Radiation-Induced Precipitates in a Self-ion Irradiated Cold-Worked 316 Austenitic Stainless Steel Used for PWR Baffle-Bolts

  • Jan MichaličkaEmail author
  • Zhijie Jiao
  • Gary Was
Conference paper
Part of the The Minerals, Metals & Materials Series book series (MMMS)


5 meV Ni++ and Fe++ ion irradiations were performed to investigate radiation-induced precipitates evolution in a cold-worked 316 austenitic stainless steel at high doses and temperatures. The irradiation conditions were 23 dpa at 380 °C, 130 dpa at 380 °C, 23 dpa at 500 °C, and 15 dpa at 600 °C. TEM selected electron diffraction (SAED), TEM dark-field imaging and energy dispersive spectroscopy (EDS) mapping were used as complementary techniques to determine crystallography, morphology and chemical composition of radiation-induced precipitates. The precipitates were predominantly in form of the Ni–Si rich γ′ phase at all irradiation conditions. The EDS analysis further determined Ni–Si–Mo–P and Ni–Si–Mn rich precipitates after irradiation at 380 and 600 °C, respectively. The precipitates were found close to saturated state between 23 and 130 dpa at 380 °C irradiation conditions. A different effect of higher irradiation temperatures was found between 500 and 600 °C. In case of the irradiation to 23 dpa at 500 °C, the average size of precipitates was similar to irradiations at 380 °C, but the density was lower. However, the precipitates revealed large size and very low density following the irradiation to 15 dpa at 600 °C. The original dislocation network introduced by cold-working was found as dominant sink for intra-granular solute radiation-induced segregation (RIS) and possibly took place as primary nucleation site of radiation-induced precipitates at irradiation temperatures 380 and 500 °C. At the temperature 600 °C, the RIS at dislocation network almost vanished and the main nucleation sites became twin boundaries as more energetically favorable intra-granular sinks.


Radiation-induced damage Neutron irradiation Self-ion irradiation Austenitic stainless steels PWR Baffle-bolts TEM EDS 



The authors gratefully acknowledge Drs. Ovidiu Toader and Fabian Naab for their assistance in conducting the self-ion irradiations, Drs. Steve Bruemmer and Dan Edwards for providing EPRI reports and valuable comments, and Dr. Ondrej Man for help with FIB sample preparation. The research could be performed thanks to support of facilities provided by the Michigan Ion Beam Laboratory and the Electron Microbeam Analysis Laboratory at University of Michigan, the CEITEC Nano Research Infrastructure at Brno University of Technology [MEYS CR (ID LM2015041)], the Tescan Orsay Holding in Brno [MIT CR (4.2 PT03/586)], and the Institute of Materials of Czech Academy of Science in Brno [MEYS CR (No. LM2015069)]. Financial support was provided by DOE under contract DE-FG07-07ID14894.


