Fundamentals of Spark Plasma Sintering (SPS): An Ideal Processing Technique for Fabrication of Metal Matrix Nanocomposites

  • N. Sharma
  • S. N. Alam
  • B. C. Ray
Chapter

Abstract

The pioneering work related to the spark plasma sintering (SPS) technique, also known as pulsed electric current sintering (PECS), started in around 1906 when the first direct current (DC) resistance sintering (RS) apparatus was developed. Later, a similar process was developed and patented in the 1960s. The present-day SPS which is now widely used for sintering metals and ceramics was introduced by the Sumitomo Coal Mining Co., Ltd. of Japan in 1990. Since then this technique which is based on the idea of using plasma generated by an electric discharge machine for sintering has attracted immense attention in the area of powder technology and development of the composites. The SPS process can be considered as a modified hot pressing process where a pulsed electric current is passed through a graphite die and the specimen is heated by the Joule heat transferred from the pressing die. In SPS, the compaction and sintering stages are combined in a single operation. Due to the pulsed electric current and the spark plasma effect, the SPS process is capable of introducing simultaneous rapid heating and cooling rates; accompanied with high pressure, this process can realize nearly full densification at a relatively lower temperature, within a very short time. In the past, materials were confined only to the monolithic form, but for better physical, chemical and tribological properties, composite materials have evolved. Metal matrix nanocomposites (MMNCs) have evoked keen interest in recent times because of their excellent structural and functional properties and have the potential to replace the existing materials in a wide range of applications. MMNCs refer to materials where rigid nanosized reinforcements, typically having size <100 nm, are embedded in ductile metals or alloys which act as the matrices providing attractive physical and mechanical properties such as high specific modulus, strength-to-weight ratio, fatigue strength, temperature stability and wear resistance. The properties of the MMNCs can be designed and custom-made as per the requirement of the application. MMNCs received much attraction as compared to the metal matrix composites (MMCs) due to the size and strength of the nanometric reinforcements. Apart from the nanofillers, a fine grain size of the matrix could also contribute to the improvement in the properties of the composites. As conventional processing techniques require a long holding time at high sintering temperatures, which can damage the structure of the nanofillers, processes like the SPS are the ideal routes for development of such composites. Also during conventional sintering, abnormal grain coarsening becomes particularly severe which in turn implies that achieving a very high level of densification and maintaining a fine grain size is very difficult. Attaining a uniform dispersion of the nanofillers in the composites is not easy using liquid-processing techniques due to the difference in the densities of the nanofiller, and the matrix and the non-wettability at the interface between them lead to a heterogeneous structure that affects the overall properties of the nanocomposites. By SPS, prevention or reduction in grain growth, to maintain the nanostructure of the matrix, is possible through careful control of consolidation parameters, particularly heating rate, sintering temperature and time. Due to the short period of sintering, grain growth can be restricted, and materials having submicron-sized or nanosized microstructures having enhanced properties can be developed. As the SPS technique requires very short sintering time, it is ideally suited for the development of nanocomposites reinforced with carbonaceous nanofillers like graphene or its derivatives and carbon nanotubes (CNTs), as short sintering time is essential for preserving their structural integrity and intrinsic properties. A wide variety of materials like metals and alloys, ceramics, composites, cermets etc. can be successfully developed by the SPS process. However, it should be noted that although SPS presents many advantages as compared to other conventional sintering techniques, it also has a few limitations. One of the major drawbacks of the SPS process is the heterogeneity of temperature field during the temperature cycle, resulting in heterogeneous microstructures in the sintered samples. Also, SPS allows only simple symmetrical shapes and is expensive as it requires a pulsed DC generator. The focus of this chapter will be on the fundamentals of the SPS technique, the kinetics of densification and grain growth during SPS and how the SPS technique could be effectively used to develop metal matrix nanocomposites (MMNCs). The chapter provides a detailed overview of the SPS process, the current state of research in the area of MMNCs developed by the SPS and its future.

