Influence of Cr2O3 and Basicity on Viscosity of Ti-Bearing Blast Furnace Slag

  • Guibao QiuEmail author
  • Jian Wang
  • Shiyuan Liu
  • Qingjuan Li
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)

Abstract

The influence of Cr2O3 and basicity on the viscosity of CaO–SiO2-15 wt% Al2O3-9 wt% MgO-22 wt% TiO2–Cr2O3 slag was investigated in the temperature range of 1673–1773 K. The viscosity decreased with increasing basicity at fixed content of Cr2O3 due to the depolymerization of silicon structure. At a fixed content of basicity, the viscosity decreased with increasing Cr2O3 when the mass percentage of Cr2O3 was below 1%. Different models were also used to predict the effect of Cr2O3 on the viscosity of blast furnace slag, and the results show that the optical basicity model agrees well with the experimental values. With the initial addition of Cr2O3 content, the slag melting temperature increased from 1660 to 1673 K. When the basicity increased from 1.0 to 1.2, the slag melting temperature increased from 1655 to 1720 K.

Keywords

Viscosity Cr2O3 Basicity Ti-bearing slag 

Notes

Acknowledgements

The work described in this paper was supported by a grant from the Natural Science Foundation of China (Project no. 51674055).

References

  1. 1.
    Yang Y (2014) Northeastern UniversityGoogle Scholar
  2. 2.
    Deng J, Xue X, Liu G (2007) J Mater Metall 6:83–86Google Scholar
  3. 3.
    Peng B, Wu G, Dai B, Zhang P, Zhang L (2012) Metal materials and metallurgical engineering, pp 18–21Google Scholar
  4. 4.
    Zhang YZ, Yan MS, Xiang L, Yin JC, Tao W (2005) J Mater Metall 253–255Google Scholar
  5. 5.
    Sunahara K, Nakano K, Hoshi M, Inada T, Komatsu S, Yamamoto T (2008) ISIJ Int 48:420–429CrossRefGoogle Scholar
  6. 6.
    Banya S (1988) Iron and steel institute of Japan, Tokyo, vol 4Google Scholar
  7. 7.
    Fang L, Guofan Z (2006) Henan Metall 14:11–13Google Scholar
  8. 8.
    Park JH, Min DJ, SH S (2004) Metall Mater Trans B 35:269–275Google Scholar
  9. 9.
    Ohno A,. Ross HU (1963) Canadian metallurgical quarterly, pp 259–279(221)Google Scholar
  10. 10.
    Saito N, Hori N, Nakashima K, Mori K (2003) Metall Mater Trans B 34:509–516CrossRefGoogle Scholar
  11. 11.
    Xu RZ, Zhang JL, Wang ZY, Jiao KX (2017) Steel Res Int 88Google Scholar
  12. 12.
    Qiu G, Chen L, Zhu J, Lv X, Bai C (2015) Trans Iron Steel Inst Jpn 55:1367–1376CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  • Guibao Qiu
    • 1
    Email author
  • Jian Wang
    • 1
  • Shiyuan Liu
    • 1
  • Qingjuan Li
    • 1
  1. 1.College of Materials Science & Engineering, Chongqing UniversityChongqingChina

Personalised recommendations