Effects of Cr2O3, FeO and CaO/SiO2 Ratio on the Apparent Viscosity of CaO-SiO2-MgO-MnO-FeO-Cr2O3 Slags

  • Bing Huang
  • Mingmei ZhuEmail author
  • Yong Zhong
  • Aiping Zhang
  • Tiancheng Lin
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

In this study, the effects of Cr2O3, FeO and CaO/SiO2 ratio on the apparent viscosity of the CaO-SiO2-MgO-MnO-FeO-Cr2O3 slags are investigated at 1500 °C. Apparent viscosity of the slags is measured using the rotating cylinder method and the liquid and solid phases are calculated using the thermodynamic calculation software FactSage. The experimental results showed that the apparent viscosity of slags increases with increasing CaO/SiO2 ratio and Cr2O3 content and decreases with the FeO addition. The thermodynamic calculations results showed that Cr2O3 content has a minor effect on the mass fraction of liquid phases, nevertheless it can promote the formation of spinels resulting in increased amount of solid phases as well as, increased slag apparent viscosity. The liquid slag phases were increased with increasing of FeO content therefore, the apparent viscosity of the slag was reduced. However, the liquid slag phases were decreased with increasing of CaO/SiO2 ratio, which resulted in increased slag apparent viscosity.

Keywords

Steelmaking slag bearing chromium Apparent viscosity High-temperature experiment Thermodynamic calculation 

References

  1. 1.
    Huang XH (2014) Iron and steel metallurgy principle, 4th ed. Metallurgical industry press, metallurgical industry press, Beijing, p 316Google Scholar
  2. 2.
    Ostrovski OI, Utochkin YI, Pavlov AV, et al (2007) Viscosity of the CaO-CaF2 system containing chromium oxide. ISIJ Int, 34(9):773–775CrossRefGoogle Scholar
  3. 3.
    Xu C, Wang W, Zhou L, Xie S, Zhang C (2015) The effects of Cr2O3 on the melting, viscosity, heat transfer, and crystallization behaviors of mold flux used for the casting of Cr-bearing alloy steels. Metall Mater Trans B 46(2):882–892CrossRefGoogle Scholar
  4. 4.
    Qiu G, Chen L, Zhu J et al (2015) Effect of Cr2O3 addition on viscosity and structure of ti-bearing Blast Furnace slag. ISIJ Int 55(7):1367–1376CrossRefGoogle Scholar
  5. 5.
    Huang WJ, Zhao YH, et al (2016) Viscosity property and structure analysis of FeO-SiO2-V2O3-TiO2-Cr2O3 slags. ISIJ Int 56(4):594–601Google Scholar
  6. 6.
    Xu R, Zhang J, Fan X et al (2017) Effect of MnO on high-alumina slag viscosity and corrosion behavior of refractory in slags. ISIJ Int 57(11):1887–1894CrossRefGoogle Scholar
  7. 7.
    Li Q, Gao J, Zhang Y et al (2017) Viscosity measurement and structure analysis of Cr2O3-bearing CaO-SiO2-MgO-Al2O3 slags. Metall Mater Trans B 48(1):346–356CrossRefGoogle Scholar
  8. 8.
    Li Q, Yang S, Zhang Y et al (2017) Effects of MgO, Na2O, and B2O3 on the viscosity and structure of Cr2O3-bearing CaO-SiO2-Al2O3 slags. ISIJ Int 57(4):689–696CrossRefGoogle Scholar
  9. 9.
    Chen M, Raghunath S et al (2013) Viscosity measurements of “FeO”-SiO2 Slag in equilibrium with metallic Fe. Metall Mater Trans B, 44(3):506–515CrossRefGoogle Scholar
  10. 10.
    Seong SH, Sungmo J, Youngseok L, et al (2007) Viscosity of highly basic slags. ISIJ Int, 47(8):1090–1096 Google Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  • Bing Huang
    • 1
  • Mingmei Zhu
    • 1
    Email author
  • Yong Zhong
    • 1
  • Aiping Zhang
    • 1
  • Tiancheng Lin
    • 1
  1. 1.College of Materials Science and EngineeringChongqing UniversityChongqingChina

Personalised recommendations