Wettability Behavior of Si/C and Si–Sn Alloy/C System

  • Yaqiong Li
  • Lifeng ZhangEmail author
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

During the Si growth process in the zone melting directional solidification experiment, the wettability behavior of Si source/solvent metal and solvent metal/seed substrate is an important issue for Si purification and growth. In this work, the wettability behavior of Si/C and Si-90 wt% Sn alloy/C system was studied by using the sessile drop method. The results show that Si and Si–Sn alloy wet C substrate, and the wettability gradually improves with the holding time due to the generation of a SiC layer in the metal/C interface and the infiltration Si or Si–Sn alloy into C substrate. Moreover, the addition of Sn into Si melt is beneficial for Si to wet C substrate, because Sn hinders the generation of SiC and Si promotes Sn wetting C substrate.

Keywords

Wettability Si Si–Sn alloy C substrate 

Notes

Acknowledgements

The authors are grateful for support from the National Science Foundation China (Grant No. 51334002, No. 51604023), Beijing Key Laboratory of Green Recycling and Extraction of Metals (GREM), the Laboratory of Green Process Metallurgy and Modeling (GPM2) and the High Quality steel Consortium (HQSC) at the School of Metallurgical and Ecological Engineering at University of Science and Technology Beijing (USTB).

References

  1. 1.
    Díaz AC (2014) Energy life cycle assessment (LCA) of silicon-based photovoltaic technologies and the influence of where it is manufactured and installed. Ph.D. thesis, University of BacelonaGoogle Scholar
  2. 2.
    Louwen A, Van Sark W, Schropp R, Faaij A (2016) A cost roadmap for silicon heterojunction solar cells. Sol Energy Mater Sol Cells 147:295–314CrossRefGoogle Scholar
  3. 3.
    Ohshima Y, Yoshikawa T, Morita K (2011) Effect of solidification conditions on Si growth from Si–Cu melts. Supplemental Proc Mate Processing Energy Mater 1:677–684CrossRefGoogle Scholar
  4. 4.
    Obinata I, Komatsu N (1957) Method of refining silicon by alloying. Science Reports of the Research Institutes, Tohoku University. Ser. A, Phys Chem Metal. A-9:118–130Google Scholar
  5. 5.
    Xiaodong M, Lei Y, Yoshikawa T, Zhao B, Morita K (2015) Effect of solidification conditions on the silicon growth and refining using Si–Sn melt. J Cryst Growth 430:98–102CrossRefGoogle Scholar
  6. 6.
    Xiaodong M, Yoshikawa T, Morita K (2013) Si growth by directional solidification of Si–Sn alloys to produce solar-grade Si. J Cryst Growth 377:192–196CrossRefGoogle Scholar
  7. 7.
    Nishi Y, Kang Y, Morita K (2010) Control of Si crystal growth during solidification of Si–Al melt. Mater Trans 51(7):1227–1230CrossRefGoogle Scholar
  8. 8.
    Li Y, Li J, Tan Y, Zhang L, Kazuki M (2016) Directional growth of bulk silicon from Si–Al–Sn melts. J Inorganic Mater 31(8):791–796CrossRefGoogle Scholar
  9. 9.
    Zhang L, Ma Y, Li Y (2017) Preparing crystalline silicon from Si–Sn solvent by zone melting directional solidification method. Mater Sci Semicond Process 71:12–19CrossRefGoogle Scholar
  10. 10.
    Ciftja A, Engh TA, Tangstad M (2010) Wetting properties of molten silicon with graphite materials. Metal Mater Trans A. 41(12):3183–3195CrossRefGoogle Scholar
  11. 11.
    Yuan Z, Huang W, Mukai K (2004) Wettability and reactivity of molten silicon with various substrates. Appl Phys A Mater Sci Process 78(4):617–622CrossRefGoogle Scholar
  12. 12.
    Liu G, Muolo M, Valenza F, Passerone A (2010) Survey on wetting of SiC by molten metals. Ceram Int 36(4):1177–1188CrossRefGoogle Scholar
  13. 13.
    Benouahmane Z, Zhang L, Li Y (2017) Influence of oxygen content on the wettability of silicon on graphite. In: Energy Technology 2017. Springer International Publishing, pp 395–401Google Scholar
  14. 14.
    Li J, Hausner H (1991) Wettability of silicon carbide by gold, germanium and silicon. J Mater Sci Lett 10(21):1275–1276CrossRefGoogle Scholar
  15. 15.
    Li Y, Zhang L, Benouahmane Z (2016) Effect of oxidation on wetting behavior between silicon and silicon carbide. In: 7th international symposium on high-temperature metallurgical processing. Springer. pp 237–242Google Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  1. 1.School of Metallurgical and Ecological EngineeringUniversity of Science and Technology Beijing (USTB)BeijingChina
  2. 2.Beijing Key Laboratory of Green Recycling and Extraction of MetalUniversity of Science and Technology BeijingBeijingChina

Personalised recommendations