Keywords

Spark plasma sintering (SPS) Metal matrix nanocomposites (MMNC) Carbon nanotubes (CNT) Graphene Al-based MMNCs 

Notes

Acknowledgement

We gratefully acknowledge the support provided by the XRD, SEM laboratories of Metallurgical and Materials Engineering Department and FESEM and Thermal analysis laboratory, Ceramic Engineering Department, NIT Rourkela. We also thank the Physics Department and the Central Research Facility, IIT Kharagpur, for their sincere support. The use of SPS facility at IIT Kanpur, procured with partial funding from Department of Science and Technology, Government of India as well as CARE funding from IIT Kanpur, is gratefully acknowledged. We would also like to acknowledge the Advanced Centre for Materials Science (ACMS), IIT Kanpur.

References

  1. Akinrinlola B, Gauvin R, Brochu M (2012) Improving the mechanical reliability of cryomilled Al-Mg alloy using a two-stage spark plasma sintering cycle. Scr Mater 66(7):455–458CrossRefGoogle Scholar
  2. Alam SN, Sharma N, Ray BC, Yadav S, Biswas K (2017) Effect of graphite nanoplatelets on the mechanical properties of alumina-based composites. Ceram Int 43(14):11376–11389CrossRefGoogle Scholar
  3. Al-Qutub AM, Khalil A, Saheb N, Hakeem AS (2013) Wear and friction behavior of Al6061 alloy reinforced with carbon nanotubes. Wear 297(1–2):752–761CrossRefGoogle Scholar
  4. Anderson MP, Grest GS, Doherty RD, Li K, Srolovitz DJ (1989) Inhibition of grain growth by second phase particles: three dimensional Monte Carlo computer simulation. Scr Metall 23:753–758CrossRefGoogle Scholar
  5. Azarniya A, Sovizi S, Boyuk MRRT et al (2017) Physicomechanical properties of spark plasma sintered carbon nanotube-containing ceramic matrix nanocomposites. Nanoscale 9(35):12779–12820CrossRefGoogle Scholar
  6. Boesel RW, Jacobson MI, Yoshioka IS (1969) Spark sintering tames exotic P/M materials. Mater Eng 70:32–35Google Scholar
  7. Casellas D, Nagl MM, Llanes L, Anglada M (2003) Fracture toughness of alumina and ZTA ceramics: microstructural coarsening effects. J Mater Process Technol 143–144:148–152CrossRefGoogle Scholar
  8. Cavaliere P, Sadeghi B, Shabani A (2017) Carbon nanotube reinforced aluminum matrix composites produced by spark plasma sintering. J Mater Sci 52:8618–8629CrossRefGoogle Scholar
  9. Chunfeng D, Xuexi Z, Yanxia M, Dezun W (2007) Fabrication of aluminum matrix composite reinforced with carbon nanotubes. Rare Metals 26(5):450–455CrossRefGoogle Scholar
  10. Clemares IA, Osoro GM, Fernandez A et al (2010) Transparent alumina/ceria nanocomposites by spark plasma sintering. Adv Eng Mater 12(11):1154–1160CrossRefGoogle Scholar
  11. Clyens S, Al-Hassani STS, Johnson W (1976) The compaction of powder metallurgy bars using high voltage electrical discharges. Int J Mech Sci 18(1):37–40CrossRefGoogle Scholar
  12. Conrad H (2002) Thermally activated plastic flow of metals and ceramics with an electric field or current. Mater Sci Eng A 322(1–2):100–107CrossRefGoogle Scholar
  13. Couret A, Molenat G, Galy J, Thomas M (2008) Microstructures and mechanical properties of TiAl alloys consolidated by spark plasma sintering. Intermetallics 16(9):1134–1141CrossRefGoogle Scholar
  14. Cremer GD (1944) Sintering together powders metals such as bronze, brass or aluminum. US Patent No. 2,355,954. https://patents.google.com/patent/US2355954
  15. Dash K, Ray BC, Chaira D (2012) Synthesis and characterization of copper-alumina metal matrix composite by conventional and spark plasma sintering. J Alloys Compd 516:78–84CrossRefGoogle Scholar
