Investigation on Clogging of Submerged Entry Nozzles for GCr15 Bearing Steels

  • Gong Cheng
  • Lifeng ZhangEmail author
  • Wenbo Wang
  • Qiangqiang Wang
  • Piotr Roman Scheller
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

Clogging of submerged entry nozzles for GCr15 bearing steels has been investigated by industrial experiments coupled with mathematical simulations. It was found that clogs on the submerged entry nozzle with four ports were mainly CaO-MgO-Al2O3 inclusions with the size of 2–6 μm, which cannot be avoided by removal of inclusions from the liquid steel. Cathodoluminescence microscopy was also applied for the characterisation of submerged entry nozzle clogging. Mathematical simulations were carried out to predict the main clogging location at the submerged entry nozzle with different types. The results showed that the percentage of inclusions entrapped on the cylindrical submerged entry nozzle and four-port one was 39.7 and 46.5%, respectively. It indicated that the cylindrical submerged entry nozzle helped reduce the probability of submerged entry nozzle clogging and was beneficial for the improvement of the fatigue property of bearing steels.

Keywords

Inclusion Clogging Mathematical simulation 

Notes

Acknowledgements

The authors are grateful for support from the National Science Foundation China (Grant No. U1860206), the Fundamental Research Funds for the Central Universities (Grant No. FRF-TP-15-001C2), Beijing Key Laboratory of Green Recycling and Extraction of Metals (GREM) and the High-quality Steel Consortium (HQSC) at the School of Metallurgical and Ecological Engineering at University of Science and Technology Beijing (USTB), China.

References

  1. 1.
    Zhang L, Thomas B (2003) State of the art in evaluation and control of steel cleanliness. Trans Iron Steel Inst Jpn 43(3):271–291CrossRefGoogle Scholar
  2. 2.
    Zhang L (2006) Indirect methods of detecting and evaluating inclusions in steel—a review. J Iron Steel Res (Int) 13(4):1–8CrossRefGoogle Scholar
  3. 3.
    Park J, Todoroki H (2010) Control of MgO·Al2O3 spinel inclusions in stainless steels. ISIJ Int 50(10):1333–1346CrossRefGoogle Scholar
  4. 4.
    Zhang L (2013) Nucleation, growth, transport, and entrapment of inclusions during steel casting. JOM 65(9):1138–1144CrossRefGoogle Scholar
  5. 5.
    Zhang L, Thomas B (2006) State of the art in the control of inclusions during steel ingot casting. Metall Mater Trans B 37(5):733–761CrossRefGoogle Scholar
  6. 6.
    Zhang L, Wang Y, Zuo X (2008) Flow transport and inclusion motion in steel continuous-casting mold under submerged entry nozzle clogging condition. Metall Mater Trans B 39(4):534–550CrossRefGoogle Scholar
  7. 7.
    Xie W, Bao Y, Wang M, Zhang X (2015) Relationship between high frequency defect detection and inclusions in GCr15 Bearing Steel. Iron Steel 50(3):44–48Google Scholar
  8. 8.
    Andersson M, Appelberg J, Tilliander A, Nakajima K, Shibata H, Kitamura S, Jonsson L (2006) Some aspects on grain refining additions with focus on clogging during casting. ISIJ Int 46(6):814–823CrossRefGoogle Scholar
  9. 9.
    Pielet H, Bhattacharya D (1984) Thermodynamics of nozzle blockage in continuous casting of calcium-containing steels. Metall Trans B 15(4):743CrossRefGoogle Scholar
  10. 10.
    Szekely J, Dinovo S (1974) Thermal criteria for tundish nozzle or taphole blockage. Metall Trans 5(3):747–754CrossRefGoogle Scholar
  11. 11.
    Verma N, Pistorius P, Fruehan R, Potter M, Lind M, Story S (2011) Transient inclusion evolution during modification of alumina inclusions by calcium in liquid steel: part I. Background, experimental techniques and analysis methods. Metall Mater Trans B 42(4):711–719CrossRefGoogle Scholar
  12. 12.
    Yang S, Wang Q, Zhang L, Li J, Peaslee K (2012) Formation and modification of MgO·Al2O3—based inclusions in alloy steels. Metall Mater Trans B 43(4):731–750CrossRefGoogle Scholar
  13. 13.
    Ren Y, Zhang L, Li S (2015) Transient evolution of inclusions during calcium modification in linepipe steels. ISIJ Int 54(12):2772–2779CrossRefGoogle Scholar
  14. 14.
    Yang G, Wang X, Huang F, Yang D, Wei P, Hao X (2015) Influence of calcium addition on inclusions in LCAK steel with ultralow sulfur content. Metall Mater Trans B 46(1):145–154CrossRefGoogle Scholar
  15. 15.
    Zhao D, Li H, Bao C, Yang J (2015) Inclusion evolution during modification of alumina inclusions by calcium in liquid steel and deformation during hot rolling process. Trans Iron Steel Inst Jpn 55(10):2115–2124CrossRefGoogle Scholar
  16. 16.
    Ogino K, Nogi K, Yamase O (1983) Effects of selenium and tellurium on the surface tension of molten iron and the wettability of alumina by molten iron. ISIJ Int 23(3):234–239CrossRefGoogle Scholar
  17. 17.
    Cramb A, Jimbo I (1989) Calculation of the interfacial properties of liquid steel-slag systems. Steel Res 60(3):157–165CrossRefGoogle Scholar
  18. 18.
    Zouvelou N, Mantzouris X, Nikolopoulos P (2007) Interfacial energies in oxide/liquid metal systems with limited solubility. Int J Adhes Adhes 27(5):380–386CrossRefGoogle Scholar
  19. 19.
    Ruan G, Li N (2005) Local corrosion mechanism of refractory at slag-iron(steel)interface. Mater Rev 19(2):47–49Google Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  • Gong Cheng
    • 1
    • 2
  • Lifeng Zhang
    • 1
    • 2
    Email author
  • Wenbo Wang
    • 1
    • 2
  • Qiangqiang Wang
    • 3
  • Piotr Roman Scheller
    • 1
  1. 1.School of Metallurgical and Ecological EngineeringUniversity of Science and Technology Beijing (USTB)BeijingChina
  2. 2.Beijing Key Laboratory of Green Recycling and Extraction of MetalUniversity of Science &Technology BeijingBeijingChina
  3. 3.College of Materials Science and EngineeringChongqing UniversityChongqingChina

Personalised recommendations