  1. 1.
    S.J. Zinkle, G.S. Was, Acta Mater. 61, 735–758 (2013)CrossRefGoogle Scholar
  2. 2.
    E.P. Simonen, F.A. Garner, N.A. Klymyshyn, M.B. Toloczko, Response of PWR Baffle-Former Bolt loading to swelling, irradiation creep and bolt replacement as revealed using finite element modeling, in Proceedings of the 12th International Conference on Environmental Degradation of Materials in Nuclear Power System—Water Reactors (2005)Google Scholar
  3. 3.
    S.M. Bruemmer, E.P. Simonen, P.M. Scott, P.L. Andresen, G.S. Was, J.L. Nelson, J. Nucl. Mater. 274, 299–314 (1999)CrossRefGoogle Scholar
  4. 4.
    K. Fukuya, K. Fujii, H. Nishioka, Y. Kitsunai, J. Nucl. Sci. Technol. 43, 159–173 (2006)CrossRefGoogle Scholar
  5. 5.
    K. Fujii, K. Fukuya, J. Nucl. Mater. 469, 82–88 (2016)CrossRefGoogle Scholar
  6. 6.
    A. Etienne, B. Radiguet, P. Pareige, J.-P. Massoud, C. Pokor, J. Nucl. Mater. 382, 64–69 (2008)CrossRefGoogle Scholar
  7. 7.
    D.J. Edwards, E.P. Simonen, F.A. Garner, L.R. Greenwood, B.M. Oliver, S.M. Bruemmer, J. Nucl. Mater. 317, 32–45 (2003)CrossRefGoogle Scholar
  8. 8.
    B.W. Arey, D.G. Atteridge, S.M. Bruemmer, Production of Tailored Alloys to Isolate Metallurgical Variables Promoting IASCC (EPRI, Palo Alto, CA, 2006)Google Scholar
  9. 9.
    D.J. Edwards, E.P. Simonen, S.M. Bruemmer, Characterization of Neutron-Irradiated 300-Series Stainless Steels (EPRI, Palo Alto, CA, 2006) (EP-P14516/C7130)Google Scholar
  10. 10.
    D.J. Edwards, S.M. Bruemmer, Characterization of CIR II Irradiated Stainless Steels (EPRI, Palo Alto, CA, 2008) (EP-P19021/C9406)Google Scholar
  11. 11.
    A.R. Laborne, P. Gavoille, J. Malaplate, C. Pokor, B. Tanguy, J. Nucl. Mater. 460, 72–81 (2015)CrossRefGoogle Scholar
  12. 12.
    M. Ernestová, J. Burda, J. Kočík, E. Keilová, J. Michalička, C. Pokor, Influence of the neutron spectrum on the sensitivity to IASCC and microstucture of CW 316 material, in Fontevraud 8—Contribution of Materials Investigations and Operating Experience to LWRs’ Safety, Performance and Reliability, France, Avignon (2014)Google Scholar
  13. 13.
    Z. Jiao, G.S. Was, J. Nucl. Mater. 425, 105–111 (2012)CrossRefGoogle Scholar
  14. 14.
    Z. Jiao, G.S. Was, J. Nucl. Mater. 449, 200–206 (2014)CrossRefGoogle Scholar
  15. 15.
    G. Gupta, Z. Jiao, A.N. Ham, J.T. Busby, G.S. Was, J. Nucl. Mater. 351, 162 (2006)CrossRefGoogle Scholar
  16. 16.
    E. Getto, Z. Jiao, A.M. Monterrosa, K. Sun, G.S. Was, J. Nucl. Mater. 465, 116e126 (2015)CrossRefGoogle Scholar
  17. 17.
    J.F. Ziegler, J.P. Biersack, SRIM2008 Program (IBM Corp, Yorktown, NY, 2008)Google Scholar
  18. 18.
    R.E. Stoller, M.B. Toloczko, G.S. Was, A.G. Certain, S. Dwaraknath, F.A. Garner, Nuclear instruments methods Phys. Res., Sect. B 310 75–80 (2013)Google Scholar
  19. 19.
    W. Van Renterghem et al., J. Nucl. Mater. 413, 95–102 (2011)CrossRefGoogle Scholar
  20. 20.
    T. Toyama, Y. Nozawa, W. Van Renterghem, Y. Matsukawa, M. Hatakeyama, Y. Nagai, A. Al Mazouzi, S. Van Dyck, J. Nucl. Mater. 418, 62–68 (2011)CrossRefGoogle Scholar
  21. 21.
    J. Michalicka, A. Hojna, E. Keilova, J. Kocik, TEM radiation damage investigation of neutron irradiated baffle-to-former bolt extracted from a decommissioned WWER-440 reactor, in Proceedings of the 16th International Conference on Environmental Degradation of Materials in Nuclear Power System—Water Reactors (2013)Google Scholar
  22. 22.
    E.H. Lee, P.J. Maziasz, A.F. Rowcliffe, in The Metallurgical Society of AIME, ed. by J.R. Holland, et al. (Warrendale, PA, 1981), pp. 191–218Google Scholar
  23. 23.
    G.S. Was, T. Allen, Mater. Charact. 32, 239–255 (1994)CrossRefGoogle Scholar
  24. 24.
    P.J. Maziasz, J. Nucl. Mater. 169, 95–115 (1989)CrossRefGoogle Scholar
  25. 25.
    P.J. Maziasz, J. Nucl. Mater. 205, 118–145 (1993)CrossRefGoogle Scholar
  26. 26.
    A. Etienne et al., J. Nucl. Mater. 406, 244–250 (2010)CrossRefGoogle Scholar
  27. 27.
    Z. Jiao, G.S. Was, Acta Mater. 59, 1220–1238 (2011)CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society 2019

Authors and Affiliations

  1. 1.CEITEC Nano Research Infrastructure, Brno University of TechnologyBrnoCzech Republic
  2. 2.Department of Nuclear Engineering and Radiological SciencesUniversity of MichiganAnn ArborUSA

Personalised recommendations