  16. Diouf S, Molinari A (2012) Densification mechanisms in spark plasma sintering: effect of particle size and pressure. Powder Technol 221:220–227CrossRefGoogle Scholar
  17. Feest E (1986) A metal matrix composites for industrial application. Mater Des 7(2):58–64CrossRefGoogle Scholar
  18. Feng H, Zhou Y, Jia D, Meng Q (2005) Rapid synthesis of Ti alloy with B addition by spark plasma sintering. Mater Sci Eng A 390(1–2):344–349CrossRefGoogle Scholar
  19. Furuya Y, Watanabe R, Yaguchi H, Saito M, Kubo T, Abe T, Omori M (1998) Preparation of smart composites by SPS. In: Proceedings of the Third Symposium on Spark Plasma Sintering, Kure, pp 42–45Google Scholar
  20. Geguzin YAE, Kaganovsky YUS, Onoprienko AA, Zung FN (1975) Behaviour of metallic granules at the surface of an ionic crystal in an external electric field. Sov Phys Solis State 17(3):457–458Google Scholar
  21. Giuntini D, Olevsky EA, Cardona CG et al (2013) Localized overheating phenomena and optimization of spark-plasma sintering tooling design. Materials 6:2612–2632CrossRefGoogle Scholar
  22. Goldberger WM, Merkle BD (2001) Electroconsolidation offers fast, low-cost densification. Met Powder Rep 56(2):30–33CrossRefGoogle Scholar
  23. Grasso S, Sakka Y, Maizza G (2009) Electric current activated/assisted sintering (ECAS): a review of patents. Sci Technol Adv Mater 10:053001CrossRefGoogle Scholar
  24. Grasso S, Kim EY, Saunders T, Yu M et al (2016) Ultra-rapid crystal growth of textured SiC using flash spark plasma sintering route. Cryst Growth Des 16:2317–2321CrossRefGoogle Scholar
  25. Groza JR (1999) Nanosintering. Nanostruct Mater 12:987–992CrossRefGoogle Scholar
  26. Groza JR, Anderson KR, Fendorf M, Echer CJ (1999) Surface oxide debonding in field assisted powder sintering. Mater Sci Eng A 270(2):278–282CrossRefGoogle Scholar
  27. Guillon O, Julian JG, Dargatz B, Kessel T, Schierning G et al (2014) Field-assisted sintering technology/spark plasma sintering: mechanisms, materials, and technology developments. Adv Eng Mater 16(7):830–849CrossRefGoogle Scholar
  28. Herring C (1950) Effect of change of scale on sintering phenomena. J Appl Phys 21:301–303CrossRefGoogle Scholar
  29. Hiremath A, Hemanth J (2017) Experimental evaluation of the coefficient of thermal expansion of chilled aluminum alloy-borosilicate glass (P) composite. J Mater Environ Sci 8(12):4246–4252Google Scholar
  30. Holland TB, Ovidko IA, Wang H, Mukherjee AK (2010) Elevated temperature deformation behavior of spark plasma sintered nanometric nickel with varied grain size distributions. Mater Sci Eng A 528(2):663–671CrossRefGoogle Scholar
  31. Hughes GD, Smith SD, Pandey CS et al (1986) Hall-petch strengthening for the microhardness of twelve nanometer grain diameter electrodeposited nickel. Scr Metall 20(1):93–97CrossRefGoogle Scholar
  32. Hulbert DM, Anders A, Andersson J, Lavernia EJ, Mukherjee AK (2009) A discussion on the absence of plasma in spark plasma sintering. Scr Matell 60:835–838CrossRefGoogle Scholar
  33. Inoue K (1965) Electric discharge heat treatment of metals in electrolytes. US Patent No. 3,188,245. https://patents.google.com/patent/US3198675
  34. Inoue K (1966) Method of and apparatus for controlling the porosity of electrically sintered bodies. US Patent No. 3241-956. https://patents.google.com/patent/US3317705
  35. Jung H, Gusev VE, Baek H, Wang Y, Diebold GJ (2011) Ludwig-Soret effect in a linear temperature field: theory and experiments for steady state distributions. Phys Lett A 375(19):1917–1920CrossRefGoogle Scholar
