micro-voids with improved mechanical strength through underwater friction stir welding. Two dissimilar aluminum alloys with different mechanical properties were successfully joined by using direct application of groundwater during friction stir welding. Taguchi method was used to design the experimental runs and identify optimal process parameters setting. After the welding process, the samples were cut into the desired size as required for tensile test and hardness test. Scanning electron microscopy was used to understand grain behavior at weld nugget zone after the tensile test. Fewer defects as well as improved mechanical strength with minimum spindle speed i.e.1000 rpm and welding speed 16 & 20 mm/min were observed. Minimum spindle speed leads to reduce power consumption. Fine equiaxed grains were also observed.

Keywords

Dissimilar Aluminium Alloy Taguchi Method Underwater friction stir welding Tunnel defect Onion ring Pinhole 

References

  1. 1.
    Omar Salih S, Ou H, Sun W, McCartney DG (2015) A review of friction stir welding of aluminium matrix composites. Mater Des 86:61–71CrossRefGoogle Scholar
  2. 2.
    Shah PH, Badheka V (2016) An experimental investigation of temperature distribution and joint properties of Al 7075 T651 friction stir welded aluminium alloys. Procedia Technol 23:543–550CrossRefGoogle Scholar
  3. 3.
    Yoo J, Yoon J, Min K, Lee H (2015) Effect of friction stir welding process parameters on mechanical properties and macro structure of Al-Li alloy. Procedia Manuf 2:325–330CrossRefGoogle Scholar
  4. 4.
    Tan S, Zheng F, Chen J, Han J, Wu Y, Peng L (2017) Effects of process parameters on microstructure and mechanical properties of friction stir lap linear welded 6061 aluminum alloy to NZ30K magnesium alloy. J Magnesium Alloys 5(1):56–63CrossRefGoogle Scholar
  5. 5.
    Sharma HK, Bhatt K, Shah K, Joshi U (2016) Experimental analysis of friction stir welding of dissimilar alloys AA6061 and Mg AZ31 using circular butt joint geometry. Procedia Technol 23:566–572CrossRefGoogle Scholar
  6. 6.
    Ugender S, Kumar A, Reddy AS (2014) Experimental investigation of tool geometry on mechanical properties of friction stir welding of AA 2014 aluminium alloy. Procedia Mater Sci 5:824–831CrossRefGoogle Scholar
  7. 7.
    Lee H, Yoon J, Yoo J, No K (2016) Friction stir welding process of aluminum-lithium alloy 2195. Procedia Eng 149:62–66CrossRefGoogle Scholar
  8. 8.
    Shen Z, Chen Y, Haghshenas M, Gerlich AP (2015) Role of welding parameters on interfacial bonding in dissimilar steel/aluminum friction stir welds. Int J Eng Sci Technol 18:270–277CrossRefGoogle Scholar
  9. 9.
    Casalino G, Campanelli S, Mortello M (2014) Influence of shoulder geometry and coating of the tool on the friction stir welding of aluminium alloy plates. Procedia Eng 69:1541–1548CrossRefGoogle Scholar
  10. 10.
    Liu XC, Sun YF, Fujii H (2017) Clarification of microstructure evolution of aluminum during friction stir welding using liquid CO2 rapid cooling. Mater Des 129:151–163CrossRefGoogle Scholar
  11. 11.
    Joints S, Sabari S, Malarvizhi S, Balasubramanian V (2016) Influences of tool traverse speed on tensile properties of air cooled and water cooled friction stir Welded AA2519-T87 aluminium alloy joints. J Mater Process Technol 237:286–300CrossRefGoogle Scholar
  12. 12.
    Sabari S, Malarvizhi S, Balasubramanian V, Reddy GM (2016) Experimental and numerical investigation on under-water friction stir welding of armour Grade AA2519-T87 aluminium alloy. Def Technol 12(2016):324–333CrossRefGoogle Scholar
  13. 13.
    Rathod P, Aravindan S, Rao PV (2016) Performance evaluation of novel micro-textured tools in improving the machinability of aluminum alloy (Al 6063). Procedia Technol 23:296–303CrossRefGoogle Scholar

Copyright information

© Springer Nature Switzerland AG 2020

Authors and Affiliations

  • Rahul B. Dhabale
    • 1
  • Vijaykumar S. Jatti
    • 2
  1. 1.Department of Mechanical Engineering, Symbiosis Institute of Technology (SIT)Symbiosis International University (SIU)PuneIndia
  2. 2.Department of Mechanical Engineering, D Y Patil College of EngineeringSavitribai Phule Pune University (SPPU)Akurdi, PuneIndia

Personalised recommendations