  36. Kim KH, Chae JH, Park JS, Ahn JP, Shim KB (2003) Sintering behavior and mechanical properties of B4C ceramics fabricated by spark plasma sintering. Mater Charact 50:31–37CrossRefGoogle Scholar
  37. Kim KT, Cha SI, Hong SH (2006) Microstructures and tensile behavior of carbon nanotube reinforced Cu matrix nanocomposites. Mater Sci Eng A 430(1–2):27–33CrossRefGoogle Scholar
  38. Kodash VY, Groza JR, Cho KC et al (2004) Field-assisted sintering of Ni nanopowders. Mater Sci Eng A 385(1–2):367–371CrossRefGoogle Scholar
  39. Kubota M (2007) Properties of nano-structured pure Al produced by mechanical grinding and spark plasma sintering. J Alloys Compd 434-435:294–297CrossRefGoogle Scholar
  40. Kumar HGP, Xavior MA (2014) Graphene reinforced metal matrix composite (GRMMC): a review. Proc Eng 97:1033–1040CrossRefGoogle Scholar
  41. Libardi S, Leoni M, Facchini L, Incau MD et al (2007) Effect of the dispersion of nanometric silica particles on the thermal stability of a nanostructured iron based powder. Mater Sci Eng A 445–446:244–250CrossRefGoogle Scholar
  42. Lim BS, Kim CJ, Kim BJ (2006) The effects of interfacial bonding on mechanical properties of single-walled carbon nanotube reinforced copper matrix nanocomposites. Nanotechnology 17:5759–5764CrossRefGoogle Scholar
  43. Lukianova OA, Novikov VY, Parkhomenko AA, Sirota VV, Krasilnikov VV (2017) Microstructure of spark plasma-sintered silicon nitride ceramics. Nanoscale Res Lett 12:293–299CrossRefGoogle Scholar
  44. Mamedov V (2002) Spark plasma sintering as advanced PM sintering method. Powder Metall 45:322–328CrossRefGoogle Scholar
  45. Matsugi K, Ishibashi N, Hatayama T, Yanagisawa O (1996) Microstructure of spark sintered titanium-aluminide compacts. Intermetallics 4(6):457–467CrossRefGoogle Scholar
  46. Mayo MJ (1996) Processing of nanocrystalline ceramics from ultrafine particles. Int Mater Rev 41:85–115CrossRefGoogle Scholar
  47. McTaggart FK (1967) Plasma chemistry in electrical discharges. Elsevier Scientific Publishing Company, AmsterdamGoogle Scholar
  48. Munir ZA, Tamburini UA, Ohyanagi M (2006) The effect of electric field and pressure on the synthesis and consolidation of materials: a review of the spark plasma method. J Mater Sci 41:763–777CrossRefGoogle Scholar
  49. Murakami T, Xu CN, Kitahara A (1999) Microstructure, mechanical properties and oxidation behavior of powder compacts of the Nb-Si-B system prepared by spark plasma sintering. Intermetallics 7(9):1043–1048CrossRefGoogle Scholar
  50. Niihara K (1991) New design concept of structural ceramics-ceramic nanocomposites. J Ceram Soc Jpn 99:974–982CrossRefGoogle Scholar
  51. Olevsky E, Froyen L (2006) Constitutive modelling of spark plasma sintering of conductive materials. Scr Mater 55:1175–1178CrossRefGoogle Scholar
  52. Olevsky EA, Froyen L (2008) Impact of thermal diffusion on densification during SPS. J Am Ceram Soc 92:122–132CrossRefGoogle Scholar
  53. Olevsky EA, Kandukuri S, Froyen L (2007) Consolidation enhancement in spark plasma sintering: impact of high heating rates. J Appl Phys 102(11):114913CrossRefGoogle Scholar
  54. Olevsky EA, Bradbury WL, Haines CD, Martin DG, Kapoor D (2012) Fundamental aspects of spark plasma sintering: experimental analysis of scalability. J Am Ceram Soc 95:2406–2413CrossRefGoogle Scholar
  55. Omori M (2000) Sintering, consolidation, reaction and crystal growth by the spark plasma system (SPS). Mater Sci Eng A 287:183–188CrossRefGoogle Scholar
  56. Orru R, Richeri R, Locci AM, Cincotti A, Cao G (2009) Consolidation/synthesis of materials by electric current activated/assisted sintering. Mater Sci Eng R 63:127–287CrossRefGoogle Scholar
  57. Queyreau S, Monnet G, Devincre B (2010) Orowan strengthening and forest hardening superposition examined by dislocation dynamics simulations. Acta Mater 58(17):5586–5595CrossRefGoogle Scholar
  58. Raichenko AI, Burenkov GL, Leshchinsky VI (1973) Theoretical analysis of the elmentary act of electric discharge sintering. Phys Sinter 5(2):215–225Google Scholar
  59. Raju G, Basu B (2014) Spark plasma sintering of nanoceramic composites. Compr Hard Mater 2:177–205Google Scholar
  60. Randall GM (2010) Coarsening in sintering: grain shape distribution, grain size distribution, and grain growth kinetics in solid-pore systems. Crit Rev Solid State Mater Sci 35:263–305CrossRefGoogle Scholar
  61. Ravi KR, Murugesan A, Udhayabanu V, Subramanian R, Murty BS (2012) Microstructure and mechanical property of Fe-Al2O3 nanocomposites synthesized by reactive milling followed by spark plasma sintering. Mater Sci Forum 710:291–296CrossRefGoogle Scholar
  62. Razavi M, Rahimipour MR, Mansoori R (2008) Synthesis of TiC–Al2O3 nanocomposite powder from impure Ti chips, Al and carbon black by mechanical alloying. J Alloys Compd 450:463–467CrossRefGoogle Scholar
  63. Reis J, Chaim R (2008) Densification maps for spark plasma sintering of nanocrystalline MgO ceramics: particle coarsening and grain growth effects. Mater Sci Eng A 491(1–2):356–363CrossRefGoogle Scholar
  64. Saboori A, Pavese M, Badini C, Fino P (2017) Development of Al- and Cu-based nanocomposites reinforced by graphene nanoplatelets: fabrication and characterization. Front Mater Sci 11(2):171–181CrossRefGoogle Scholar
  65. Sadeghi B, Shamanian M, Ashrafizadeh F, Cavaliere P, Rizzo A (2017) Influence of Al2O3 nanoparticles on microstructure and strengthening mechanism of Al-based nanocomposites produced via spark plasma sintering. J Mater Eng Perform 26(6):2928–2936CrossRefGoogle Scholar
  66. Sadeghi B, Shamanian M, Ashrafizadeh F et al (2018) Microstructural behaviour of spark plasma sintered composites containing bimodal micro- and nano-sized Al2O3 particles. Pow Met 61(1):50–63CrossRefGoogle Scholar
  67. Saheb N, Khalil A, Hakeem AS et al (2014) Spark plasma sintering of CNT reinforced Al6061 and Al2124 nanocomposites. Adv Mater Sci Eng 2014(535640):1–9CrossRefGoogle Scholar
  68. Shi X, Xu F, Zhang Z, Dong Y, Tan Y, Wang L, Yang J (2010) Mechanical properties of hot-pressed Al2O3/SiC composites. Mater Sci Eng A 527:4646–4649CrossRefGoogle Scholar
  69. Skiba T, Hausild P, Karlík M et al (2010) Mechanical properties of spark plasma sintered FeAl intermetallics. Intermetallics 18(7):1410–1414CrossRefGoogle Scholar
  70. Suarez M, Fernandez A, Menendez JL et al (2013) Challenges and opportunities for spark plasma sintering: a key technology for a new generation of materials. In: Ertug B (ed) Sintering applications. InTech, Rijeka, pp 319–342Google Scholar
  71. Supova M, Martynkova GS, Barabaszova K (2011) Effect of nanofillers dispersion in polymer matrices: a review. Sci Adv Mater 3:1–25CrossRefGoogle Scholar
  72. Suryanarayana C (2011) Synthesis of nanocomposites by mechanical alloying. J Alloys Compd 509(1):229–234CrossRefGoogle Scholar
  73. Tamari N, Tanaka T, Tanaka K (1995) Effect of spark plasma sintering on densification and mechanical properties of silicon carbide. J Ceram Soc Jpn 103(7):740–742CrossRefGoogle Scholar
  74. Taylor GF (1933) Apparatus for making hard metal compositions. US Patent No. 1,896,854. https://patents.google.com/patent/US1896854
  75. Thostenson ET, Li C, Chou TW (2005) Nanocomposites in context. Compos Sci Technol 65:491–516CrossRefGoogle Scholar
  76. Tiwari D, Basu B, Biswas K (2009) Simulation of thermal and electrical field evolution during spark plasma sintering. Ceram Int 35(2):699–708CrossRefGoogle Scholar
  77. Tokita M (1993) Trends in advanced SPS spark plasma sintering systems and technology. J Soc Powder Technol Jpn 30(11):790–804CrossRefGoogle Scholar
  78. Tokita M (1999) Mechanism of spark plasma sintering. In: Miyake S, Samandi M (eds) Proceedings of the International Symposium on Microwave, Plasma and Thermochemcial Processing of Advanced Materials, JWRI. Osaka Universities, Osaka, pp 69–76Google Scholar
  79. Udhayabanu V, Ravi KR, Murugan K (2011) Development of Ni-Al2O3 in-situ nanocomposite by reactive milling and spark plasma sintering. Metall Mater Trans A 42(7):2085–2093CrossRefGoogle Scholar
  80. Umeda J, Kondoh K, Imai H (2009) Friction and wear behavior of sintered magnesium composite reinforced with CNT-Mg2Si/MgO. Mater Sci Eng A 504(1–2):157–162CrossRefGoogle Scholar
  81. Vanmeensel K, Laptev A, Hennicke J et al (2005) Modelling of the temperature distribution during field assisted sintering. Acta Mater 53(16):4379–4388CrossRefGoogle Scholar
  82. Voisin T, Durand L, Karnatak N, Gallet SL et al (2013) Temperature control during spark plasma sintering and application to up-scaling and complex shaping. J Mater Process Technol 213:269–278CrossRefGoogle Scholar
  83. Wang D, Yuan H, Qiang J (2017) The microstructure evolution, mechanical properties and densification mechanism of TiAl-based alloys prepared by spark plasma sintering. Metals 7:201CrossRefGoogle Scholar
  84. WOK(Web of Knowledge) citation report (2012) http://wok.mimas.ac.uk/news/2012/20120924
  85. Yamanaka S, Gonda R, Kawasaki A et al (2007) Fabrication and Thermal Properties of Carbon Nanotube/Nickel Composite by Spark Plasma Sintering Method. Mat. Trans. 48(9):2506–2512Google Scholar
  86. Yamazaki K, Risbud SH, Aoyama H, Shoda K (1996) PAS (Plasma activated sintering): transient sintering process control for rapid consolidation of powders. J Mater Process Technol 56(1–4):955–965CrossRefGoogle Scholar
  87. Yanagisawa O, Hatayama T, Matsugi K (1994) Recent research on spark sintering. Materia Jpn 33(12):1489–1496CrossRefGoogle Scholar
  88. Zadeh AS (2012) Comparison between current models for the strength of particulate-reinforced metal matrix nanocomposites with emphasis on consideration of Hall–Petch effect. Mater Sci Eng A 531:112–118CrossRefGoogle Scholar
  89. Zadra M, Casari F, Girardini L, Molinari A (2007) Spark plasma sintering of pure aluminium powder: mechanical properties and fracture analysis. Powder Metall 50(1):40–45CrossRefGoogle Scholar
  90. Zener C (1948) Theory of Strain Interaction of Solute Atoms. Phys. Rev. 639:74Google Scholar
  91. Zhang ZH, Wang FC, Wang L et al (2008) Microstructural characteristics of large-scale ultrafine grained copper. Mater Charact 59(3):329–333Google Scholar

Copyright information

© Springer Nature Switzerland AG 2019

Authors and Affiliations

  • N. Sharma
    • 1
  • S. N. Alam
    • 1
  • B. C. Ray
    • 1
  1. 1.Metallurgical and Materials Engineering DepartmentNational Institute of Technology RourkelaRourkelaIndia

Personalised recommendations